Preparation method of anti-migration protein transportation carrier material
A carrier material and anti-migration technology, applied in the field of medical materials, can solve problems such as unfixation, postoperative instability, and difficult operation, and achieve good bioadhesion, prolong residence time, and improve the effect of action time
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0015] Example 1
[0016] Take pig tooth soap and vacuum freeze-dry, pulverize and pass through a 200-mesh sieve to obtain a sieved powder and add the sieved powder to a 55% ethanol solution by mass fraction, stir and mix, and place in a water bath at 65°C Heating for 2 hours, standing to cool to room temperature, filtering and collecting the filtrate, and rotating the filtrate to 1 / 5 of the original volume at 55°C to obtain the rotary evaporation liquid and adding it to a macroporous adsorption resin column, and then using a mass fraction of 30 % ethanol solution elution treatment, control the elution rate of ethanol solution to 2BV / h, after the elution is completed, collect the eluent and add mass fraction 5% chitosan solution to the eluent at a mass ratio of 1:8 , stirred and mixed and placed under 200W for ultrasonic dispersion for 10 minutes to obtain a dispersion; in parts by weight, weigh 45 parts of deionized water, 3 parts of glacial acetic acid, and 6 parts of nano-h...
Example Embodiment
[0017] Example 2
[0018] Take pig tooth soap and vacuum freeze-dry, pulverize and pass through a 200-mesh sieve to obtain a sieved powder and add the sieved powder to a 55% ethanol solution by mass fraction, stir and mix, and place in a water bath at 67°C Heating for 2 hours, standing to cool to room temperature, filtering and collecting the filtrate, and rotating the filtrate at 57°C to 1 / 5 of the original volume to obtain a rotary evaporation liquid and adding it to a macroporous adsorption resin column, and then using a mass fraction of 30 % ethanol solution elution treatment, control the elution rate of ethanol solution to 2BV / h, after the elution is completed, collect the eluent and add mass fraction 5% chitosan solution to the eluent at a mass ratio of 1:8 , stirred and mixed and placed under 250W for ultrasonic dispersion for 12 minutes to obtain a dispersion; in parts by weight, weigh 47 parts of deionized water, 4 parts of glacial acetic acid, and 7 parts of nano-hyd...
Example Embodiment
[0019] Example 3
[0020] Take pig tooth soap and vacuum freeze-dry, crush and pass through a 200-mesh sieve to obtain a sieved powder and add the sieved powder to a 55% ethanol solution with a mass fraction of 1:10, stir and mix, and place in a water bath at 70°C Heating for 3 hours, standing to cool to room temperature, filtering and collecting the filtrate, and rotating the filtrate at 60°C to 1 / 5 of the original volume to obtain the rotary evaporation liquid and adding it to a macroporous adsorption resin column, and then using a mass fraction of 30 % ethanol solution elution treatment, control the elution rate of ethanol solution to 2BV / h, after the elution is completed, collect the eluent and add mass fraction 5% chitosan solution to the eluent at a mass ratio of 1:8 , stirred and mixed and placed under 300W for ultrasonic dispersion for 15 minutes to obtain a dispersion; in terms of parts by weight, weigh 50 parts of deionized water, 5 parts of glacial acetic acid, and ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap