Wear-resistant paint applied to suitcase and preparation method thereof

A technology of wear-resistant coatings and suitcases, which is applied in the field of coatings, can solve the problems of peeling of the suitcase surface coating, scratches, poor wear resistance, etc., and achieve excellent aging resistance, increased density, and excellent wear resistance Effect

Inactive Publication Date: 2018-07-06
HEFEI YUANKE GARMENT DESIGN CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The coating used on the surface of the existing suitcase has poor wear resistance. After long-term use, the coating on the surface of the suitcase will peel off and scratches will appear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of wear-resisting paint that is used for suitcase, comprises the raw material of following parts: 65 parts of epoxy resin, 35 parts of tung oil, 25 parts of ethyl acetate, 20 parts of modified silicon carbide, 15 parts of modified nanometer silicon dioxide, 10 parts of modified nano titanium dioxide, 10 parts of modified quartz powder, 5 parts of trioxane, 5 parts of barium sulfate, 3 parts of polymethyl methacrylate, 3 parts of zinc borate, 1 part of sodium phytate, curing agent 1 part, 1 part of methylisothiazolinone, 0.6 parts of sodium dodecylbenzenesulfonate, 14 parts of additives and 25 parts of water.

[0034] in,

[0035] The preparation method of described modified silicon carbide is:

[0036] (1) Take nano-scale silicon carbide and add it to concentrated sulfuric acid, ultrasonically treat it for 10 minutes, filter it with suction, wash until neutral, and then dry it to obtain acidified silicon carbide;

[0037] (2) Mix the acidified silicon carbide a...

Embodiment 2

[0059] A kind of wear-resisting paint that is used for suitcase, comprises the raw material of following parts: 85 parts of epoxy resin, 45 parts of tung oil, 35 parts of ethyl acetate, 25 parts of modified silicon carbide, 20 parts of modified nano silicon dioxide, 12 parts of modified nano titanium dioxide, 12 parts of modified quartz powder, 8 parts of trioxane, 8 parts of barium sulfate, 6 parts of polymethyl methacrylate, 6 parts of zinc borate, 4 parts of sodium phytate, curing agent 4 parts, 4 parts of methylisothiazolinone, 1.2 parts of sodium dodecylbenzenesulfonate, 116 parts of additives and 35 parts of water.

[0060] in,

[0061] The preparation method of described modified silicon carbide is:

[0062] (1) Take nano-scale silicon carbide and add it to concentrated sulfuric acid, ultrasonically treat it for 15 minutes, filter it with suction, wash until neutral, and then dry it to obtain acidified silicon carbide;

[0063] (2) Mix the acidified silicon carbide an...

Embodiment 3

[0084] A kind of wear-resisting paint that is used for suitcase, comprises the raw material of following parts: 75 parts of epoxy resin, 40 parts of tung oil, 30 parts of ethyl acetate, 22.5 parts of modified silicon carbide, 17.5 parts of modified nano silicon dioxide, 11 parts of modified nano titanium dioxide, 11 parts of modified quartz powder, 6.5 parts of trioxane, 6.5 parts of barium sulfate, 4.5 parts of polymethyl methacrylate, 4.5 parts of zinc borate, 2.5 parts of sodium phytate, curing agent 2.5 parts, 2.5 parts of methylisothiazolinone, 0.9 parts of sodium dodecylbenzenesulfonate, 15 parts of additives and 30 parts of water.

[0085] in,

[0086] The preparation method of described modified silicon carbide is:

[0087] (1) Take nano-scale silicon carbide and add it to concentrated sulfuric acid, sonicate for 13 minutes, filter with suction, wash until neutral, and then dry to obtain acidified silicon carbide;

[0088] (2) Mix the acidified silicon carbide and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses anti-wear paint applied to suitcase and a preparation method thereof and relates to the technical field of paint. The anti-wear paint is prepared from the following raw materials in parts by weight: 65 to 85 parts of epoxy resin, 35 to 45 parts of tung oil, 25 to 35 parts of acetic ether, 20 to 25 parts of modified silicon carbide, 15 to 20 parts of modified nano silicon dioxide, 10 to 12 parts of modified nano titanium oxide, 10 to 12 parts of modified quartz powder, 5 to 8 parts of trioxane, 5 to 8 parts of barium sulfate, 3 to 6 parts of polymethyl methacrylate, 3 to6 parts of zinc borate, 1 to 4 parts of sodium phytate, 1 to 4 parts of curing agent, 1 to 4 parts of methyl isothiazolinone, 0.6 to 1.2 parts of sodium dodecyl benzene sulfonate, 14 to 16 parts of aid and 25 to 35 parts of water. The anti-wear paint disclosed by the invention has the advantages of excellent wear resistance and ageing resistance.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a wear-resistant coating for suitcases and a preparation method thereof. Background technique [0002] Suitcase is a class in bags. It includes a luggage body, a telescopic pull rod and a luggage bottom wheel, and is widely used because of its convenience. Suitcases have a long history. Suitcases, from wooden boxes and large suitcases for clothing only, to portable suitcases and trolley cases in various shapes, the suitcases in people's hands are constantly evolving. [0003] The coating used on the surface of the existing suitcase has poor wear resistance, and after long-term use, the coating on the surface of the suitcase will peel off and scratches will appear. Contents of the invention [0004] The object of the present invention is to provide a wear-resistant coating for suitcases and a preparation method thereof, which have excellent wear resistance and aging resistan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D191/00C09D133/12C09D7/62
Inventor 张力
Owner HEFEI YUANKE GARMENT DESIGN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com