Oxygen-resistant shock-resistant synthetic rubber preparation method

A technology of synthetic rubber and production method, which is applied in the field of industrial production and can solve the problems of easy wear and shock absorption, decay, and lack of application.

Inactive Publication Date: 2018-09-07
芜湖盛创新材料科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the deficiencies of the prior art, the present invention provides an oxygen-resistant and shock-resistant synthetic rubber production method, which solves the phenomenon that most of the synthetic rubbers are oxidized with air during use, causing the rubber to break and rot , during the use of rubber, it is easy to be worn and has poor shock absorption performance, so it cannot be widely used.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A method for making oxygen-resistant and shock-resistant synthetic rubber, the oxygen-resistant and shock-resistant synthetic rubber is composed of rubber, zinc oxide, sulfur, stearic acid, accelerator DM, white filler, softener, accelerator TMTD and carbon black , including the following steps:

[0043] The first step: selection and placement of polymerization kettle and heating device

[0044] Choose a chemical laboratory with a good environment, select a suitable polymerization kettle in the laboratory, and install a suitable heating device on the test bench;

[0045] Step 2: Find the corresponding preparation raw materials and select the reaction ratio

[0046] Put 100 parts of rubber, 3 parts of zinc oxide, 1 part of stearic acid and 1.75 parts of sulfur into a polymerization kettle, and fully mix and stir the rubber, zinc oxide, stearic acid and sulfur at a high temperature of 100 degrees to form a mixture. Then add 0.5 parts of accelerator DM, talcum powder, so...

Embodiment 2

[0054] A method for making oxygen-resistant and shock-resistant synthetic rubber, the oxygen-resistant and shock-resistant synthetic rubber is composed of rubber, zinc oxide, sulfur, stearic acid, accelerator DM, white filler, softener, accelerator TMTD and carbon black , including the following steps:

[0055] The first step: selection and placement of polymerization kettle and heating device

[0056] Choose a chemical laboratory with a good environment, select a suitable polymerization kettle in the laboratory, and install a suitable heating device on the test bench;

[0057] Step 2: Find the corresponding preparation raw materials and select the reaction ratio

[0058] Put 100 parts of rubber, 3 parts of zinc oxide, 1 part of stearic acid and 1.75 parts of sulfur into the polymerization kettle, then fully mix and stir the rubber, zinc oxide, stearic acid and sulfur to form a mixture, and then add white carbon black , white filler, softener, accelerator TMTD and Zhongchao ...

Embodiment 3

[0066] A method for making oxygen-resistant and shock-resistant synthetic rubber, the oxygen-resistant and shock-resistant synthetic rubber is composed of rubber, zinc oxide, sulfur, stearic acid, accelerator DM, white filler, softener, accelerator TMTD and carbon black , including the following steps:

[0067] The first step: selection and placement of polymerization kettle and heating device

[0068] Choose a chemical laboratory with a good environment, select a suitable polymerization kettle in the laboratory, and install a suitable heating device on the test bench;

[0069] Step 2: Find the corresponding preparation raw materials and select the reaction ratio

[0070] Put 100 parts of rubber, 3 parts of zinc oxide, 1 part of stearic acid and 1.75 parts of sulfur into the polymerization kettle, then fully mix and stir the rubber, zinc oxide, stearic acid and sulfur to form a mixture, and then add the accelerator MD , white carbon black, ester plasticizer, accelerator TMTD...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an oxygen-resistant shock-resistant synthetic rubber preparation method. Oxygen-resistant shock-resistant synthetic rubber consists of rubber, zinc oxide, sulfur, stearic acid,an accelerant DM, a white filler, a softening agent, an accelerant TMTD (Tetramethylthiuram Disulfide) and carbon black. By adopting the oxygen-resistant shock-resistant synthetic rubber preparationmethod, under the action of the zinc oxide, the synthetic rubber has good corrosion resistance, tearing resistance and elasticity, and the consequence that the synthetic rubber has cracks and the stability of the synthetic rubber is affected since the synthetic rubber is reacted with irritant gases in the air when being used; due to reactions of the synthetic rubber after desulfuration, the synthetic rubber has shock resistance and durability, and the consequence that damage of the synthetic rubber is accelerated since the synthetic rubber is aged and abraded in the use process can be avoided;due to stirring and mixing of a polymerization kettle, raw materials can be sufficiently stirred, and the consequence that the use of the synthetic rubber is affected because of insufficient stirringcan be avoided.

Description

technical field [0001] The invention relates to the technical field of industrial production, in particular to an oxygen-resistant and shock-resistant synthetic rubber production method. Background technique [0002] Rubber refers to a highly elastic polymer material with reversible deformation. It is elastic at room temperature, can produce large deformation under a small external force, and can return to its original shape after the external force is removed. Rubber is a completely amorphous polymer. Its glass transition temperature is low and its molecular weight is often large, greater than hundreds of thousands. Early rubber was obtained from latex of plants such as rubber trees and rubber grasses. After processing, it is elastic and insulating. Durable, water and air impermeable material. High elastic polymer compound. Divided into two kinds of natural rubber and synthetic rubber. Natural rubber is processed by extracting gum from rubber trees, rubber grass and othe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L21/00C08L91/06C08K13/02C08K3/22C08K3/06C08K5/09C08K5/47C08K5/40C08K3/04C08K3/34
CPCC08L21/00C08K3/04C08K3/06C08K3/22C08K3/34C08K5/09C08K5/40C08K5/47C08K13/02C08K2003/2296C08L2201/08C08L91/06
Inventor 段国凡
Owner 芜湖盛创新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More