Glass fiber yarn efficient impregnating agent

A technology of glass fiber yarn and sizing agent, applied in the field of glass fiber, can solve the problem of inability to produce high-quality and multi-variety glass fibers, and achieve the effects of high moisturizing performance and thermal stability, good mechanical properties, and good penetration effect.

Inactive Publication Date: 2018-05-25
ANHUI TONGLI NEW MATERIALS
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The sizing agent is an indispensable surface treatment material in the production of glass fiber. The quality of the glass fiber and the variety of varieties largely depend on the sizing agent. Without a good sizing agent, it is impossible to produce High quality and variety of glass fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of high-efficiency sizing agent for glass fiber yarn, in terms of weight percentage, its components include:

[0017] Epoxy resin emulsion 21%, polyacrylate 16%, ammonia water 1%, silane coupling agent 0.8%, silicone lubricant 0.05%, cationic lubricant 0.05%, nonionic lubricant 1.3%, dodecylbenzenesulfon 1% sodium bicarbonate, 0.5% imidazoline, 4% gasoline, 0.9% ammonium chloride, 0.08% fatty diamine, and the balance is deionized water.

Embodiment 2

[0019] A kind of high-efficiency sizing agent for glass fiber yarn, in terms of weight percentage, its components include:

[0020] Epoxy resin emulsion 13%, polyacrylate 24%, ammonia water 2%, silane coupling agent 0.2%, silicone lubricant 0.5%, cationic lubricant 0.7%, nonionic lubricant 0.3%, dodecylbenzenesulfonate 0.5% sodium bicarbonate, 1% imidazoline, 8% gasoline, 0.3% ammonium chloride, 0.8% fatty diamine, and the balance is deionized water.

Embodiment 3

[0022] A kind of high-efficiency sizing agent for glass fiber yarn, in terms of weight percentage, its components include:

[0023] Epoxy resin emulsion 15%, polyacrylate 22%, ammonia water 1.7%, silane coupling agent 0.4%, silicone lubricant 0.2%, cationic lubricant 0.3%, nonionic lubricant 0.9%, dodecylbenzenesulfonate 0.7% sodium bicarbonate, 0.7% imidazoline, 7% gasoline, 0.7% ammonium chloride, 0.3% fatty diamine, and the balance is deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of glass fiber, in particular to a glass fiber yarn efficient impregnating agent. The glass fiber yarn efficient impregnating agent provided by the invention comprises the following components: 13 to 21 percent of epoxy resin emulsion, 16 to 24 percent of polyacrylic ester, 1 to 2 percent of ammonia water, 0.2 to 0.8 percent of a silane coupling agent,0.05 to 0.5 percent of an organosilicon lubricating agent, 0.05 to 0.7 percent of a cationic lubricating agent, 0.3 to 1.3 percent of a non-ionic lubricating agent, 0.5 to 1 percent of sodium dodecylbenzene sulfonate, 0.5 to 1 percent of imidazoline, 4 to 8 percent of gasoline, 0.3 to 0.9 percent of ammonium chloride, 0.08 to 0.8 percent of aliphatic diamine and the balance of deionized water. The glass fiber yarn efficient impregnating agent provided by the invention has good penetration effect, high moisturizing property and high heat stability, can give high mechanical property to the glass fiber yarn and realizes a good weaving effect.

Description

technical field [0001] The invention relates to the technical field of glass fibers, in particular to a high-efficiency sizing agent for glass fiber yarns. Background technique [0002] Glass fiber is an inorganic non-metallic material with excellent performance. There are many kinds. The advantages are good insulation, strong heat resistance, good corrosion resistance and high mechanical strength, but the disadvantages are brittleness and poor wear resistance. It is made of glass balls or waste glass through high-temperature melting, wire drawing, winding, weaving and other processes. The diameter of its single filament is several microns to more than 20 microns, which is equivalent to a hair. 1 / 20-1 / 5 of that, each bundle of fiber precursors consists of hundreds or even thousands of monofilaments. The glass fiber is often used as reinforcing material of composite material, electrical insulation and heat insulation materials, substrate and other national economy fields. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C25/465
CPCC03C25/36C03C25/285
Inventor 苏本璋
Owner ANHUI TONGLI NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products