Adhesive for safe dental implant and preparation method thereof

A dental implant and adhesive technology, applied in dental preparations, dentistry, dental prosthesis, etc., can solve the problems of complex price comparison on the surface of enamel, more activities and more force, and no product has been developed, so as to achieve good biocompatibility , High bonding strength, easy to use

Inactive Publication Date: 2020-09-22
上海御齿台医疗科技有限公司
View PDF21 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Dental adhesives are used in the mouth, there is a lot of water, the price ratio of the enamel surface is complicated, and the activities are more and more forceful. It is difficult to bond in the process of tooth repair. People have been exploring more effective dental adhesives for a long time. Although there are also a lot of results, the results are not satisfactory, and no satisfactory products have been developed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive for safe dental implant and preparation method thereof
  • Adhesive for safe dental implant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] The adhesive for safe dental implant is prepared from the following raw materials in parts by weight: polyethylene glycol acrylate 20wt%, 2-hydroxy-4'-(2-hydroxyethoxy)-2-methylpropiophenone 0.15 % by weight, 0.06% by weight of sodium benzene sulfinate, 30% by weight of dopamine-based compound, 4% by weight of aluminum oxide, 3% by weight of crosslinkable polymethyl methacrylate, 5% by weight of zirconia, 0.1% by weight of triclosan, the balance For absolute ethanol.

[0054] The preparation process of the polyethylene glycol acrylate is as follows: 15g of polyethylene glycol and 300mL of toluene are placed in a reaction vessel, mixed evenly, heated to 90°C and kept for 60 minutes, then naturally cooled to 20°C to obtain a mixed solution; Add 100mL of dichloromethane and 6mL of triethylamine into the mixture, and stir at 300 rpm for 20 minutes under the protection of nitrogen; Stir and react at 300 rpm for 24 hours; after the reaction, filter the reaction solution with...

Embodiment 2

[0060] The adhesive for safe dental implant is prepared from the following raw materials in parts by weight: polyethylene glycol acrylate 20wt%, 2-hydroxy-4'-(2-hydroxyethoxy)-2-methylpropiophenone 0.15 wt%, sodium benzenesulfinate 0.06wt%, dopamine-based compound 30wt%, aluminum oxide 4wt%, crosslinkable polymethyl methacrylate 3wt%, pretreated zirconia 5wt%, triclosan 0.1 %, the balance is absolute ethanol.

[0061] The preparation process of the polyethylene glycol acrylate is as follows: 15g of polyethylene glycol and 300mL of toluene are placed in a reaction vessel, mixed evenly, heated to 90°C and kept for 60 minutes, then naturally cooled to 20°C to obtain a mixed solution; Add 100mL of dichloromethane and 6mL of triethylamine into the mixture, and stir at 300 rpm for 20 minutes under the protection of nitrogen; Stir and react at 300 rpm for 24 hours; after the reaction, filter the reaction solution with a 100-mesh filter cloth and collect the filtrate; add sodium bica...

Embodiment 3

[0068] The adhesive for safe dental implant is prepared from the following raw materials in parts by weight: polyethylene glycol acrylate 20wt%, 2-hydroxy-4'-(2-hydroxyethoxy)-2-methylpropiophenone 0.15 wt%, sodium benzenesulfinate 0.06wt%, dopamine-based compound 30wt%, aluminum oxide 4wt%, crosslinkable polymethyl methacrylate 3wt%, pretreated zirconia 5wt%, triclosan 0.1 %, the balance is absolute ethanol.

[0069] The preparation process of the polyethylene glycol acrylate is as follows: 15g of polyethylene glycol and 300mL of toluene are placed in a reaction vessel, mixed evenly, heated to 90°C and kept for 60 minutes, then naturally cooled to 20°C to obtain a mixed solution; Add 100mL of dichloromethane and 6mL of triethylamine into the mixture, and stir at 300 rpm for 20 minutes under the protection of nitrogen; Stir and react at 300 rpm for 24 hours; after the reaction, filter the reaction solution with a 100-mesh filter cloth and collect the filtrate; add sodium bica...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a safe adhesive for dental implants and a preparation method of the adhesive. The safe adhesive for dental implants is prepared from raw materials as follows: polyethylene glycol-acrylate, 2-hydroxy-4'-(2-hydroxyethoxy)-2-methylphenylacetone, benzene sulfinic acid sodium salt, a biological compound, aluminum oxide, crosslinked polymethyl methacrylate, pretreated zirconium oxide, triclosan and the balance of a solvent. The safe adhesive for dental implants has no harm to tooth tissue and oral mucosa, does not decompose and age under the action of bacteria and enzyme in saliva, has higher adhesion for a dental material and has high bonding strength.

Description

technical field [0001] The invention relates to a dental adhesive, in particular to an adhesive for safe dental implantation and a preparation method thereof. Background technique [0002] Dental adhesives have been used in the restoration of teeth since more than half a century ago. In 1940, polymethyl methacrylate was used for the first time in dental repair surgery, but this dental adhesive was not widely used after that because it was not hard enough and the bonding force was not strong. It is known that a composite binder that is still in use until now appeared in 1965. The base material of this binder is polyfunctional methyl methacrylate, and the filler is inorganic powder. Dental adhesives are used in the mouth, there is a lot of water, the price ratio of the enamel surface is complicated, and the activities are more and more forceful. It is difficult to bond in the process of tooth repair. People have been exploring more effective dental adhesives for a long time. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K6/898A61K6/891A61K6/887A61K6/60A61K6/71A61K6/30A61K6/15
CPCA61K6/15A61K6/30A61K6/80A61K6/831A61K6/878A61K6/887A61K6/891A61K6/898C08L5/08C08L71/02C08L33/12
Inventor 杨爱芳杨笑云杨锐
Owner 上海御齿台医疗科技有限公司