Composition for preparing dental temporary crown bridge, and preparation method of composition

A composition and temporary technology, applied in dental preparations, dentistry, dental prosthesis, etc., can solve the problems of hardened materials such as rough spots, easy to break, and brittle materials, and achieve low oxygen inhibition layer, fast curing speed, and good toughness Effect

Active Publication Date: 2018-10-16
吉林省登泰克牙科材料有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

What's more serious is that a large number of air bubbles and hard lumps are produced, which are difficult to remove, which leads to coarse spots and strong stains on the hardened material
Also, due to their hardness, these materials are brittle and break easily

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0058] The present invention provides a kind of preparation method for making the composition of dental temporary crown and bridge as described in above-mentioned technical solution, comprising:

[0059] Mix and stir the acrylate monomer, silicone-modified acrylate, self-curing accelerator and filler to obtain the matrix component;

[0060] The acrylate monomer, silicone-modified acrylate, self-curing initiator and filler are mixed and stirred to obtain a matrix component.

[0061] The present invention has clearly described the specific components and proportions of the acrylate monomer, silicone-modified acrylate, self-curing accelerator and filler mixed above, and will not repeat them here. The specific way of stirring is not limited, and those familiar to those skilled in the art can be used; the stirring time is preferably 5-10 hours; stirring at room temperature is enough.

[0062] The present invention has clearly described the specific components and proportions of th...

Embodiment 1

[0067] The following components were stirred together to form the catalytic component (mass %):

[0068] Bisphenol A diglycidyl acrylate 30%

[0069] Tripropylene Glycol Diacrylate 15%

[0070] (1,1,3,3-Tetramethyldisiloxane-1,3-diyl)dipropane-1,3-diyl diacrylate 7%

[0071] Strontium glass powder 25%

[0072] Fumed silicon 3%

[0073] Barium glass powder 19%

[0074] 2,4-Dichlorobenzoyl peroxide 1%

[0075] The following components were stirred together to form the matrix component (mass %):

[0076] Bisphenol A diglycidyl acrylate 30%

[0077] Tripropylene Glycol Diacrylate 15%

[0078] (1,1,3,3-Tetramethyldisiloxane-1,3-diyl)dipropane-1,3-diyl diacrylate 7%

[0079] Strontium glass powder 25%

[0080] Fumed silicon 3%

[0081] Barium glass powder 19%

[0082] Dimethyl-p-toluidine 0.97%

[0083] Pigment 0.03%

[0084] Preparation method: the above-mentioned components, the matrix component and the catalytic component are mixed separately, and stirred at room tem...

Embodiment 2

[0087] The following components were stirred together to form a catalyst paste (mass %):

[0088] Ethoxylated Bisphenol A Dimethacrylate 32%

[0089] Triethylene glycol diacrylate 13%

[0090] (1,1,1,3,5,5,5-heptamethyl-3-trisiloxanyl)methacrylate 7%

[0091] Strontium glass powder 20%

[0092] Fumed silicon 3%

[0093] Barium glass powder 24%

[0094] Benzoyl Peroxide 1%

[0095] The following components were stirred together to form a base paste (mass %):

[0096] Ethoxylated Bisphenol A Dimethacrylate 32%

[0097] Triethylene glycol diacrylate 13%

[0098] (1,1,1,3,5,5,5-heptamethyl-3-trisiloxanyl)methacrylate 7%

[0099] Strontium glass powder 20%

[0100] Fumed silicon 3%

[0101] Barium glass powder 24%

[0102] Dimethyl-p-toluidine 0.97%

[0103] Pigment 0.03%

[0104] Preparation method: the above-mentioned components, the matrix component and the catalytic component are mixed separately, and stirred at room temperature for 6-8 hours.

[0105] Measurement...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
modulusaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a composition for preparing dental temporary crown bridge. The composition is prepared from a matrix component and a catalytic component, wherein the matrix component is prepared from 40-60 parts by weight of acrylate monomer, 1-10 parts by weight of organosilicon modified acrylate, 0.5-1 part by weight of self-curing accelerator and 40-50 parts by weight of filler; the catalytic component is prepared from 40-60 parts by weight of acrylate monomer, 1-10 parts by weight of organosilicon modified acrylate, 1-2 parts by weight of self-curing initiator and 40-50 parts by weight of filler. The composition for preparing the dental temporary crown bridge is prepared by means of cooperation of the acrylate monomer and the organosilicon modified acrylate and in combination ofa self-curing reaction of the curing accelerator, the filter and the curing initiator. The composition for preparing the dental temporary crown bridge is rapid in curing speed, high in strength and good in toughness, and also has the characteristic of being low in oxygen inhibition layer.

Description

technical field [0001] The invention relates to the technical field of materials, in particular to a composition for making dental temporary crowns and bridges and a preparation method thereof. Background technique [0002] A temporary crown, also known as a temporary crown, is a temporary full crown that is temporarily bonded in the patient's mouth after the preparation of the tooth for crown restoration and before the completion of the final crown restoration, and the patient cannot freely wear it. [0003] Traditional temporary crown materials consist of liquid / powder mixtures mixed together. The liquid in this combination consists essentially of a monofunctional monomer (such as methyl methacrylate) and an activator; the powder consists of a polymer (polymethyl methacrylate) and a catalyst. Systems of this type are easy to manipulate and they produce crowns and bridges that are significantly resistant to fracture. However, the aforementioned liquids are problematic. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61K6/083
CPCA61K6/889C08L33/08
Inventor 闫鹏涛慕琪吴慧殷锐马荣堂
Owner 吉林省登泰克牙科材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap