Continuous casting and rolling method for preparing wire rod for 5183 aluminum alloy welding wire

A technology of aluminum alloy welding wire, continuous casting and rolling, which is applied in the field of continuous casting and rolling for the preparation of wire rods for 5183 aluminum alloy welding wire, which can solve the problems of high tool and mold consumption and energy consumption, low product yield, and large floor space. problems, to achieve the effects of high production efficiency, low product scrap rate, and small hidden dangers of safety accidents

Inactive Publication Date: 2018-06-22
江苏和拓铝线有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these two kinds of process equipment require large investment, many processes, large floor area, high tool and mold consumption and energy consumption, high geometric waste in the production process, and relatively low product yield.
Especially the control of alloy composition, magnesium content and hydrogen content before and after continuous casting and continuous drawing, and the problem of easy wire breakage during drawing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Continuous casting and rolling method for preparing wire rod for 5183 aluminum alloy welding wire
  • Continuous casting and rolling method for preparing wire rod for 5183 aluminum alloy welding wire
  • Continuous casting and rolling method for preparing wire rod for 5183 aluminum alloy welding wire

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The concrete steps of the continuous casting and rolling method for preparing wire rods for 5183 aluminum alloy welding wire are as follows:

[0040] The first step is to carry out batching, calculate the returned materials, aluminum ingots for remelting, magnesium ingots and intermediate alloys, select the returned materials with a Si content of less than 0.06%, and the 5-ton grade is Al99.90 b (Wt, Si<0.06%) aluminum ingots for remelting,

[0041] The second step is smelting. The smelting equipment includes a vertical aluminum melting furnace and a holding furnace. The recycled material and aluminum ingots for remelting are loaded into the vertical aluminum melting furnace from the feeding port for smelting. The melting temperature is 700 ° C ~ 720 ° C. ℃, when the aluminum material in the shaft furnace is melted, the aluminum melt in the vertical aluminum melting furnace is introduced into the holding furnace through the diversion launder, and the alloying of the alu...

Embodiment 2

[0050] The concrete steps of the continuous casting and rolling method for preparing wire rods for 5183 aluminum alloy welding wire are as follows:

[0051] The first step is to carry out batching, calculate the returned materials, aluminum ingots for remelting, magnesium ingots and intermediate alloys, select the returned materials with a Si content of less than 0.06%, and the 5-ton grade is Al99.90 b (Wt, Si<0.06%) aluminum ingots for remelting,

[0052] The second step is smelting. The smelting equipment includes a vertical aluminum melting furnace and a holding furnace. The recycled material and aluminum ingots for remelting are loaded into the vertical aluminum melting furnace from the feeding port for smelting. The melting temperature is 710 ° C ~ 730 ° C ℃, when the aluminum material in the shaft furnace is melted, the aluminum melt in the vertical aluminum melting furnace is introduced into the holding furnace through the diversion launder, and the alloying of the alum...

Embodiment 3

[0061] The concrete steps of the continuous casting and rolling method for preparing wire rods for 5183 aluminum alloy welding wire are as follows:

[0062] The first step is to carry out batching, calculate the returned materials, aluminum ingots for remelting, magnesium ingots and intermediate alloys, select the returned materials with a Si content of less than 0.06%, and the 5-ton grade is Al99.90 b (Wt, Si<0.06%) aluminum ingots for remelting.

[0063] The second step is to smelt. The smelting equipment includes a vertical aluminum melting furnace and a holding furnace. The recycled material and aluminum ingots for remelting are put into the vertical aluminum melting furnace from the feeding port for melting. When the aluminum material in the vertical furnace melts After completion, the temperature of the aluminum melt in the water storage chamber is raised to 730°C to 750°C, and then the aluminum melt in the vertical aluminum melting furnace is introduced into the holding...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
areaaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a continuous casting and rolling process for a wire rod for an aluminum alloy welding wire, in particular to a continuous casting and rolling method for preparing a wire rod for a 5183 aluminum alloy welding wire. The continuous casting and rolling method for preparing wire rod for 5183 aluminum alloy welding wire comprises the steps that (1) burdening is carried out; (2)smelting is carried out; (3) melt is subjected to purification, including degassing, impurity removing, drossing, covering agent spraying, and warm keeping and standing; (4) continuous casting is carried out to prepare aluminum alloy wire ingots; (5) continuous rolling is carried out to obtain an aluminum alloy wire rod; (6) and the aluminum alloy wire rod without oil-water quenching guide rod iscarried out to form a circle by double frames. The continuous casting and rolling method for preparing 5183 aluminum alloy wire rod has the advantages of high production efficiency, moderate cost, stable wire rod quality, hydrogen content less than or equal to 0.12 ml / 100 g, and excellent mechanical properties.

Description

technical field [0001] The invention relates to a continuous casting and rolling process for wire rods for aluminum alloy welding wires, in particular to a continuous casting and rolling method for preparing wire rods for 5183 aluminum alloy welding wires. Background technique [0002] ER5183 is usually used as AlMg4.5Mn alloy filler metal, which is a non-heat-treatable aluminum alloy. The composition is: 4.3%-5.0% magnesium, 0.5-1.0% manganese and appropriate chromium and titanium, which can be used for MIG or TIG welding of bobbins or longitudinal incisions. As a general-purpose welding consumable with a wide range of uses, this This alloy is generally used in the welding process of ships, drilling equipment, trains, automobiles, storage tanks and pressure vessels. The applicable base metals include 5083, 5086, 5456, 5052, 5652 and 5056. [0003] Welding wire is an important factor affecting the weld metal composition, structure, liquid-solidus temperature, thermal cracki...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/08C22F1/047B21C37/04
CPCB21C37/047C22C21/08C22F1/047
Inventor 周天国
Owner 江苏和拓铝线有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap