Preparation method of visible light catalysis composite film

A composite film, visible light technology, applied in catalyst activation/preparation, chemical instruments and methods, special compound water treatment, etc., can solve the problems that hinder the industrial application of photocatalytic degradation of pollutants, the difficulty of separation and recovery of titanium dioxide powder, and the photocatalytic effect is not outstanding. and other problems, to achieve the effect of improving the efficiency of catalytic degradation, reducing the cost of catalytic degradation, and increasing the ability of pollutants

Active Publication Date: 2018-12-25
HUNAN UNIV OF SCI & TECH
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, pure TiO 2 Photocatalysts have the defects of high recombination rate of photogenerated electron-hole pairs, relatively low quantum efficiency, unremarkable photocatalytic effect and narrow spectral response range, and there is the problem of separation and recovery of titanium dioxide powder in use, which seriously hinders Industrial Application of Titanium Dioxide Photocatalytic Degradation of Pollutants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of visible light catalysis composite film
  • Preparation method of visible light catalysis composite film
  • Preparation method of visible light catalysis composite film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] One of the embodiments of the preparation method of a visible light catalytic composite film of the present invention comprises the following steps:

[0056] (1) Weigh 8g of titanium dioxide P25 and 6g of diatomaceous earth into a beaker, add 56g of absolute ethanol, and stir in a constant temperature water bath at 70°C for 0.5 hours.

[0057] (2) Weigh 0.5g of silane coupling agent KH540 and dissolve it in 0.5g of absolute ethanol, and add dropwise to the suspension obtained in step (1), the dropping rate is controlled at 1 drop / second, at 70°C After stirring in a constant temperature water bath for 2 hours, suction filtration, repeated washing with absolute ethanol and deionized water three times, and vacuum drying at a temperature of 60°C for 4 hours to obtain a coupling-modified diatomite / titanium dioxide inorganic powder.

[0058] (3) Weigh 8 g of diatomite / titanium dioxide inorganic powder modified by coupling, add it to 50 ml of ferric chloride solution with a su...

Embodiment 2

[0065] One of the embodiments of the preparation method of a visible light catalytic composite film of the present invention comprises the following steps:

[0066] (1) Weigh 10g of titanium dioxide P25 and 8g of diatomaceous earth into a beaker, add 72g of absolute ethanol, and stir in a constant temperature water bath at 70°C for 0.5 hours.

[0067] (2) Weigh 0.63g of silane coupling agent KH550 and dissolve it in 0.63g of absolute ethanol, and add dropwise to the suspension obtained in step (1), the dropping rate is controlled at 1 drop / second, at 70°C Stir in a constant temperature water bath for 2 hours, then filter with suction, rinse with absolute ethanol and deionized water three times, and dry in vacuum at a temperature of 70°C for 3.5 hours to obtain a coupling-modified diatomite / titanium dioxide inorganic powder.

[0068] (3) Weigh 8 g of diatomite / titanium dioxide inorganic powder modified by coupling, add it to 50 ml of ferric chloride solution with a substance am...

Embodiment 3

[0075] One of the embodiments of the preparation method of a visible light catalytic composite film of the present invention comprises the following steps:

[0076] (1) Weigh 11g of titanium dioxide P25 and 9g of diatomaceous earth into a beaker, add 80g of absolute ethanol, and stir in a constant temperature water bath at 70°C for 0.5 hours.

[0077] (2) Weigh 0.69g of silane coupling agent KH560 and dissolve it in 0.69g of absolute ethanol, and add dropwise to the suspension obtained in step (1), the dropping rate is controlled at 1 drop / second, at 70°C After stirring in a constant temperature water bath for 2 hours, suction filtration, repeated washing with absolute ethanol and deionized water three times, and vacuum drying at a temperature of 75°C for 4 hours to obtain a coupling-modified diatomite / titanium dioxide inorganic powder.

[0078] (3) Weigh 8 g of diatomite / titanium dioxide inorganic powder modified by coupling, add it to 50 ml of ferric chloride solution with a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Shore hardnessaaaaaaaaaa
Shore hardnessaaaaaaaaaa
Shore hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of visible light catalysis composite film, comprising: dispersing titanium dioxide and diatomite in anhydrous ethyl alcohol to obtain a suspension; dissolving silane coupling agent in ethyl alcohol, adding the resulting solution to the suspension to obtain coupling-modified diatomite / titanium dioxide inorganic powder; adding the powder into iron chloride solution to obtain Fe3+-modified coupling-modified diatomite / titanium dioxide inorganic powder; adding the Fe3+-modified coupling-modified diatomite / titanium dioxide inorganic powder into polyurethane macromolecular solution, mixing well, adding calcium carbonate powder having the solid content of 10%, and mixing to obtain a coating liquid; forming film, soaking the film in 300 mg / L of xanthenedye solution for certain time to obtain xanthene dye-sensitized diatomite / titanium dioxide composite film, namely the visible light catalysis composite film. The visible light catalysis composite filmherein has the advantages of high light utilization rate, high catalytic efficiency and good stability and is applicable to degradation of water pollutants.

Description

technical field [0001] The invention belongs to the technical field of photocatalysts, in particular to a method for preparing a visible light catalytic composite film. Background technique [0002] At present, photocatalytic degradation of pollutants has become an important research field. TiO 2 、WO 3 , ZnO, SnO 2 , CdS, FeO 3 etc. are commonly used n-type semiconductor photocatalyst materials, among which TiO 2 With its high chemical stability, resistance to light corrosion, not easy to dissolve, and deep valence band energy level, it can be used in TiO 2 On the surface, the acceleration of some endothermic chemical reactions, coupled with its non-toxicity and low cost, has become a green environmental management technology with great application prospects. [0003] Diatomite is a natural mineral with a light, porous structure whose main component is amorphous silica. It has a high specific surface area, good adsorption performance, stable chemical properties, non-to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J31/38B01J37/00B01J35/10C02F1/30C02F101/30
CPCC02F1/30B01J31/38B01J37/0018C02F2305/10C02F2101/308B01J35/61B01J35/657B01J35/39
Inventor 周虎王晓虹张少伟蹇建王桃芬左宇璐何楚娴
Owner HUNAN UNIV OF SCI & TECH