PBT heat conducting and heat resisting material for LED lamp holder

A technology for LED lamp holders and heat-resistant materials, which is applied in the field of heat-resistant materials and their preparation, and PBT heat conduction, and can solve problems such as poor light transmission and reduced external luminous efficiency

Inactive Publication Date: 2018-06-29
HEILONGJIANG XINDA ENTERPRISE GRP
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to light and heat damage to the resin used for packaging, the light transmittance of the LED is deteriorated, and the external luminous efficiency is reduced.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Heat the glass fiber in a muffle furnace for dewaxing, add 1% silane coupling agent by mass fraction into the water-ethanol mixture and soak for 2 hours, then wash it, put it in an oven at 80 degrees Celsius and dry it for 3 hours for later use; PP-R , E-MA-GMA, TAF lubricant, AIN powder, antioxidant 1010, calcium stearate according to the ratio of 100:15:2:10:1:0.5, add to the high-speed mixer and mix for 10 minutes, put it in an oven at 80°C Dry for 1 hour and set aside; add the dried PP-R, E-MA-GMA, TAF lubricant, AIN powder, antioxidant 1010, calcium stearate into the extruder, and then add 20 A portion of the treated glass fiber is extruded and granulated to obtain a heat-conducting and heat-resistant PBT material.

Embodiment 2

[0017] Heat the glass fiber in a muffle furnace for dewaxing, add 1% silane coupling agent by mass fraction into the water-ethanol mixture and soak for 2 hours, then wash it, put it in an oven at 80 degrees Celsius and dry it for 3 hours for later use; PP-R , E-MA-GMA, TAF lubricant, AIN powder, antioxidant 1010, calcium stearate according to the ratio of 100:15:2:15:1:0.5 into the high-speed mixer and mix for 10 minutes, put it in an oven at 80 ℃ Dry for 1 hour and set aside; add the dried PP-R, E-MA-GMA, TAF lubricant, AIN powder, antioxidant 1010, calcium stearate into the extruder, and then add 20 A portion of the treated glass fiber is extruded and granulated to obtain a heat-conducting and heat-resistant PBT material.

Embodiment 3

[0019] Heat the glass fiber in a muffle furnace for dewaxing, add 1% silane coupling agent by mass fraction into the water-ethanol mixture and soak for 2 hours, then wash it, put it in an oven at 80 degrees Celsius and dry it for 3 hours for later use; PP-R , E-MA-GMA, TAF lubricant, AIN powder, antioxidant 1010, calcium stearate according to the ratio of 100:15:2:20:1:0.5, add to the high-speed mixer and mix for 10 minutes, put it in an oven at 80°C Dry for 1 hour and set aside; add the dried PP-R, E-MA-GMA, TAF lubricant, AIN powder, antioxidant 1010, calcium stearate into the extruder, and then add 20 A portion of the treated glass fiber is extruded and granulated to obtain a heat-conducting and heat-resistant PBT material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a PBT heat conducting and heat resisting material for an LED lamp holder and a preparation method of the PBT heat conducting and heat resisting material and relates to a heat resisting plastic material and a preparation method thereof. The heat conducting and heat resisting PBT mainly comprises a resin matrix, a reinforcing system, a heat conducting system, a lubricating system and an antioxidant system; the resin matrix is PBT; the reinforcing system is glass fibers; the lubricating system comprises a TAF lubricant and calcium stearate; the antioxidant system is an antioxidant 1010. According to the heat conducting and heat resisting PBT material prepared by the preparation method disclosed by the invention, the glass fibers are used as a reinforcing framework, anethylene-methyl acrylate-glycidyl methacrylate (E-MA-GMA) terpolymer is used as a compatibilizer, and AIN is filled as a heat conducting factor; better strength and toughness are kept under the condition of ensuring high heat conductivity of the PBT material; meanwhile, the PBT plastic has the advantages of easiness in processing, batch production, low cost and the like, so that the heat conducting plastic is applied to the related fields of LED lamp holders and the like.

Description

technical field [0001] The invention relates to a heat-resistant plastic material and a preparation method thereof, in particular to a PBT heat-conducting and heat-resistant material used for an LED lamp holder and a preparation method thereof. Background technique [0002] With the global warming caused by greenhouse gas emissions, people have enhanced their awareness of energy conservation and environmental protection. The use of new energy-saving light-emitting diodes (Light Emitting Diode, referred to as LED) has attracted the attention of the international community. Since light-emitting diodes (LEDs) have the advantages of small size, high luminous efficiency, low energy consumption, high brightness, and environmental protection, governments of various countries have increased funding and corresponding policy support for LED research and development. In the past decade, LED technology has developed rapidly. Generally, about 15% to 20% of the input power of a high-pow...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L23/14C08L23/08C08K13/06C08K9/06C08K7/14C08K3/28C09K5/14
CPCC08L23/14C08L67/02C08L2201/08C09K5/14C08L23/0884C08K13/06C08K9/06C08K7/14C08K2003/282
Inventor 于敬阳崔成杰谢众
Owner HEILONGJIANG XINDA ENTERPRISE GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com