Preparation method of waterborne acrylic coating for woodenware
A water-based acrylic, water-based technology, applied in coatings and other directions, can solve the problems of poor adhesion and salt water resistance of water-based acrylic coatings, and achieve the effects of excellent dispersion, high degree of bonding, and long service life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0017] Example 1
[0018] A preparation method of water-based acrylic paint for woodware includes the following steps:
[0019] S1. Mix 80 parts of water-based acrylic emulsion, 12 parts of composite microspheres, 1 part of water-based defoamer, 2 parts of film-forming aids, 1 part of antifreeze, and 2 parts of water-based wetting and leveling agent according to parts by weight. It is 1200r / min and the stirring temperature is 70℃ to obtain the pretreated aqueous acrylic emulsion;
[0020] The composite microspheres are prepared by the following process: according to weight parts, 10 parts of medical stone powder, 6 parts of expanded perlite, and 0.2 parts of sodium lauryl sulfate are mixed and ground uniformly, 100 parts of water are added, and 2 parts of concentration are added dropwise. It is an 80g / L sodium silicate aqueous solution, stir evenly, adjust the pH of the system to 7.1-7.5, age at room temperature for 2 days, add 10 parts of soybean oil, 2 parts of hydrogen peroxide, ...
Example Embodiment
[0022] Example 2
[0023] A preparation method of water-based acrylic paint for woodware includes the following steps:
[0024] S1. Stir 100g of water-based acrylic emulsion, 4g of composite microspheres, 2g of water-based defoamer, 1g of film-forming aids, 2g of antifreeze, and 1g of water-based wetting and leveling agent at a stirring speed of 1400r / min and a stirring temperature of 50 °C to obtain a pretreated aqueous acrylic emulsion;
[0025] The composite microspheres are prepared by the following process: mix and grind 18g medical stone powder, 2g expanded perlite, and 1g sodium lauryl sulfate, add 50g water and stir evenly, and add 8g of 60g / L sodium silicate aqueous solution dropwise. , Stir uniformly, adjust the pH of the system to 7.1-7.5, age at room temperature for 4 days, add 4g soybean oil, 4g hydrogen peroxide, 50g formic acid and mix, heat to 98°C and stir for 5min to obtain composite microspheres;
[0026] S2. Stir 10g diatomaceous earth, 1g fly ash, 8g vermiculite ...
Example Embodiment
[0027] Example 3
[0028] A preparation method of water-based acrylic paint for woodware includes the following steps:
[0029] S1. Stir 95g of water-based acrylic emulsion, 8g of composite microspheres, 1.8g of water-based defoamer, 1.3g of film-forming aids, 1.6g of antifreeze, and 1.3g of water-based wetting and leveling agent at a stirring speed of 1350r / min. The stirring temperature is 55°C to obtain the pretreated aqueous acrylic emulsion;
[0030] The composite microspheres are prepared by the following process: 16g medical stone powder, 3g expanded perlite, 0.8g sodium lauryl sulfate are mixed and ground uniformly, 60g water is added and stirred evenly, and 6g of sodium silicate with a concentration of 65g / L is added dropwise. Stir the aqueous solution uniformly, adjust the pH of the system to 7.1-7.5, age at room temperature for 3.5 days, add 6g soybean oil, 3.5g hydrogen peroxide, and 60g formic acid to mix, heat up to 96°C and stir for 8min to obtain composite microsphere...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap