Preparation method of fire-proof fabric

A fire-resistant fabric and fabric technology, applied in the field of fabrics, can solve the problems of uncomfortable wearing, poor fireproof performance, rough appearance, etc., and achieve the effect of improving fireproof effect, fireproof performance and compatibility

Inactive Publication Date: 2018-11-16
HEFEI MINGYOU HIGH TEMPERATURE TECH CO LTD
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its disadvantage is that it is not very comfortable to wear, and its appearance is rough and stiff.
[0003] The existing Chinese patent document (publication number: CN102137895B) discloses a fabric composition, a fabric prepared from the composition, a laminated fabric comprising the fabric, and a composite fabric comprising the laminated fabric, wherein the fabric composition Containing at least one of polystyrene-based copolymers and ethylene-vinyl acetate-based copolymers, the fabric has poor fire resistance
[0004] Chinese patent document (publication number: CN107190404B) discloses a graphene and bio-based fiber knitted fabric and its production process, which belongs to the textile field. Blended yarn, the reverse side is composed of sorona bio-based fiber with pipe moisture-wicking structure. The fabric has antibacterial, anti-mite, antistatic and anti-radiation properties, but has poor fire resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The preparation method of a fireproof fabric of this embodiment includes the following steps:

[0027] Step 1: The nylon and cotton are slivered, spun, and weave according to the weight ratio of 3:1 to obtain a blended fabric. Then the blended fabric is soaked in a basalt fiber solution for 12 minutes, and then dried at a drying temperature of 105r / min, and then fed into the nano organic montmorillonite grafted diphenyl phosphate, soaked in flame retardant solution for 12 minutes, and then dried to obtain the mixed fabric A;

[0028] Step two, prepare the soaking agent: add epoxidized triglyceride, isopropyl p-hydroxybenzoate, and glycerin to a magnetic stirrer, the stirring speed is increased to 115r / min, the stirring time is 25min, and then the nanometer Silica, talcum powder, small red mud, volcanic mud, continue to stir for 15 minutes to obtain soaking agent;

[0029] Step three, soak the mixed fabric A in step one for 15 minutes in the soaking agent, and then dry it to ...

Embodiment 2

[0037] The preparation method of a fireproof fabric of this embodiment includes the following steps:

[0038] Step 1: Nylon and cotton are slivered, spun and woven according to a weight ratio of 3:1 to obtain a blended fabric. Then the blended fabric is soaked in a basalt fiber solution for 18 minutes, and then dried at 115r / min, then feed into the nano-organic montmorillonite grafted diphenyl phosphate, soaked in flame retardant solution for 18 minutes, and then dried to obtain mixed fabric A;

[0039] Step two, prepare the soaking agent: add epoxidized triglyceride, isopropyl p-hydroxybenzoate, and glycerin to a magnetic stirrer, the stirring speed is increased to 125r / min, the stirring time is 35min, and then the nanometer Silica, talcum powder, small red mud, volcanic mud, continue to stir for 25 minutes to obtain soaking agent;

[0040] Step 3: Soak the mixed fabric A in step 1 in the soaking agent for 25 minutes, and then dry it to obtain a fireproof fabric.

[0041] The finen...

Embodiment 3

[0048] The preparation method of a fireproof fabric of this embodiment includes the following steps:

[0049] Step 1: Nylon and cotton are slivered, spun and woven according to a weight ratio of 3:1 to obtain a blended fabric. Then the blended fabric is soaked in a basalt fiber solution for 15 minutes, and then dried at 110r / min, then feed into the nano-organic montmorillonite grafted diphenyl phosphate, soaked in flame retardant solution for 15 minutes, and then dried to obtain mixed fabric A;

[0050] Step two, prepare the soaking agent: add epoxidized triglyceride, isopropyl p-hydroxybenzoate, and glycerol into a magnetic stirrer, the stirring speed is increased to 120r / min, the stirring time is 30min, and then the nanometer Silica, talcum powder, small red mud, volcanic mud, continue to stir for 20 minutes to obtain soaking agent;

[0051] Step 3: Soak the mixed fabric A in step 1 in the soaking agent for 20 minutes, and then dry it to obtain a fireproof fabric.

[0052] The fin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a fire-proof fabric. The preparation method comprises following steps: 1, nylon and cotton are subjected to strip forming, spinning, and weaving at a weight ratio of 3:1 so as to obtain a blended fabric; the blended fabric is immersed in a basalt fibre solution for 12 to 18min, is dried at 105 to 115r / min, is immersed in a nanometer organic montmorillonite grafted dibenzyl phosphate fire resistant fluid for 12 to 18min, and dried so as to obtain a blended fabric A. The fabric flame resistance is improved greatly compared with that in the prior art, and relatively high application value and relatively promising application prospect are achieved.

Description

Technical field [0001] The invention relates to the technical field of fabrics, in particular to a method for preparing fireproof fabrics. Background technique [0002] Fabric is the material used to make clothing. As one of the three elements of clothing, fabrics can not only interpret the style and characteristics of clothing, but also directly affect the color and shape of clothing. Cotton cloth is the general term for all kinds of cotton textiles. Cotton cloth is divided into cotton, rayon and other varieties. It is mostly used to make fashion, casual wear, underwear and shirts. Its advantages are easy to keep warm, soft and close-fitting, moisture absorption, and good air permeability. Its disadvantages are easy shrinkage and wrinkle, and the appearance is not very stiff and beautiful. It must be ironed frequently; hemp is a fabric made of hemp, flax, ramie, jute, sisal, abaca and other hemp plant fibers. It is generally used to make casual wear and work wear. For ordinary...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M11/79D06M13/292D06M13/224D06M13/148D06M13/453D03D15/00D04B1/14D04B21/00D06M101/06D06M101/34D03D15/217D03D15/283D03D15/47
CPCD04B1/14D04B21/00D06M11/79D06M13/148D06M13/224D06M13/2243D06M13/2246D06M13/292D06M13/453D10B2331/02D10B2201/02D06M2101/34D06M2200/30D06M2101/06D03D15/47
Inventor 王虎
Owner HEFEI MINGYOU HIGH TEMPERATURE TECH CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com