Fire retardant coating for aluminium plate and production process thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for fire-resistant coatings and aluminum plates, applied in fire-resistant coatings, anti-corrosion coatings, alkali metal silicate coatings, etc., to achieve excellent chemical corrosion resistance, good fire resistance, and good acid and alkali resistance
Inactive Publication Date: 2018-09-21
TIANJIN MROGAN KUNDOM HI TECH DEV
View PDF4 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Applied on the surface of combustible substrates to change the combustion characteristics of the material surface and retard the rapid spread of fire; or applied to building components to improve the fire resistance limit of the special coatings, called fire-resistant coatings, but the existing fire-resistant coatings Can no longer meet the needs of the existing market
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0020] Embodiment 1: as figure 1 As shown, the present invention provides a kind of fireproof coating for aluminum plate, and the raw material of fireproof coating is composed of: sodium silicate, dimethyl silicone oil, adhesive, additive, solvent, catalyst, thickener, antibacterial agent, inorganic powder, synthetic Film agent, acid donor, foaming agent, synergist, inorganic filler, carbonization agent, epoxy resin and cellulose ether, the parts by weight of its raw materials are as follows: 10 parts of sodium silicate, 12 parts of simethicone, 5 parts of binder, 4 parts of additive, 5 parts of solvent, 1 part of catalyst, 3 parts of thickener, 4 parts of antibacterial agent, 10 parts of inorganic powder, 1 part of film forming agent, 3 parts of acid donor, foaming agent 2 parts, 3 parts of synergist, 4 parts of inorganic filler, 2 parts of carbonizing agent, 4 parts of epoxy resin and 5 parts of cellulose ether.
[0021] A kind of production process of fireproof coating for...
Embodiment 2
[0030] Embodiment 2: as figure 1 As shown, the present invention provides a kind of fireproof coating for aluminum plate, and the raw material of fireproof coating is composed of: sodium silicate, dimethyl silicone oil, adhesive, additive, solvent, catalyst, thickener, antibacterial agent, inorganic powder, synthetic Film agent, acid donor, foaming agent, synergist, inorganic filler, carbonization agent, epoxy resin and cellulose ether, the parts by weight of its raw materials are as follows: 12 parts of sodium silicate, 15 parts of simethicone, 8 parts of binder, 6 parts of additive, 7 parts of solvent, 2 parts of catalyst, 5 parts of thickener, 6 parts of antibacterial agent, 12 parts of inorganic powder, 3 parts of film forming agent, 6 parts of acid donor, foaming agent 4 parts, synergist 5 parts, inorganic filler 6 parts, charring agent 4 parts, epoxy resin 6 parts and cellulose ether 8 parts.
[0031] A kind of production process of fireproof coating for aluminum plate,...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a fire retardant coating for an aluminium plate and a production process tereof. The fire retardant coating catalyst is prepared form sodium silicate, simethicone, an adhesionagent, an annexing agent, solvent, a catalyst, a thickening agent, an antibacterial agent, inorganic powder, a film-forming agent, an acid donor, a foaming agent, a synergistic agent, inorganic fillers, a carbonization agent, epoxy resin and cellulose ether; the production process comprises the following steps of raw material preparation, dispersion, grinding, inspection and package; the fire retardant coating is good in environment protection, can continuously exert a flameproof protection effect, is wide in application range, better in fireproof performance and stronger in adhesive strength,and has better chemical corrosion resistance, better heat resistance, better acid-base resistance and better electrical insulating performance; the fireproof performance is slightly affected by timeand environments, the coating further has the advantages of lasting fire resistance, high inflaming retarding efficiency and the like, the flame retardant effect of the coating is strengthened, the effective fireproofing time of the coating is prolonged, the preparation method is simple and convenient, and the efficiency is high.
Description
technical field [0001] The invention relates to the technical field of coatings, in particular to a fireproof coating for aluminum plates and a production process thereof. Background technique [0002] Aluminum plate refers to the aluminum material with a thickness of more than 0.2mm to less than 500mm, a width of more than 200mm, and a length of less than 16m. With the progress of large equipment, there are more aluminum plates that can be as wide as 600mm). Aluminum plate refers to a rectangular plate processed by rolling aluminum ingots, which is divided into pure aluminum plate, alloy aluminum plate, thin aluminum plate, medium-thick aluminum plate, and patterned aluminum plate. The general aluminum plate often needs to be coated with fireproof paint during installation. Fireproof paint is to brush the paint on the surface of those flammable materials, which can improve the fire resistance of the material, slow down the speed of flame spread, or within a certain period ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more