Honing fluid and preparation method thereof

A honing fluid and extreme pressure additive technology, applied in the petroleum industry, lubricating compositions, etc., can solve problems affecting the health of operators, kerosene polluting the environment, kerosene is flammable and explosive, etc., to prevent sedimentation and particle growth, improve Effects of Suspension Ratio, Enhanced Low-Temperature Storage Stability and High-Temperature Storage Stability

Active Publication Date: 2018-11-16
安徽万协智能科技集团有限公司
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, kerosene pollutes the environment, affects the health of operators, and is also a major hidden danger in production. Kerosene is flammable and explosive at around 35°C, and is most prone to fire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of honing fluid, described honing fluid is counted in parts by weight, comprises extreme pressure additive 10kg, penetrating agent 13kg, antirust agent 8kg, bactericide 2kg, softening agent 0.5kg, defoamer 0.1kg, lubricant 6kg, dispersion Agent 8kg, distilled water 20kg.

[0029] The extreme pressure additive is oleic acid diethanolamine borate.

[0030] The penetrating agent is polyethylene glycol oleate.

[0031] The fungicide is a triazine fungicide, methylene bismorpholine or 1,2-benzisothiazol-3-one.

[0032] The softener is EDTA disodium salt.

[0033] The defoamer is a silicone defoamer.

[0034] The present invention also provides a kind of preparation method of honing fluid:

[0035] (1) Heat and stir the extreme pressure additive, penetrant, bactericide and distilled water for 5-8 minutes, and set the heating temperature to 35-45°C to prepare solution A;

[0036] (2) Evenly mix and stir the softener, defoamer, lubricant, and rust inhibitor, and the...

Embodiment 2

[0041] A kind of honing fluid, described honing fluid is counted in parts by weight, comprises extreme pressure additive 10kg, penetrating agent 13kg, antirust agent 8kg, bactericide 2kg, softening agent 0.5kg, defoamer 0.1kg, lubricant 6kg, dispersion Agent 8kg, distilled water 20kg.

[0042] The extreme pressure additive is oleic acid diethanolamine borate.

[0043] The penetrating agent is polyethylene glycol oleate.

[0044] The fungicide is a triazine fungicide, methylene bismorpholine or 1,2-benzisothiazol-3-one.

[0045] The softener is EDTA disodium salt.

[0046] The defoamer is a silicone defoamer.

[0047] Described dispersion agent is made by following steps:

[0048] (1) Ultrasonic-microwave co-processing of β-cyclodextrin: add β-cyclodextrin into water (the mass ratio of the two is 1:9), disperse evenly, place it in an ultrasonic-microwave co-extractor, and set the ultrasonic The frequency is 40kHz, the ultrasonic power is 50W, the microwave frequency is 245...

Embodiment 3

[0058] A kind of honing fluid, described honing fluid is counted in parts by weight, comprises extreme pressure additive 10kg, penetrating agent 13kg, antirust agent 8kg, bactericide 2kg, softening agent 0.5kg, defoamer 0.1kg, lubricant 6kg, dispersion Agent 8kg, distilled water 20kg.

[0059] The extreme pressure additive is oleic acid diethanolamine borate.

[0060] The penetrating agent is polyethylene glycol oleate.

[0061] The bactericide is a triazine bactericide.

[0062] The softener is EDTA disodium salt.

[0063] The defoamer is a silicone defoamer.

[0064] Described dispersion agent is made by following steps:

[0065] (1) Ultrasonic-microwave co-processing of β-cyclodextrin: add β-cyclodextrin into water (the mass ratio of the two is 1:9), disperse evenly, place it in an ultrasonic-microwave co-extractor, and set the ultrasonic The frequency is 40kHz, the ultrasonic power is 50W, the microwave frequency is 2450MHz, and the microwave power is 700W. After refl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a honing fluid and a preparation method thereof. The honing fluid which is characterized by measurements in mass percentage comprises an extreme pressure additive 10-15, a penetrant 10-25, a rust inhibitor 5-10, a fungicide 0.5-3, a softener 0.1-0.5, a defoamer 0.1-0.2, a lubricant 5-15, a dispersant 7-10 and distilled water 20-45. The design is simple to operate, comprehensive and practical, and easy to popularize.

Description

Technical field: [0001] The invention relates to the technical field of metalworking fluid applications, in particular to a honing fluid and a preparation method thereof. Background technique: [0002] At present, in mechanical processing, kerosene or similar mineral oil products are mainly used for honing and polishing. In foreign countries, the honing oil of Chrysler Company in the United States is refined mineral oil with a viscosity of 5.0mm2 / s (40°C). In China, mineral oil-based honing oils are used in Shanghai Santana Plant and the Second Automobile Manufacturing Plant. The source of this type of mineral oil type honing oil is very important. And it's expensive and volatile. Flammable and explosive. Since the start of production in our factory, kerosene has been used for honing and polishing in mechanical processing, because kerosene has good cleaning and permeability. FAW consumes more than 300 tons of kerosene every year, and because the country canceled the ori...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/02C10N30/06C10N30/16C10N30/04
CPCC10M173/02C10M2201/081C10M2201/102C10M2207/042C10M2207/402C10M2209/103C10M2209/104C10M2209/107C10M2209/12C10M2215/04C10M2217/044C10M2219/104C10M2227/061C10N2030/04C10N2030/06C10N2030/16C10N2010/06C10N2010/02C10N2010/04
Inventor 张建峰姚运厂姚文礼朱卫士
Owner 安徽万协智能科技集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More