Aging-resistant flame-retardant ultraviolet-curable optical fiber coating and preparation method thereof

A flame-retardant, ultraviolet light technology, applied in the direction of fire-resistant coatings, coatings, etc., can solve the problems of poor flame retardancy and aging resistance, achieve fast curing speed, improve anti-oxidation and anti-aging performance, and good adhesion Effect

Inactive Publication Date: 2018-08-07
成都市创斯德机电设备有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the above-mentioned shortcomings of poor flame retardancy and aging resistance in the existing UV-curable optical fiber coatings, and provide an aging-resistant flame-retardant UV-curable optical fiber coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An aging-resistant flame-retardant UV-curable optical fiber coating is prepared from the following raw materials in parts by weight: propoxylated glycerin triacrylate 54, methacrylic acid-1,1-dimethyl-2,2,3,4 , 4,4-hexafluorobutyl ester 13, ethoxylated trimethylolpropane triacrylate 5, photoinitiator 1844 4, ethoxylated bisphenol A diacrylate 9, isobornyl methacrylate 6, γ-ammonia Propyltriethoxysilane 3, p-hydroxyanisole 2, nanoclay 5, methyl-(butylcarbamoyl)-2-benzimidazole carbamate 1, additive 10;

[0018] The auxiliary agent is made of the following raw materials in parts by weight: sepiolite 11, nano-zinc oxide 5, barium ricinoleate 3, tributyl phosphate 2, polyhydroxymethylsiloxane 1, chitosan 29; The preparation method is to put the sepiolite into the calciner and calcinate at 490°C for 2 hours, take it out, and crush it together with nano-zinc oxide into a 70-mesh mixed powder; mix the remaining ingredients, heat to 62°C, stir for 23 minutes, and then add Mix ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aging-resistant flame-retardant ultraviolet-curable optical fiber coating. The aging-resistant flame-retardant ultraviolet-curable optical fiber coating is prepared from 50-57 parts by weight of propoxyglycerol triacrylate, 10-14 parts by weight of 1, 1-dimethyl-2, 2, 3, 4, 4, 4-hexafluorobutyl methacrylate, 3-6 parts by weight of ethoxylated trimethylolpropane triacrylate, 3-5 parts by weight of a photoinitiator 1844, 7-10 parts by weight of ethoxylated bisphenol A diacrylate, 5-7 parts by weight of isobornyl methacrylate, 2-4 parts by weight of gamma-aminopropyltriethoxysilane, 1-2 parts by weight of 4-methoxyphenol, 4-6 parts by weight of nano-clay, 1-2 parts by weight of methyl-(butylaminoformyl)-2-benzimidazole carbamate, and 9-13 parts by weight of an aid.The aging-resistant flame-retardant ultraviolet-curable optical fiber coating has high anti-oxidation and anti-aging properties, good leveling properties, a fast curing rate and good adhesion.

Description

technical field [0001] The invention relates to an optical fiber coating material, in particular to an aging-resistant and flame-retardant ultraviolet light curing optical fiber coating and a preparation method thereof. Background technique [0002] Optical fiber, referred to as optical fiber (optical fiber), is a thin fiber-like material made of plastic or glass. When light passes through it, it can form total reflection and transmit. Compared with the loss of electricity in wire transmission, the loss of light in optical fiber transmission is much lower. Therefore, optical fiber has many advantages such as low loss, small size, wide frequency band, anti-interference, light weight, and high efficiency. It is widely used as a material for long-distance information transmission. The emergence of optical fiber has laid a solid foundation for the rapid development of modern communication technology. Common fiber types include silica fiber, fluorine-doped fiber, infrared fiber...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D4/02C09D4/06C09D7/61C09D7/63C09D7/65C09D5/18
CPCC09D4/06C09D5/18
Inventor 高启新
Owner 成都市创斯德机电设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products