Production method of high temperature covering agent grade boron oxide

A production method and boron oxide technology, applied in the directions of boron oxides, boron oxide compounds, etc., can solve the problems of high vacuum degree requirements, small output, unstable dehydration effect, etc.

Active Publication Date: 2021-08-24
广东先导微电子科技有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method has the following disadvantages: directly dehydrating boric acid under a vacuum of 0.01 to 100 Pa will cause boric acid splashing and volatilization of boric acid powder, and the boric oxide splashed is adsorbed on the inner wall of the glass tube. During the subsequent high-temperature dehydration process, Boron oxide will cause crystallization or reaction with the inner wall of the quartz glass tube, resulting in product loss; and for the entire dehydration system, a high vacuum degree of less than 1 Pa is not easy to obtain, and it is difficult to maintain for a long time, which is not conducive to stable production and product quality control
The boron oxide production process adopted by the above methods has technical defects such as high calcination temperature, prone to burning of the crucible, severe boric acid or boron oxide splashing, high vacuum degree requirements, small output, and unstable dehydration effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of high temperature covering agent grade boron oxide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Dry 400g of boric acid powder with a purity of 5N at 100°C for 24 hours or more in advance, then divide it into two batches and put them into platinum crucibles, adjust the heating power of the intermediate frequency furnace, heat the boric acid to 600°C, and feed the two batches at an interval of 10 minutes . When the boric acid powder in the crucible is all in a transparent molten state and no longer bubbles, put 100g of anhydrous boron oxide with a purity of 5N into it. Adjust the heating power of the intermediate frequency furnace, heat the boron oxide to 900°C, and calcine for 15 minutes. Connect the vacuum system, turn on the vacuum switch, turn the valve to 1 / 3, and adjust the induction heating power to the set value. Observe the boiling of the melt, and control the splashing of the melt by controlling the tightness of the bottom valve. Pump the vacuum of the intermediate frequency furnace to below 50Pa within 40 minutes, tighten the bottom valve, and continue ...

Embodiment 2

[0029] Pre-dry 500g of boric acid powder with a purity of 5N at 100°C for 24 hours or more, divide it into two batches and put it into a platinum crucible, adjust the heating power of the intermediate frequency furnace, heat the boric acid to 700°C, and feed the two batches at an interval of 20 minutes. When the boric acid powder in the crucible is all in a transparent molten state and no longer bubbles, put 200g of anhydrous boron oxide with a purity of 5N into it. Adjust the heating power of the intermediate frequency furnace, heat the boron oxide to 950°C, and calcine for 30 minutes. Connect the vacuum system, turn on the vacuum switch, turn the valve to 1 / 4, and adjust the induction heating power to the set value. Observe the boiling of the melt, and control the splashing of the melt by controlling the tightness of the bottom valve. Pump the vacuum of the intermediate frequency furnace to below 50Pa within 50 minutes, tighten the bottom valve, and continue vacuum dehydrat...

Embodiment 3

[0031] Dry 600g of boric acid powder with a purity of 5N at 100°C for 24 hours or more in advance, and then divide it into two batches and put them into platinum crucibles. Adjust the heating power of the intermediate frequency furnace to heat the boric acid to 800°C. The interval between two batches of feeding is 30min. . When the boric acid powder in the crucible is all in a transparent molten state and no longer bubbles, drop 300g of anhydrous boron oxide with a purity of 5N into it. Adjust the heating power of the intermediate frequency furnace, heat the boron oxide to 1000°C, and calcine for 20 minutes. Connect the vacuum system, turn on the vacuum switch, turn the valve to 1 / 2, and adjust the induction heating power to the set value. Observe the boiling of the melt, and control the splashing of the melt by controlling the tightness of the bottom valve. Pump the vacuum of the intermediate frequency furnace to below 50Pa within 40 minutes, tighten the bottom valve, and c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
purityaaaaaaaaaa
melting pointaaaaaaaaaa
boiling pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a production method of high-temperature covering agent grade boron oxide, which comprises the following steps: S1, heating with boric acid; S2, adding anhydrous boron oxide; S3, calcining and dehydrating; S4, casting and molding. The production method of high-temperature covering agent-grade boron oxide of the present invention comprehensively considers production cost, production cycle, product quality stability, etc., does not adopt the lowest vacuum degree and the highest dehydration temperature, and produces the boron oxide that meets the requirements of high-temperature covering agent grade. Boron, and the product yield is not less than 95%.

Description

technical field [0001] The invention relates to the field of material preparation, in particular to a production method of high-temperature covering agent grade boron oxide. Background technique [0002] Liquid-enclosed crystal growth method (LEC) is a main method for preparing III-V compound semiconductors (such as gallium arsenide, gallium phosphide, and indium arsenide). Covered with a liquid phase layer to prevent the loss of volatile components of compound semiconductors. The liquid phase layer usually adopts boron oxide with purity ≥ 99.999% and water content ≤ 200ppm. [0003] The preparation method of existing anhydrous boron oxide mainly is following several. [0004] 1. Prepared by two-stage dehydration. Chinese patent application CN200810155689.X proposes a method for preparing high-temperature covering agent-grade boron oxide. In this method, boron oxide is first heated to 400-500°C in air and kept for half an hour; then boron oxide is heated to 1000°C in air ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B35/10
CPCC01B35/1027C01P2002/82C01P2006/80
Inventor 蔡新志朱刘刘留胡智向黄宇彬
Owner 广东先导微电子科技有限公司