Production method of glass ball
A production method and glass ball technology, which are applied in the directions of cleaning methods using liquids, cleaning methods and utensils, chemical instruments and methods, etc., can solve the problems of backward production methods and low production efficiency, and achieve good cleaning effects.
Inactive Publication Date: 2018-05-29
海宁市博展经编有限公司
View PDF3 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0004] Although the preparation method disclosed in this patent produces glass spheres with low cost through fewer processes, the preparation method is backward and the production efficiency is low. Therefore, it is necessary to design a production method for glass spheres
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0071] The following are specific embodiments of the present invention and in conjunction with the accompanying drawings, the technical solutions of the present invention are further described, but the present invention is not limited to these embodiments.
[0072] The production method of this glass ball, this production method comprises the following steps:
[0073] S1. Weigh waste glass, put the waste glass into a crusher and crush it to obtain glass particles; in this embodiment, the crusher is an existing product available on the market;
[0074] S2. Put sandstone, limestone, calcite, fluorite, boric acid, boron oxide, corrosion inhibitor, sodium fluorosilicate and pyrophyllite into the mixer in parts by mass, and mix them uniformly to prepare ingredients; in this embodiment , the mixer is an existing product available on the market;
[0075] S3. Put the glass grains and ingredients into a glass melting furnace, heat the temperature to 1500-1700° C., and keep it warm for...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention provides a production method of a glass ball. The production method solves the technical problems of the existing preparation method of lagging manufacturing mode, low production efficiency and the like. The production method of the glass ball comprises the following steps of S1, taking waste and old glass; putting the waste and old glass into a crushing machine to be crushed to obtain glass particles; S2, feeding sandstone, limestone, calcite, fluorite, boracic acid, boric oxide, corrosion inhibitors, sodium fluosilicate and pyrophyllite into a material mixing machine in parts by mass; after the uniform mixing, making the materials to obtain auxiliary materials; S3, simultaneously putting the glass particles and the auxiliary materials into a glass molten furnace; performingheating to reach the temperature being 1500 to 1700 DEG C; performing heat insulation for 8 to 12h; obtaining molten glass liquid; S4, cooling molten glass liquid to 600 to 700 DEG C; then, introducing cooled glass liquid into a ball making machine for shaping and processing to obtain glass ball blanks. The production method has the characteristic of high production efficiency.
Description
technical field [0001] The invention relates to a production method, in particular to a production method of glass spheres. Background technique [0002] Glass balls are colored balls made of glass. At present, most of the raw materials used to prepare glass balls are natural ores. When preparing, firstly, various ores should be crushed and added into powder, and then according to the composition of the glass, made into batch materials, sent to a glass melting furnace for melting, and formed glass liquid. , and then drain the glass liquid into the ball making machine for molding processing to obtain glass balls. [0003] After searching, for example, Chinese patent literature discloses a glass sphere and its preparation method [application number: CN201511030975.X; publication number: CN105669031A]. The glass ball and its preparation method comprise the following steps: a glass ball is made by the following steps: adding the following substances to the waste glass powder, ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More IPC IPC(8): C03C6/06C03C12/00C03B25/00B08B11/00B08B3/02B08B13/00F26B25/04F26B17/04F26B21/00