Flame-retarding and environment-friendly cable material for network cabling and preparation method thereof

A technology for network wiring and cable materials, applied in plastic/resin/wax insulators, organic insulators, etc., can solve the problems of easy aging and poor bending resistance, and achieve the effects of low volatility, long durability and small thermal expansion coefficient

Inactive Publication Date: 2018-08-03
HEFEI SIBOT SOFTWARE DEV CO LTD
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the existing telecommunication cable materials also have the disadvantages of easy aging and poor bending resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A flame-retardant and environment-friendly cable material for network wiring, comprising the following raw materials in parts by weight:

[0031] 35 parts of PVC resin, 8 parts of nano-silicon carbide, 5 parts of dinonyl phthalate, 5 parts of aluminum silicate, 10 parts of glass fiber, 5 parts of nano-zinc oxide, 4 parts of nano-antimony trioxide, modified graphene 5 parts, 4 parts of calcium carbonate, 3 parts of flame retardant, 2.5 parts of curing agent, 3.5 parts of antioxidant, 3.5 parts of stabilizer and 3 parts of silane coupling agent;

[0032] The preparation method of modified graphene is as follows: immerse graphene in sulfuric acid solution, after stirring and mixing evenly, add potassium permanganate of 0.1 times of graphene weight therein, under the condition of 35 degrees Celsius, mix and stir reaction for 20 minutes, precipitate , filtered, rinsed repeatedly with deionized water, and dried in an oven at 200 degrees Celsius to obtain the modified graphene...

Embodiment 2

[0047] A flame-retardant and environment-friendly cable material for network wiring, comprising the following raw materials in parts by weight:

[0048] 48 parts of PVC resin, 15 parts of nano-silicon carbide, 10 parts of dinonyl phthalate, 12 parts of aluminum silicate, 18 parts of glass fiber, 10 parts of nano-zinc oxide, 8 parts of nano-antimony trioxide, modified graphene 10 parts, 9 parts of calcium carbonate, 5 parts of flame retardant, 4.5 parts of curing agent, 6 parts of antioxidant, 6 parts of stabilizer and 6 parts of silane coupling agent;

[0049] The preparation method of modified graphene is as follows: immerse graphene in sulfuric acid solution, after stirring and mixing evenly, add potassium permanganate of 0.2 times of graphene weight thereinto, under the condition of 50 degrees Celsius, mix and stir reaction for 30 minutes, precipitate , filtered, rinsed repeatedly with deionized water, and dried in an oven at 300 degrees Celsius to obtain the modified graph...

Embodiment 3

[0064] A flame-retardant and environment-friendly cable material for network wiring, comprising the following raw materials in parts by weight:

[0065] 42 parts of PVC resin, 10 parts of nano-silicon carbide, 8 parts of dinonyl phthalate, 9 parts of aluminum silicate, 15 parts of glass fiber, 8 parts of nano-zinc oxide, 6 parts of nano-antimony trioxide, modified graphene 8 parts, 6 parts of calcium carbonate, 4.2 parts of flame retardant, 3.5 parts of curing agent, 4.6 parts of antioxidant, 4.2 parts of stabilizer and 4.8 parts of silane coupling agent;

[0066] The preparation method of modified graphene is as follows: immerse graphene in sulfuric acid solution, after stirring and mixing evenly, add the potassium permanganate of 0.15 times of graphene weight thereinto, under the condition of 42 degrees Celsius, mix and stir reaction for 26 minutes, precipitate , filtered, rinsed repeatedly with deionized water, and dried in an oven at 260 degrees Celsius to obtain the modif...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a flame-retarding and environment-friendly cable material for network cabling and a preparation method thereof and relates to the technical field of cable materials. The flame-retarding and environment-friendly cable material is prepared from the following raw materials in parts by weight: 35 to 48 parts of PVC (Polyvinyl Chloride) resin, 8 to 15 parts of nano silicon carbide, 5 to 10 parts of dinonyl phthalate, 5 to 12 parts of aluminum silicate, 10 to 18 parts of glass fibers, 5 to 10 parts of nano zinc oxide, 4 to 8 parts of nano antimony trioxide, 5 to 10 parts of modified graphene, 4 to 9 parts of calcium carbonate, 3 to 5 parts of flame retardant, 2.5 to 4.5 parts of curing agent, 3.5 to 6 parts of antioxidant, 3.5 to 6 parts of stabilizing agent and 3 to 6 parts of silane coupling agent. The cable material provided by the invention has a high flame-retarding coefficient and low smoke and no toxin in a combustion process; the flame-retarding and environment-friendly cable material has the advantages of high environment-friendly performance, stable chemical properties, high anti-ageing performance, high compression resistance and bending resistance, long service life, high practicability, simple preparation method and easiness for operation and production.

Description

technical field [0001] The invention relates to the technical field of cable materials, in particular to a flame-retardant and environment-friendly cable material for network wiring and a preparation method thereof. Background technique [0002] When expansion is required, high-density distribution frames can use space more efficiently by reducing the number of passive distribution frames required in each installation. Most users do not conduct certification tests on the installed network cables, but conduct inspections during the network debugging process. When the network can be connected, the installed cables are considered qualified. This approach is not only wrong but also very dangerous. Because the network traffic is very low during network debugging, the user does not feel any problems at this time. The cable verification test is to test the continuity, length of the cable, and whether the twisted pair connector is connected correctly and other general tests. [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/06C08K3/34C08K3/04C08K9/02C08K5/12H01B3/44
CPCC08K13/06C08K3/042C08K3/34C08K5/12C08K9/02C08K2201/011H01B3/443C08L27/06
Inventor 吴青明
Owner HEFEI SIBOT SOFTWARE DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com