Alpha-Fe2O3-ZnO/gangue composite photocatalyst and preparation method and application thereof

A -fe2o3-zno, coal gangue technology, applied in the field of photocatalyst preparation, can solve problems such as no reports yet

Active Publication Date: 2018-08-24
HEBEI UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] So far, no information about α-Fe 2 o 3 -Report of ZnO / coal gangue composite photocatalyst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alpha-Fe2O3-ZnO/gangue composite photocatalyst and preparation method and application thereof
  • Alpha-Fe2O3-ZnO/gangue composite photocatalyst and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Coal gangue from the Pingshuo mining area in Shanxi was crushed and fully ground, passed through a 200-mesh sieve, and calcined at 700 °C for 2 h for later use. At the same time, the preparation of Fe 3+ Iron salt solution with an ion concentration of 0.2 mol / L, Zn 2+ Zinc salt solution with ion concentration of 0.1 mol / L, 6 mol / L and 0.1 mol / L sodium hydroxide aqueous solution are used for later use.

[0046] 20 mL of zinc sulfate aqueous solution (Zn 2+ The ion concentration is 0.1 mol / L) and the calculated amount of ferric nitrate aqueous solution (Fe 3 + ion concentration of 0.2 mol / L) into a three-neck flask, distilled water to a volume of 100 mL, added 5 g of pretreated coal gangue powder, stirred magnetically for 1 h, and slowly added 6 mol / L and 0.1 mol / L of sodium hydroxide aqueous solution, the pH value of the reaction system was adjusted to 9 by controlling the addition of sodium hydroxide aqueous solution, and boiling refluxed for 3 h. After suction fi...

Embodiment 2~6

[0047] Embodiment 2~6 and comparative example 1~4

[0048] The operation steps of Examples 2-6 and Comparative Examples 1-4 are the same as those of Example 1, the difference is only in the type of zinc salt and iron salt used, the amount of iron salt aqueous solution, the coal gangue calcination temperature, the coal gangue amount and the pH of the reaction system values, as shown in Table 1.

[0049] Table 1 Examples 2~6 and Comparative Examples 1~4

[0050] .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an alpha-Fe2O3-ZnO / gangue composite photocatalyst, made from pretreated gangue, zinc salt solution and iron salt solution by boiling reflux; the molar ratio of Fe<3+> ion in the iron salt solution to Zn<2+> ion in the zinc salt solution is 2:(1-10), and the ratio of the mole number of the Zn2+ ion in the zinc salt solution to the mass of the pretreated gangue is 0.002 mol:5 g. The invention also relates to a preparation method and application of the composite photocatalyst. The composite photocatalyst herein can effectively degrade chlorophenols under the ultraviolet-visible light condition. The preparation method has the advantages of low material consumption, good process simplicity, short reaction time, relative mildness of condition, and zero environmental pollution, is a green synthetic process and is easy to industrialize.

Description

technical field [0001] The invention belongs to the field of photocatalyst preparation, in particular to an α-Fe 2 o 3 -ZnO / coal gangue composite photocatalyst, its preparation method and its application in the degradation of chlorophenol compounds. Background technique [0002] Photocatalytic technology can directly use light energy to degrade organic pollutants into small inorganic molecules under normal temperature and pressure, and has the characteristics of low energy consumption, simple operation, mild reaction conditions, and small secondary pollution. It is an ideal environmental pollution governance technology. In today's increasingly tense fossil energy and increasingly serious environmental pollution, the importance of photocatalytic technology is self-evident, and its core is to research and develop photocatalysts with excellent performance. [0003] The common photocatalytic material is TiO 2 , SnO 2 , CdS, WO 3 , ZrO 2 and Fe 2 o 3 and other n-type sem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/80B01J37/10C02F1/30C02F1/72C02F101/36C02F101/34
CPCC02F1/30C02F1/725B01J23/002B01J23/80B01J37/10C02F2101/36C02F2101/345C02F2305/10B01J35/39
Inventor 谢娟杜红霞许永权赵树春张国刚赵华许红
Owner HEBEI UNIVERSITY OF SCIENCE AND TECHNOLOGY