Welding wire powder, flux-cored wire and preparation and application

A technology of flux-cored welding wire and powder, applied in welding equipment, welding medium, manufacturing tools, etc., can solve the problems of high sensitivity to thermal cracks, welding cracks, restricting the progress of engineering construction, etc., to achieve suitable strength, improve crack resistance, The effect of stable mechanical properties

Active Publication Date: 2018-09-04
725TH RES INST OF CHINA SHIPBUILDING INDAL CORP
View PDF10 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main technical problems of this type of welding wire are: the weld structure of E308LT1-1 stainless steel flux-cored welding wire is mainly austenite, and the sensitivity to hot cracks is relatively high. Input for welding, otherwise welding cracks will appear, which greatly restricts the progress of engineering construction and affects the promotion of other matching stainless steel flux cored wires

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Welding wire powder, flux-cored wire and preparation and application
  • Welding wire powder, flux-cored wire and preparation and application
  • Welding wire powder, flux-cored wire and preparation and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] A welding wire powder, comprising the following components by mass percentage:

[0068]

[0069] A flux-cored welding wire, comprising the above-mentioned welding wire powder and sheath (stainless steel strip);

[0070] The preparation method of the described flux-cored welding wire comprises the following steps:

[0071] (1) Mix the components of the above-mentioned welding wire powder uniformly to obtain the welding wire powder;

[0072] (2) The powder obtained in the step (1) was wrapped with a 304L stainless steel strip and rolled and reduced in diameter to obtain a flux-cored welding wire, wherein the filling rate of the powder was 25wt%, and the diameter of the flux-cored wire was 1.2mm.

Embodiment 2

[0074] A welding wire powder, comprising the following components by mass percentage:

[0075]

[0076] A flux-cored welding wire, comprising the above-mentioned welding wire powder and sheath (stainless steel strip);

[0077] The preparation method of the described flux-cored welding wire comprises the following steps:

[0078] (1) Mix the components of the above-mentioned welding wire powder uniformly to obtain the welding wire powder;

[0079] (2) The powder obtained in the step (1) was wrapped with a 304L stainless steel strip, rolled and reduced in diameter to obtain a flux-cored welding wire, wherein the filling rate of the powder was 23.5wt%, and the diameter of the flux-cored wire was 1.2mm.

Embodiment 3

[0081] A welding wire powder, comprising the following components by mass percentage:

[0082]

[0083]

[0084] A flux-cored welding wire, comprising the above-mentioned welding wire powder and sheath (stainless steel strip);

[0085] The preparation method of the described flux-cored welding wire comprises the following steps:

[0086] (1) Mix the components of the above-mentioned welding wire powder uniformly to obtain the welding wire powder;

[0087] (2) The powder obtained in the step (1) was wrapped with a 304L stainless steel strip, rolled and reduced in diameter to obtain a flux-cored welding wire, wherein the filling rate of the powder was 21wt%, and the diameter of the flux-cored wire was 1.2mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of welding materials, and particularly relates to welding wire powder, flux-cored wire and preparation and application. The welding wire powder comprises,by mass, 15-18% of metal chromium, 3-5% of metal nickel, 6-8% of manganese metal, 0.6-1% of rare earth ferrosilicon, 2-4% of aluminum iron, 0.8%-1.5% of ferrotitanium, 25-28% of rutile, 1-2% of zirconsand, 6-9% of quartz, 3-5% of aluminum oxide, 3-5% of magnetite, 3-6% of potassium titanate, 1-2% of sodium fluoride, 3-4.5% of dehydrated potash feldspar, 0.15-0.3% of bismuth oxide, 0.5-1% of rareearth fluoride, and the balance iron powder. The invention further provides the flux-cored wire containing the powder. The flux-cored wire is good in welding process, small in splashing, good in spreading and fusing performance, stable in arc, easy to deslag, attractive in forming, and excellent in mechanical property.

Description

technical field [0001] The invention belongs to the technical field of welding materials, and in particular relates to a welding wire medicinal powder, a flux-cored welding wire and its preparation and application. Background technique [0002] Stainless steel flux-cored wire has the characteristics of excellent process performance, stable mechanical properties, high production efficiency and low overall cost, which has prompted the continuous increase in the proportion of flux-cored welding wire in welding materials in recent years, so the demand for stainless steel flux-cored wire continues to increase . [0003] E308LT1-1 stainless steel flux-cored wire is widely used in welding of structural parts and surfacing of corrosion-resistant layers in petrochemical, pressure vessel, shipbuilding, steel structure and engineering machinery and other fields. The main technical problems of this type of welding wire are: the weld structure of E308LT1-1 stainless steel flux-cored wel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K35/02B23K35/24B23K35/40
CPCB23K35/0266B23K35/24B23K35/40
Inventor 叶凡亢天佑王青云
Owner 725TH RES INST OF CHINA SHIPBUILDING INDAL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com