Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Environment-friendly light weight decorative heat insulation board and preparation method thereof

A thermal insulation board, lightweight technology, applied in ceramic products, other household appliances, applications, etc., can solve the problems of heat loss, non-compliance with energy conservation and environmental protection, waste of energy, etc., to reduce heat loss, improve product market competitiveness, reduce The effect of production costs

Inactive Publication Date: 2018-07-24
温州月煌科技有限公司
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The thermal insulation effect of the board is a key indicator to measure the quality of the board. If the thermal insulation effect is poor, it will lead to heat loss and waste of energy, which does not meet the demands of energy conservation and environmental protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] This embodiment relates to an environmentally friendly lightweight decorative insulation board, including the following raw materials in parts by weight: 10 parts of waste glass, 8 parts of construction waste, 7 parts of closed-cell perlite, 5 parts of polyethylene, 9 parts of iron tailings, and 10 parts of cement 5 parts of epoxy resin, 12 parts of bentonite, 6 parts of calcined kaolin, 3 parts of polyester fiber, 2 parts of zirconium silicate, 2 parts of tungsten carbide, 1 part of aluminum oxide, 2 parts of glass fiber, modified longan shell 4 parts of powder, 2 parts of foaming agent, 2 parts of active agent and appropriate amount of water.

[0030] Wherein, the preparation method of the modified longan shell powder is as follows:

[0031] (1) Air-dry the longan shell and put it into a pulverizer to pulverize it, then put it into an agate ball mill jar, then add zirconia balls with a diameter of 5mm, mill it at a speed of 500r / min for 5 hours, and get longan shell p...

Embodiment 2

[0044] This embodiment relates to an environmentally friendly lightweight decorative insulation board, including the following raw materials in parts by weight: 20 parts of waste glass, 14 parts of construction waste, 12 parts of closed-cell perlite, 10 parts of polyethylene, 16 parts of iron tailings, and 20 parts of cement 11 parts of epoxy resin, 26 parts of bentonite, 12 parts of calcined kaolin, 6 parts of polyester fiber, 5 parts of zirconium silicate, 4 parts of tungsten carbide, 3 parts of aluminum oxide, 3 parts of glass fiber, modified longan shell 8 parts of powder, 3 parts of foaming agent, 4 parts of active agent and appropriate amount of water.

[0045] Wherein, the preparation method of the modified longan shell powder is as follows:

[0046] (1) Air-dry the longan shell and put it into a pulverizer to crush it, then put it into an agate ball mill jar, then add zirconia balls with a diameter of 5mm, and ball mill it at a speed of 600r / min for 5 hours, and take it ...

Embodiment 3

[0059] This embodiment relates to an environmentally friendly lightweight decorative insulation board, including the following raw materials in parts by weight: 15 parts of waste glass, 10 parts of construction waste, 9 parts of closed-cell perlite, 6 parts of polyethylene, 10 parts of iron tailings, and 12 parts of cement 7 parts of epoxy resin, 15 parts of bentonite, 8 parts of calcined kaolin, 4 parts of polyester fiber, 3 parts of zirconium silicate, 2.5 parts of tungsten carbide, 1.3 parts of aluminum oxide, 2.2 parts of glass fiber, modified longan shell 5 parts of powder, 2.1 parts of foaming agent, 2.4 parts of active agent and appropriate amount of water.

[0060] Wherein, the preparation method of the modified longan shell powder is as follows:

[0061] (1) Air-dry the longan shell and put it into a pulverizer to crush it, then put it into an agate ball mill jar, then add zirconia balls with a diameter of 5mm, and ball mill it at a speed of 520r / min for 5 hours, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly light weight decorative heat insulation board, which is prepared from the following raw materials in parts by weight: 10 to 20 parts of waste glass, 8-14 parts of construction waste, 7-12 parts of closed-cell perlite, 5-10 parts of polyethylene, 9-16 parts of iron tailings, 10-20 parts of cement, 5-11 parts of epoxy resin, 12-26 parts of bentonite, 6-12 parts of calcined kaolin, 3-6 parts of polyester fibers, 2-5 parts of zirconium silicate, 2-4 parts of tungsten carbide, 1-3 parts of aluminum oxide, 2-3 parts of glass fibers, 4-8 parts of modified longan shell powder, 2-3 parts of foaming agent and 2-4 parts of active agent. The environment-friendly light weight decorative heat insulation board is scientific and reasonable in formula; the prepared product is good in heat insulation effect, low in heat conductivity coefficient, and high in breaking strength and shock strength.

Description

technical field [0001] The invention belongs to the technical field of thermal insulation boards, and in particular relates to an environmentally friendly lightweight decorative thermal insulation board and a preparation method thereof. Background technique [0002] The thermal insulation effect of the board is a key indicator to measure the quality of the board. If the thermal insulation effect is poor, it will lead to heat loss and waste of energy, which does not meet the demands of energy conservation and environmental protection. In the purification workshop, the insulation effect of the board is highly required. Only with a good insulation effect can the heat be prevented from being lost and the utilization rate of energy can be improved. Contents of the invention [0003] The present invention provides an environmentally friendly lightweight decorative thermal insulation board and its preparation method, which solves the problems in the background technology. The for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B38/10C04B20/02C04B18/24C04B111/40
CPCC04B20/023C04B28/00C04B2111/40C04B14/22C04B18/16C04B14/18C04B24/2611C04B18/12C04B24/281C04B14/104C04B14/106C04B16/0683C04B14/046C04B14/303C04B14/42C04B14/322C04B24/16C04B18/24C04B2103/42C04B38/10Y02W30/91
Inventor 刘东升
Owner 温州月煌科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com