Preparing method for ultra-thin galvanized plate
A galvanized sheet, ultra-thin technology, applied in hot-dip plating process, coating, metal material coating process and other directions, can solve the problems of not achieving good results, poor economic benefits, polluting the environment, etc., to improve product quality , Increase the temperature and ensure the effect of hardenability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0022] Example 1:
[0023] A preparation method of ultra-thin galvanized sheet includes the following steps:
[0024] (1) Steel strip pretreatment: the carbon steel cold-rolled sheet is first brushed with 5% hydrochloric acid and then washed with water; then washed with 22% sodium hydroxide, then washed with water, and finally with water Dry after spray washing treatment;
[0025] (2) The configuration of the zinc pot solution: the weight percentage of the chemical composition in the zinc pot solution is Al (aluminum): 24.51%, Fe (iron): 0.379%, B (boron): 0.0002%, Mg (magnesium): 0.0140 %, Cu (copper): 0.0231%, Mn (manganese): 0.0055%, Si (silicon): 0.171%, Pb (lead): 0.066%, Sb (antimony): 0.0188%, Ti (titanium): 0.0135%, Sn (tin): 0.053%, Cd (cadmium): 0.041%, Cr (chromium): 0.050%, Zn (zinc): 74.6549%;
[0026] (3) Steel strip annealing treatment: Put the steel strip pretreated in step 1) into the annealing reduction furnace, change the process control mode of the annealing redu...
Example Embodiment
[0032] Example 2:
[0033] A preparation method of ultra-thin galvanized sheet includes the following steps:
[0034] (1) Steel strip pretreatment: the carbon steel cold-rolled sheet is first brushed with 5% hydrochloric acid, then rinsed with water; then washed with 25% sodium hydroxide, then washed with water, and finally with water Dry after spray washing treatment;
[0035] (2) The configuration of the zinc pot solution: the weight percentage of the chemical composition in the zinc pot solution is Al (aluminum): 24.51%, Fe (iron): 0.379%, B (boron): 0.0002%, Mg (magnesium): 0.0140 %, Cu (copper): 0.0231%, Mn (manganese): 0.0055%, Si (silicon): 0.171%, Pb (lead): 0.066%, Sb (antimony): 0.0188%, Ti (titanium): 0.0135%, Sn (tin): 0.053%, Cd (cadmium): 0.041%, Cr (chromium): 0.050%, Zn (zinc): 74.6549%;
[0036] (3) Steel strip annealing treatment: Put the steel strip pretreated in step 1) into the annealing reduction furnace, change the process control mode of the annealing reducti...
Example Embodiment
[0042] Example 3:
[0043] A preparation method of ultra-thin galvanized sheet includes the following steps:
[0044] (1) Steel strip pretreatment: the carbon steel cold-rolled sheet is first scrubbed with 5% hydrochloric acid, then rinsed with water; then after scrubbing with 30% sodium hydroxide, then scrubbed with water, and finally with water Dry after spray washing treatment;
[0045] (2) The configuration of the zinc pot solution: the weight percentage of the chemical composition in the zinc pot solution is Al (aluminum): 24.51%, Fe (iron): 0.379%, B (boron): 0.0002%, Mg (magnesium): 0.0140 %, Cu (copper): 0.0231%, Mn (manganese): 0.0055%, Si (silicon): 0.171%, Pb (lead): 0.066%, Sb (antimony): 0.0188%, Ti (titanium): 0.0135%, Sn (tin): 0.053%, Cd (cadmium): 0.041%, Cr (chromium): 0.050%, Zn (zinc): 74.6549%;
[0046] (3) Steel strip annealing treatment: Put the steel strip pretreated in step 1) into the annealing reduction furnace, change the process control mode of the annea...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap