A colored pencil lead with high flexural strength and preparation method thereof
A technology of flexural strength and pencil lead, which is applied in the field of stationery, can solve the problems of low flexural strength of colored pencil lead, high processing conditions and equipment requirements, and difficult erasure of writing marks, so as to improve erasability, Low cost, beautiful writing effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0040] Adopt following process method to prepare a kind of high-performance red pencil lead:
[0041] a. In terms of parts by mass, take by weighing 25 parts of phenolic resin, 15 parts of polyethylene resin, 35 parts of talc, 20 parts of red pigment powder, 5 parts of nano silicon dioxide and 150 parts of butanone;
[0042]b. Mechanically blending the weighed raw material and methyl ethyl ketone at 80° C. to remove 80% of the total mass of methyl methyl ethyl ketone to obtain a mixture;
[0043] c. Roll the mixture through a roller mill at 100°C for 6 times to obtain a uniformly dispersed red film-like material;
[0044] d. Extrude the film-like material in the step c and cut it into 15cm rods in a rod making machine;
[0045] e. Extrude the rod in step d into a core at 130° C. with a single-screw extruder and cut it into 8 cm short cores;
[0046] f. Dry the short lead in an oven at 100°C for 2 hours to obtain a red pencil lead with high flexural strength;
[0047] g. Pla...
Embodiment 2
[0050] Adopt following process method to prepare a kind of high-performance yellow pencil lead:
[0051] a. In terms of parts by mass, weigh 35 parts of water-based polyurethane resin, 12 parts of polyvinyl alcohol resin, 30 parts of kaolin, 18 parts of yellow pigment powder, 5 parts of nano titanium dioxide and 200 parts of water;
[0052] b. Mechanically blending the weighed raw materials and water at 110°C to remove 85% of the water mass to obtain a mixture;
[0053] c. the mixture is rolled 6 times at 110° C. through a roll mill to obtain a uniformly dispersed yellow film-like material;
[0054] d. Extrude the film-like material in the step c and cut it into 15cm rods in a rod making machine;
[0055] e. Extrude the rod in step d into a core at 135° C. with a single-screw extruder and cut it into 20 cm short cores;
[0056] f. Dry the short lead in an oven at 100°C for 2 hours to obtain a yellow pencil lead with high flexural strength;
[0057] g. Place the yellow penci...
Embodiment 3
[0060] Adopt following process method to prepare a kind of high-performance green pencil lead:
[0061] a. In terms of parts by mass, weigh 35 parts of cyanate resin, 12 parts of rubber resin, 30 parts of diatomaceous earth, 18 parts of green pigment powder, 5 parts of nano zinc oxide and 100 parts of chloroform;
[0062] b. mechanically blending the weighed raw material and chloroform at 80° C. to remove 85% of the total mass of chloroform in chloroform to obtain a mixture;
[0063] c. The mixture is rolled 8 times at 110°C through a roll mill to obtain a uniformly dispersed green film-like material;
[0064] d. Extrude the film-like material in the step c and cut it into 15cm rods in a rod making machine;
[0065] e. Extrude the rod in step d into a core at 140°C with a single-screw extruder and cut it into 10cm short cores;
[0066] f. Dry the short lead in an oven at 120°C for 2 hours to obtain a colored pencil lead with high flexural strength;
[0067] g. Place the col...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com