Biosoluble ultrafine glass wool and preparation method thereof

An ultra-fine glass fiber, soluble technology, applied in glass manufacturing equipment, manufacturing tools, etc., can solve the problems of life safety threats of production personnel and users, and achieve the effect of thin diameter, good thermal insulation effect and low thermal conductivity

Inactive Publication Date: 2018-10-16
CHONGQING MAGU FIBER NEW MATERIAL CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These products basically belong to the categories of European Union Class 2 "probable carcinogen" and Class 3 "probable carcinogen", which pose a potential threat to the safety of production personnel and users.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biosoluble ultrafine glass wool and preparation method thereof
  • Biosoluble ultrafine glass wool and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0029] Mix 372kg of quartz sand and 15kg of water in the mixer, then add 161kg of soda ash and 82kg of borax, and finally add 16kg of calcite, 93kg of dolomite, 40kg of feldspar and 136kg of cullet in order, stir and mix for 4min, and the rotating speed is 30rad / min; In a conventional horseshoe flame furnace, the above-mentioned mixture is melted, clarified and homogenized into liquid glass, the melting temperature is 1360°C, and the clarification and homogenization temperature is 1100°C-1200°C; the above-mentioned liquid glass is introduced into a high-speed rotating centrifuge at high speed Centrifugal fiberization, the temperature of the liquid glass root stream is 1050°C, the average temperature of the centrifuge is 980°C, and the rotation speed is 3000rad / min; the above-mentioned high-speed fiberized liquid glass is stretched by gradient high-temperature airflow, the top airflow temperature is 1400°C, and the bottom The air temperature is 1100°C and the air flow is 42m 3 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses biosoluble ultrafine glass wool and a preparation method thereof. The biosoluble ultrafine glass wool comprises the following chemical components by mass: 60-68 parts of SiO2,0 to 3 parts of Al2O3, 6 to 12 parts of CaO and MgO, 15 to 20 parts of Na2O and K2O, 4 to 4.9 parts of B2O3, 3 to 5 parts of BaO, and no more than 4 parts of Fe2O3, SO3, ZrO2 and CeO2, wherein the content of CeO2 is not less than 0.5 part. The biosoluble ultrafine glass wool has good biosolubility and thermal insulation properties; the ultrafine glass wool has a small fiber diameter and a low thermal conductivity (wherein thermal conductivity at room temperature can be as low as 0.03 W / (m.K)), and is good in heat preservation effect; once the glass wool is inhaled into a respiratory system byan organism, or even enters the lung, the half-life of the glass wool is less than 40 days, and the glass wool can be quickly dissolved by the lung fluid of the organism and does not cause any inflammation.

Description

technical field [0001] The invention relates to a glass wool and a preparation method thereof, in particular to a biosoluble ultrafine glass wool and a preparation method thereof. Background technique [0002] At present, fire-proof porous inorganic fiber thermal insulation materials, such as glass wool, mineral wool and rock wool, have been widely used in thermal insulation and energy-saving fields such as heat pipes, home appliances, refrigeration, construction and industry. Traditional inorganic fiber materials belong to SiO 2 、Al 2 o 3 It is a silicate fiber, which has excellent thermal insulation performance, chemical stability and corrosion resistance. However, the diameter of the fiber is small, so it is easily inhaled into the lungs by the human respiratory system during production and use, and cannot be completely dissolved after a long time, thus posing a potential threat to human health. In 2001, the International Agency for Research on Cancer (IARC) carried o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C6/04C03C6/02C03C3/089C03C3/093C03B37/04C03B37/02
CPCC03C1/002C03B37/02C03B37/0213C03B37/04C03C3/089C03C3/093
Inventor 陈舟祝坤
Owner CHONGQING MAGU FIBER NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap