Plastic bag with high thermal stability

A high thermal stability, plastic bag technology, applied in the field of plastic bags, can solve the problems of insufficient thermal stability and tensile strength, achieve the effect of improving tensile strength and heat distortion temperature, and reducing costs

Inactive Publication Date: 2018-12-21
怀宁县日升塑业有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Plastic bags are a common daily necessities for people nowadays. Plastic bags are widely used in large and small supermarkets and all walks of life due to their bright colors, novel patterns, convenient use, and low price. However, the plastic bags currently on the market are mainly polyethylene plastic bags. Main, high transparency, safe and beautiful, but there are shortcomings of insufficient thermal stability and tensile strength, which need to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A high thermal stability plastic bag, its raw materials include: 75kg of main ingredients, 2kg of bis(3,4-dimethyldibenzylidene) sorbitol, 0.4kg of vinyl-terminated silicone oil, 2kg of zinc stearate, and 0.1kg of microcrystalline paraffin kg, cocamidopropyl betaine 0.9kg, filler reinforcing agent 4kg, silane coupling agent 1kg, antioxidant 1kg, compound lubricant 3kg.

[0017] The main material is high-density polyethylene, ethylene-vinyl acetate copolymer, and acrylonitrile-butadiene-styrene copolymer in a weight ratio of 60:20:1. The filling reinforcing agent consists of zeolite powder, calcined kaolin and bentonite in a weight ratio of 2:0.4:4.

[0018] The composite lubricant is prepared by the following process: mix 12kg of zinc stearate, 4kg of oleic acid amide, and 34kg of vinyl bisstearamide, stir at room temperature for 10 minutes, heat up to 171°C and continue stirring for 12 minutes, cool to room temperature, grind for 20 minutes, and grind under pressure i...

Embodiment 2

[0020] A high thermal stability plastic bag, its raw materials include: main material 125kg, bis(3,4-dimethyldibenzylidene) sorbitol 1kg, vinyl-terminated silicone oil 1kg, zinc stearate 1kg, microcrystalline paraffin 0.6kg , cocamidopropyl betaine 0.4kg, filler reinforcing agent 8kg, silane coupling agent 0.2kg, antioxidant 3kg, compound lubricant 1kg.

[0021] The main material is high-density polyethylene, ethylene-vinyl acetate copolymer, and acrylonitrile-butadiene-styrene copolymer in a weight ratio of 100:12:4. The filling and reinforcing agent consists of zeolite powder, calcined kaolin and bentonite in a weight ratio of 1:1.5:1.

[0022] The composite lubricant is prepared by the following process: mix 20kg of zinc stearate, 2kg of oleic acid amide, and 55kg of vinyl bisstearamide, stir at room temperature for 4 minutes, raise the temperature to 178°C and continue stirring for 4 minutes, cool to room temperature, grind for 30 minutes, and grind under pressure is 340P...

Embodiment 3

[0024] A high thermal stability plastic bag, its raw materials include: main material 85kg, bis(3,4-dimethyldibenzylidene) sorbitol 1.8kg, vinyl-terminated silicone oil 0.6kg, zinc stearate 1.7kg, microcrystalline 0.2kg of paraffin, 0.7kg of cocamidopropyl betaine, 5kg of filler reinforcing agent, 0.8kg of silane coupling agent, 1.5kg of antioxidant, and 2.5kg of compound lubricant.

[0025] The main material is high-density polyethylene, ethylene-vinyl acetate copolymer, and acrylonitrile-butadiene-styrene copolymer in a weight ratio of 70:18:2. The filling reinforcing agent consists of zeolite powder, calcined kaolin and bentonite in a weight ratio of 1.8:0.6:3.

[0026] The composite lubricant is prepared by the following process: mix 14kg of zinc stearate, 3.5kg of oleic acid amide, and 40kg of vinyl bisstearamide, stir at room temperature for 8 minutes, heat up to 172°C and continue stirring for 10 minutes, cool to room temperature, grind for 22 minutes, and grind The pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
heat deflection temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a plastic bag with high thermal stability which is characterized by being prepared from the following raw materials in parts by weight: 75-125 parts of a main ingredient, 1-2 parts of di-(3,4-dimethyl benzylidene) sorbitol, 0.4-1 part of vinyl end silicone oil, 1-2 parts of zinc stearate, 0.1-0.6 part of microcrystalline wax, 0.4-0.9 part of cocoamidopropyl betaine, 4-8 parts of a filling reinforcing agent, 0.2-1 part of a silane coupling agent, 1-3 part of an antioxidant, and 1-3 part of a composite lubricant. The main ingredient comprises the following components in parts by weight: 60-100 parts of high density polyethylene, 12-20 parts of an ethylene-vinyl acetate copolymer, and 1-4 parts of an acrylonitrile-butadiene-styrene copolymer. The composite lubricant isprepared by adopting the following processes: mixing zinc stearate, oleamide and N,N-ethylene bis-stearamide, stirring at the room temperature, heating and continuously stirring, cooling, and grinding. The plastic bag with high thermal stability is high in toughness, and extremely excellent in tensile strength.

Description

technical field [0001] The invention relates to the technical field of plastic bags, in particular to a plastic bag with high thermal stability. Background technique [0002] Plastic bags are a common daily necessities for people nowadays. Plastic bags are widely used in large and small supermarkets and all walks of life due to their bright colors, novel patterns, convenient use, and low price. However, the plastic bags currently on the market are mainly polyethylene plastic bags. Mainly, it has high transparency, safety, and beauty, but it has the shortcomings of insufficient thermal stability and tensile strength, which need to be solved urgently. Contents of the invention [0003] Based on the technical problems in the background technology, the present invention proposes a plastic bag with high thermal stability, which has good toughness, excellent tensile strength and excellent thermal stability. [0004] A kind of high thermal stability plastic bag proposed by the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08L55/02C08L83/07C08L91/06C08K13/02C08K5/19C08K5/098C08K7/26C08K3/34C08K5/20
CPCC08K2201/014C08L23/06C08L2201/08C08L2205/035C08L23/0853C08L55/02C08L83/04C08L91/06C08K13/02C08K5/19C08K5/098C08K7/26C08K3/346C08K5/20
Inventor 汪传红
Owner 怀宁县日升塑业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap