Nuclear power station reactor core cooling system safety injection box composite steel plate and manufacturing method thereof

A technology for core cooling and clad steel plates, which is applied in the field of clad steel plates for nuclear power and its manufacturing, can solve the problems of shortening the quenching and tempering heat treatment cycle of steel plates, poor shear strength plate shape, and reducing production costs, etc., to achieve excellent strength and toughness properties and Intergranular corrosion resistance, excellent strength and toughness, and good composite effect

Inactive Publication Date: 2018-12-14
ANGANG STEEL CO LTD
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a composite steel plate for the safety injection tank of the core cooling system of a nuclear power plant and its manufacturing method. It is designed in terms of composite plate blanks, and combined with suitable heating, rolling and heat treatment processes, it solves the problem of composite plate shearing. The problem of relatively poor shear strength, bonding ratio and plate shape after heat treatment, at the same time shortens the quenching and tempering heat treatment cycle of steel plates and reduces production costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nuclear power station reactor core cooling system safety injection box composite steel plate and manufacturing method thereof
  • Nuclear power station reactor core cooling system safety injection box composite steel plate and manufacturing method thereof
  • Nuclear power station reactor core cooling system safety injection box composite steel plate and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] The following embodiments are used to specifically illustrate the content of the present invention, and these embodiments are only a general description of the content of the present invention, and do not limit the content of the present invention.

[0028] The chemical composition of the carbon steel in the clad steel plate meets the requirements of ASME SA-533 "Quenching and Tempering Manganese-Molybdenum and Manganese-Molybdenum Nickel Alloy Steel Plate for Pressure Vessels", the weight percentage is C≤0.25%, Mn: 1.07%~1.62% , P≤0.025%, S≤0.025%, Si: 0.13%~0.45%, Mo: 0.41%~0.64%, Ni: 0.37%~0.73%, the balance is Fe and inevitable impurity elements; 304L austenitic stainless steel The composition meets the requirements of ASTM A240 Standard "Standard Specification for Chromium and Chromium Nickel Stainless Steel Plates, Sheets and Strips for Pressure Vessels and General Purposes", the weight percentage is C≤0.03%, Mn≤2.0%, Si≤0.75% , P≤0.045%, S≤0.030%, Cr: 17.5%~19.5%, N...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nuclear power station reactor core cooling system safety injection box composite steel plate and a manufacturing method thereof. The steel plate is composed of carbon steel of tempered sorbite organization and 304L austenitic stainless steel. The steel billets are symmetrically compounded, an upper layer and a lower layer are carbon steel, two layers in the middle are stainless steel, and an isolating agent is added between the two layers of the stainless steel. The vacuum degree of a composite billet is 1.0-5.0 x 10<-2>Pa. A heating temperature is 1200-1250 DEG C, heating time is 10-15 hours, a single-pass pressing rate is 5%-15%, and the final rolling temperature is larger than or equal to 1000 DEG C. The quenching temperature is 890-920 DEG C, the heat preservation time is 2-3 min / mm, the temperature rising rate is 1.0-1.5min / mm, and water is cooled to be less than or equal to 100 DEG C after being discharged from a furnace. The tempering temperature is 630-660 DEG C, the heat preservation time is 4-6 min / mm, and the temperature rising rate is 1.5-2.0 min / mm. According to the manufacturing method, the produced steel plate has high normal temperature andhigh temperature performance, good shearing strength and bonding strength, and meets requirements for the steel usage by the nuclear station.

Description

Technical field [0001] The invention belongs to the technical field of metal composite plate production, and particularly relates to a composite steel plate for nuclear power and a manufacturing method thereof. Background technique [0002] Heterogeneous composite steel plates are materials for key equipment such as nuclear island regulators and safety injection boxes. Due to the particularity of their application environment, it is necessary to ensure that they have both high mechanical properties and good corrosion resistance. The manufacturing method of the equipment is: surfacing a layer of stainless steel outside the carbon steel that plays a role of strength, and relying on the thickness of the surfacing to maintain the quality of the stainless steel, but the production cycle of this manufacturing method is long and the uneven heat of the surfacing process will cause the equipment Severe deformation; another manufacturing method is currently using explosive composite techno...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D1/25C21D8/02C22C38/00C22C38/02C22C38/04C22C38/08C22C38/12C22C38/58
CPCC22C38/04C21D1/25C21D8/0226C22C38/002C22C38/02C22C38/08C22C38/12C22C38/58
Inventor 颜秉宇孙殿东王长顺胡海洋王爽刘祥李文斌段江涛胡昕明欧阳鑫
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com