A kind of silk fibroin medical bioadhesive and preparation method thereof

A bio-adhesive, silk fibroin technology, applied in pharmaceutical formulations, surgical adhesives, applications, etc., can solve the problems of low adhesive strength, long coagulation time, troublesome storage, etc., and achieve super-strong adhesion performance, good Biocompatible, easy-to-use effect

Active Publication Date: 2021-04-27
FUZHOU UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention overcomes the problems of low bonding strength, long setting time and troublesome storage of existing bioadhesives, and the prepared silk fibroin medical bioadhesive can be used for almost all trauma wounds, and has the advantages of bonding tissues, covering Wounds, filling defects and gaps, hemostasis, antibacterial, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of silk fibroin medical bioadhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Preparation of silk fibroin solution

[0019] After heating 2L of deionized water to boiling, add 6 g of sodium carbonate and wait until it is fully dissolved. Put 5 g silkworm raw silk into it, and degummed it at 100 °C. Wash thoroughly with deionized water and dry in an oven at 60 °C. The dried degummed silk fibroin fibers were dissolved in LiBr solution at 60 °C for 6 h. The dissolved solution was put into a dialysis bag and dialyzed against deionized water for 72 h. The dialyzed solution was filtered and centrifuged to obtain a silk fibroin solution with a mass fraction of about 20% after repeated twice. 10 g of catechol was dissolved in slightly alkaline Tris-HCl buffer and stirred for 0.5 h to obtain a 10% catechol solution. At room temperature, 10% catechol solution and 20% silk fibroin solution were uniformly mixed for 0.5 h at a mass ratio of 800:1 to obtain a silk fibroin adhesive with adhesive properties. The adhesive can be used for hemostatic adhesion ...

Embodiment 2

[0021] After heating 10L of deionized water to boiling, add 50g of sodium carbonate and wait until it is fully dissolved. Put 25 g silkworm raw silk into it, and degumming process at 90 °C. Wash thoroughly with deionized water and dry in an oven at 50 °C. The dried degummed silk fibroin fibers were dissolved in LiBr solution at 80 °C for 3 h. The dissolved solution was put into a dialysis bag and dialyzed against deionized water for 60 h. The dialyzed solution was filtered and centrifuged to obtain a silk fibroin solution with a mass fraction of about 40% after repeated twice. 500 g of tannic acid was dissolved in slightly alkaline Tris-HCl buffer and stirred for 50 h to obtain a 500% tannic acid solution. At room temperature, a 500% tannic acid solution and a 40% silk fibroin solution were uniformly mixed for 30 h at a mass ratio of 1:1 to obtain a silk fibroin adhesive with adhesive properties. The adhesive can be used for hemostatic adhesion of organs, bones, joints and...

Embodiment 3

[0023] After heating 15L of deionized water to boiling, add 100 g of sodium carbonate and wait for it to fully dissolve. Put 15 g silkworm raw silk into it, and degummed it at 80 °C. Wash thoroughly with deionized water and dry in an oven at 70 °C. The dried degummed silk fibroin fibers were dissolved in a calcium chloride / absolute ethanol / water ternary solution at 60°C for 6 h. The dissolved solution was put into a dialysis bag and dialyzed against deionized water for 40 h. The dialyzed solution was filtered and centrifuged to obtain a silk fibroin solution with a mass fraction of about 5% after repeated twice. Dissolve 1 g of epicatechin in water and stir for 30 h to obtain a 1% epicatechin solution. At room temperature, a 1% epicatechin solution and a 5% silk fibroin solution were uniformly mixed for 50 h at a mass ratio of 1:600 ​​to obtain a silk fibroin adhesive with adhesive properties. The adhesive can be used for hemostatic adhesion of tissues such as nerves, muco...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a silk fibroin medical bioadhesive and a preparation method thereof, belonging to the fields of biomaterial preparation and biomedical application. The adhesive is prepared by uniformly mixing silk fibroin solution and polyphenol polymer solution at room temperature. The silk fibroin bioadhesive prepared by the invention has the characteristics of high bonding strength in a humid environment, fast bonding speed, safety and non-toxicity, good biocompatibility, low price and the like. Its operation is simple and easy to master, and there is no need for secondary operations such as stitches removal after surgery, which reduces the pain of patients, and the small or even scarless wounds also play a cosmetic role. , covering wounds, filling defects and gaps, hemostasis, antibacterial, etc., can be used as a hemostatic adhesive material for skin, organs, blood vessels, nerves, muscles, mucous membranes, bones, joints, eyes and other tissues, and has a wide range of clinical application prospects .

Description

technical field [0001] The invention belongs to the field of biomaterial preparation and biomedical application, and in particular relates to a silk fibroin medical bioadhesive and a preparation method thereof. Background technique [0002] According to statistics, millions of people need surgical treatment every year due to trauma, which mainly includes skin, muscle, connective tissue, internal organs, bone and so on. The most commonly used method clinically is to suture the wound with sutures, rivets and other materials. This method ensures that the suture is firm and the wound is not easy to crack. Patients have thread-knot reactions to varying degrees, leaving "centipede"-like scars after surgery. With the rapid development of modern medicine, the clinical requirements for surgical methods and auxiliary materials are getting higher and higher, not only to reduce the pain of patients to the greatest extent, but also to restore the appearance perfectly while restoring the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L24/10A61L24/00A61L24/04
CPCA61L24/001A61L24/046A61L24/108A61L2400/04C08L89/00
Inventor 白树猛张雪亮杨黄浩黄晓卫
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com