Corrosion-resistant cobalt alloy with excellent casting property for surface boat and submarine

A casting performance, submarine technology, applied in the field of alloys, can solve the problem of not being able to effectively fill the gaps between dendrites, and achieve the effect of high density and excellent mechanical properties

Inactive Publication Date: 2018-12-18
GUANGZHOU YUZHI TECH CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, during the solidification process of the alloy, the dendrite backbone and side branches are formed by the precipitation of the first phase, so that the subsequent melt cannot effectively fill the gaps between the dendrites, and it will also promote the formation of pores and porosity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A corrosion-resistant cobalt alloy with excellent casting properties for surface craft and submarines. In terms of weight percentage, the composition of the alloy is Ba:1.0wt.%, In:4.0wt.%, Ag:1.5wt.%, W:0.4wt.%, Bi:2.0wt.%, V:0.4wt.% , Ge: 2.0wt.%, Re: 0.2wt.%, and the balance is cobalt. The above-mentioned corrosion-resistant cobalt alloy with excellent casting performance for surface boats and submarines comprises the following steps: adding the above proportioned raw materials into an induction furnace under an argon environment, and using a graphite crucible; melting at 1600 degrees Keep warm for 10 minutes, stir evenly with high-frequency induction furnace electromagnetically; after stirring evenly, keep warm at 1600 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 50-100mm, and uses water cooling to cool down. Heat the obtained ingot at room temperature to 1650-1700 degrees and keep it warm for 10 minutes; then...

Embodiment 2

[0021] A corrosion-resistant cobalt alloy with excellent casting properties for surface craft and submarines. In terms of weight percentage, the composition of the alloy is Ba:1.5wt.%, In:6.0wt.%, Ag:2.0wt.%, W:0.8wt.%, Bi:3.0wt.%, V:0.6wt.%. , Ge: 3.4wt.%, Re: 0.4wt.%, and the balance is cobalt. The above-mentioned corrosion-resistant cobalt alloy with excellent casting performance for surface boats and submarines comprises the following steps: adding the above proportioned raw materials into an induction furnace under an argon environment, and using a graphite crucible; melting at 1600 degrees Keep warm for 10 minutes, stir evenly with high-frequency induction furnace electromagnetically; after stirring evenly, keep warm at 1600 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 50-100mm, and uses water cooling to cool down. Heat the obtained ingot at room temperature to 1650-1700 degrees and keep it warm for 10 minutes; the...

Embodiment 3

[0024] A corrosion-resistant cobalt alloy with excellent casting properties for surface craft and submarines. In terms of weight percentage, the composition of the alloy is Ba:1.2wt.%, In:4.5wt.%, Ag:1.8wt.%, W:0.6wt.%, Bi:2.5wt.%, V:0.5wt.% , Ge: 2.8wt.%, Re: 0.3wt.%, and the balance is cobalt. The above-mentioned corrosion-resistant cobalt alloy with excellent casting performance for surface boats and submarines comprises the following steps: adding the above proportioned raw materials into an induction furnace under an argon environment, and using a graphite crucible; melting at 1600 degrees Keep warm for 10 minutes, stir evenly with high-frequency induction furnace electromagnetically; after stirring evenly, keep warm at 1600 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 50-100mm, and uses water cooling to cool down. Heat the obtained ingot at room temperature to 1650-1700 degrees and keep it warm for 10 minutes; then...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a corrosion-resistant cobalt alloy with excellent casting property for a surface boat and a submarine. The alloy consists of the following components in percentage by weight: 1.0-1.5wt% of Ba, 4.0-6.0wt% of In, 1.5-2.0wt% of Ag, 0.4-0.8wt% of W, 2.0-3.0wt% of Bi, 0.4-0.6wt% of V, 2.0-3.4wt% of Ge, 0.2-0.4wt% of Re and the balance of cobalt. The material provides a novel materials science scheme for a corrosion-resistant cobalt alloy used under a marine environment, and also provides the cobalt alloy with excellent casting property. The alloy is implemented and industrialized, so that commercial upgrading needs, on the high-end cobalt alloy material, of the surface boat and submarine field in China are greatly promoted.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a cobalt alloy. Background technique [0002] Superalloys, also known as heat-strength alloys, heat-resistant alloys or superalloys, are based on Fe, Co and Ni, and are austenitic alloy materials that can withstand relatively large and complex stresses while maintaining surface stability when used above 600 degrees. Due to its good heat resistance, high strength, excellent ductility, hot workability, weldability, fatigue resistance and corrosion resistance, superalloys are widely used in fields such as petrochemical, thermoelectric, nuclear power, and transportation. fields, aerospace and defense, etc. Especially in today's top aero-engine field, the usage of superalloys is about 50% of the total. [0003] Superalloys originated in the 1930s, because the aerospace conditions required the use of high-temperature resistant materials to prepare turbochargers, so superalloys appeare...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C19/07C22C1/02C22F1/10
CPCC22C1/02C22C19/07C22F1/10
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com