Waterproof and antiskid paint composition and use method

A technology of anti-skid coating and composition, applied in the direction of coating, etc., can solve the problems of complicated construction, low surface friction coefficient, rough surface, etc.

Active Publication Date: 2018-11-09
东胜军
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, although the ordinary solvent-based epoxy floor paint on the market is convenient for construction, clean and stain-resistant, its surface friction coefficient is low and cannot achieve anti-skid effect. The common practice is to add quartz to the ordinary solvent-based epoxy floor paint Sand is made into a rough surface to achieve the anti-slip effect. This method has the problems of rough surface, poor stain resistance, poor cleaning performance, and cumbersome construction. It is not suitable for anti-slip coating in indoor places.
At the same time, ordinary floor paint does not have a composition design for waterproofing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Prepare materials by weight. Among them, component A is: 15 parts of silicone rubber emulsion, 3 parts of siloxane, 3.5 parts of titanium dioxide, 3.5 parts of sodium carbonate, 0.8 parts of magnesium oxide, 6 parts of calcined clay, 0.5 parts of antibacterial agent, and 0.3 parts of defoaming agent , 0.2 parts of sodium hexametaphosphate, 2.5 parts of calcium sulfate, 7 parts of silicon micropowder, 10 parts of ethanol, and 17 parts of water. Among them, component B is: 20 parts of acrylic acid emulsion, 4 parts of ethanol, 7 parts of ethyl orthosilicate, 8 parts of montmorillonite, and 1.5 parts of persulfate. The mass ratio of component A and component B is 0.8:1.

[0035] Fully mix and stir the various substances in component A, fully mix and stir the various substances in component B, add component B to component A according to the proportion, mix and stir uniformly, and obtain the coating composition . The waterproof and anti-skid coating composition prepared a...

Embodiment 2

[0037] The coating composition was prepared according to the ingredients and ratios in Example 1, the only difference being that the silicon micropowder and the organic solvent in component A were provided by 10 parts of silicon wafer cutting waste liquid.

Embodiment 3

[0039] Prepare the coating composition according to the ingredients and ratios in Example 1, the only difference is that, using the layered coating method, the first layer is coated with 1.2 mm of component A, and the second layer is coated with 1 mm of component B.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a waterproof and antiskid paint composition. An organic silicon rubber emulsion and an acrylic emulsion are utilized for forming a paint matrix, and siloxane, ethyl orthosilicate and silica powder are utilized for forming a siliceous particle-gel composite cross-linked network, so that the elasticity of a formed coating is increased, and the coating can adapt to more micro-deformations without cracking; and wrinkles are formed on the surface of the organic matrix by utilizing a common drying process, and simultaneously, micro salient points are further formed on the surfaces of the wrinkles in the presence of siliceous particles, thereby obtaining a better antiskid property. The invention also provides a method for preparing a waterproof and antiskid coating by utilizing the paint composition. The paint is prepared from a component A and a component B which are capable of reacting, and the component A and the component B are mixed and then covered or are coveredin a layered mode.

Description

technical field [0001] The invention relates to a coating composition and its application method, in particular to a waterproof and anti-skid coating composition and its application method. Background technique [0002] With the improvement of residents' living standards, indoor sports and fitness activities have gradually become one of the main ways of residents' leisure and entertainment. Coatings can provide anti-slip coatings in indoor sports venues to avoid slipping and falling injuries when sports methods are improper or negligent. For example, there is a demand for anti-slip in indoor badminton halls, table tennis halls, and even swimming pools. At the same time, considering the complexity of the indoor sports environment and the special effect of indoor waterproof requirements, higher requirements are also put forward for the waterproof performance of this coating. [0003] At present, although the ordinary solvent-based epoxy floor paint on the market is convenien...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/00C09D183/04C09D7/61
CPCC08K2003/2241C08K2003/265C09D7/61C09D133/00C08L83/04C08K3/36C08K3/22C08K3/26C08K3/346C08K3/00C08K7/14C08K13/04C08K7/28
Inventor 米战康冬白寅昆晁敏
Owner 东胜军