Polymer, composition for organic electroluminescence element, and organic electroluminescence element

A polymer, 6-membered ring technology, applied in the field of polymers, can solve the problems of poor driving stability, has not yet reached a practical level, difficult to layer by wet film-forming methods, and achieves excellent durability, hole accumulation suppression, Excellent hole injection effect

Active Publication Date: 2018-09-14
MITSUBISHI CHEM CORP
View PDF26 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the wet film formation method is difficult to laminate, so compared with the device obtained by the vacuum evaporation method, the driving stability is poor, and the current situation is that it has not yet reached the practical level except for some

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polymer, composition for organic electroluminescence element, and organic electroluminescence element
  • Polymer, composition for organic electroluminescence element, and organic electroluminescence element
  • Polymer, composition for organic electroluminescence element, and organic electroluminescence element

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0425] make out figure 1 The organic electroluminescence device shown.

[0426] After depositing an indium tin oxide (ITO) transparent conductive film on a glass substrate 1 by sputtering, a 2mm-wide stripe was patterned using a common photolithography technique and hydrochloric acid etching to form an anode 2 with a film thickness of 70nm. . After patterning, the ITO substrate is cleaned in the order of ultrasonic cleaning with aqueous surfactant solution, water washing with ultrapure water, ultrasonic cleaning with ultrapure water, and water washing with ultrapure water, then dried with compressed air, and finally UV ozone cleaning.

[0427] Next, prepare the arylamine polymer containing the following structural formula (P1), 4-isopropyl-4'-methyldiphenyliodonium tetrakis(pentafluorophenyl) boron represented by the structural formula (A1) A coating solution for forming a hole injection layer of acid salt and ethyl benzoate. This coating solution was formed into a film on...

Embodiment 2

[0470] For the hole transport layer 4, a coating solution for forming a hole transport layer containing a polymer 2 (P4) represented by the following structural formula was prepared, and formed on the hole injection layer 3 by spin coating under the following conditions. The film was heated to form a hole transport layer with a film thickness of 20 nm.

[0471]

[0472]

[0473] Solvent Cyclohexylbenzene

[0474] Coating solution concentration 1.5% by weight

[0475]

[0476]

[0477] For the light-emitting layer 5, a coating solution for forming a light-emitting layer containing compounds (H3) and (D2) represented by the following structural formulas was prepared, and a film was formed by spin coating under the following conditions, and heating was performed. On the layer 4, a light emitting layer with a film thickness of 41 nm was formed.

[0478] Except for this, an organic electroluminescent element was produced in the same manner as in Example 1. Table 10 sho...

Embodiment 3

[0501] The hole mobility of polymer 3 (P6) was measured using the time-of-flight (TOF) method in the same manner as the method described in JP-A-2014-51667.

[0502]

[0503] First, an ITO transparent conductive film (ITO stripes) was deposited on a glass substrate with a thickness of 70 nm, and the resulting substrate (manufactured by GEOMATEC) was subjected to ultrasonic cleaning with an aqueous surfactant solution, water washing with ultrapure water, ultrapure water After cleaning in the order of ultrasonic cleaning with pure water and water washing with ultrapure water, drying with compressed air was performed, and ultraviolet ozone cleaning was performed thereafter.

[0504] Dissolve (P6) at a concentration of 10% by mass in a solvent of toluene and silicone oil (manufactured by Shin-Etsu Silicones: KF-96) to prepare a solution, and spin coating on the cleaned substrate. film forming. It should be noted that all film formation was performed in a nitrogen atmosphere. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface tensionaaaaaaaaaa
reid vapor pressureaaaaaaaaaa
visible light transmittanceaaaaaaaaaa
Login to View More

Abstract

Provided is a polymer having a repeating unit represented by the following formula (1). In the formula, Ar1, Ar2, and Ar3 each independently represent an aromatic hydrocarbon group or aromatic heterocyclic group, which may optionally have a substituent group, and n represents an integer equal to 4 or greater. Multiple aromatic hydrocarbon groups and aromatic heterocyclic groups may be linked directly, or through at least two linking groups.

Description

[0001] This application is a divisional application. The Chinese national application number of the original application is 201480054297.8, and the filing date is October 2, 2014. The title of the invention is "polymer, composition for organic electroluminescent element, organic electroluminescent element, Organic EL display device and organic EL lighting". technical field [0002] The present invention relates to a polymer, in particular to a polymer useful as a hole injection layer and a hole transport layer of an organic electroluminescent element, a composition for an organic electroluminescent element containing the polymer, and an organic electroluminescent element having the polymer. Organic EL display and organic EL lighting of light-emitting elements. Background technique [0003] As a method for forming an organic layer in an organic electroluminescence element, a vacuum vapor deposition method and a wet film-forming method are mentioned. Vacuum deposition is easy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G73/02H01L51/50
CPCC08G73/0266H10K71/12H10K85/111H10K85/151H10K50/15H10K50/17
Inventor 饭田宏一朗李延军梅基友和
Owner MITSUBISHI CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com