Anti-crease finishing agent for shirt fabric and application of anti-crease finishing agent

An anti-wrinkle finishing agent and fabric technology, which is applied in fiber treatment, biochemical fiber treatment, textiles and papermaking, etc., can solve the problems of high cost, poor wear resistance, and low cost of anti-wrinkle finishing agents, and reduce addition, improve affinity, damage reduction effect

Inactive Publication Date: 2019-01-08
常州依丝特纺织服饰有限公司
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the problems of high cost and poor wear resistance of anti-wrinkle finishing agents in the prior art, the present invention provides an anti-wrinkle finishing agent for shirt fabrics and its application. The anti-wrinkle finishing agent effectively improves the anti-wrinkle effect of shirts and is low in cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] An anti-wrinkle finishing agent for shirt fabrics, comprising the following components in parts by weight: 1 part of nano-titanium dioxide, 12 parts of malic acid, 20 parts of isopropanol, 8 parts of sodium sulfate, 20 parts of plant extracts, 2 parts of silk protein 2 parts, 2 parts of sorbitan fatty acid ester, 18 parts of amino silicone oil, 1-3 parts of silicone emulsion, 3 parts of coconut oil fatty acid diethanolamide, 35 parts of modified polyurethane, 2 parts of oxidized sodium carboxymethyl cellulose, 30 parts of deionized water.

[0022] Wherein, the modified polyurethane is formed by mixing zinc oxide, polyurethane and chitosan, and the molar ratio of zinc oxide, polyurethane and chitosan is 3:5:1. The average molecular weight of described chitosan is 1.6 * 10 -4 .

[0023] The plant extract is a mixture of Ginkgo biloba, Lemongrass and Dendrobium candidum rods, added deionized water to distill for 20 minutes, filtered, and concentrated to a water content o...

Embodiment 2

[0030] An anti-wrinkle finishing agent for shirt fabrics, comprising the following components in parts by weight: 3 parts of nano-titanium dioxide, 15 parts of malic acid, 28 parts of isopropanol, 12 parts of sodium sulfate, 28 parts of plant extracts, 6 parts of silk protein 3 parts, 3 parts of sorbitan fatty acid ester, 25 parts of amino silicone oil, 2 parts of silicone emulsion, 6 parts of coconut oil fatty acid diethanolamide, 38 parts of modified polyurethane, 6 parts of oxidized sodium carboxymethyl cellulose, deionized water 42 servings.

[0031] Wherein, the modified polyurethane is formed by mixing zinc oxide, polyurethane and chitosan, and the molar ratio of zinc oxide, polyurethane and chitosan is 3:5:1. The average molecular weight of described chitosan is 1.7 * 10 -4 . The plant extract is a mixture of Ginkgo biloba, Lemongrass and Dendrobium candidum rods, added deionized water to distill for 25 minutes, filtered, and concentrated to a water content of 20%. 2...

Embodiment 3

[0038] An anti-wrinkle finishing agent for shirt fabrics, comprising the following components in parts by weight: 5 parts of nano-titanium dioxide, 18 parts of malic acid, 30 parts of isopropanol, 14 parts of sodium sulfate, 30 parts of plant extracts, 8 parts of silk protein 4 parts, 4 parts of sorbitan fatty acid ester, 27 parts of amino silicone oil, 3 parts of silicone emulsion, 8 parts of coconut oil fatty acid diethanolamide, 40 parts of modified polyurethane, 8 parts of oxidized sodium carboxymethyl cellulose, deionized 48 parts of water.

[0039] Wherein, the modified polyurethane is formed by mixing zinc oxide, polyurethane and chitosan, and the molar ratio of zinc oxide, polyurethane and chitosan is 3:5:1. The average molecular weight of described chitosan is 1.8 * 10 -4 . The plant extract is a mixture of Ginkgo biloba, Lemongrass and Dendrobium officinale rods, added deionized water to distill for 30 minutes, filtered, and concentrated to a water content of 20%. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hydrophilicityaaaaaaaaaa
hydrophilicityaaaaaaaaaa
hydrophilicityaaaaaaaaaa
Login to view more

Abstract

The invention discloses an anti-crease finishing agent for a shirt fabric and an application of the anti-crease finishing agent. The anti-crease finishing agent comprises the following components in parts by weight: 1-5 parts of nano titanium dioxide, 12-18 parts of malic acid, 20-30 parts of isopropyl alcohol, 8-14 parts of sodium sulfate, 20-30 parts of plant extract, 2-8 parts of silk protein,2-4 parts of sorbitan fatty acid ester, 18-27 parts of amino silicone oil, 1-3 parts of organosilicone emulsion, 3-8 parts of coconut fatty acid diethanol amide, 35-40 parts of modified polyurethane,2-8 parts of sodium carboxymethyl cellulose oxide, and 30-48 parts of deionized water. Compared with the prior art, the anti-crease effect of the shirt fabric is improved by using the silk protein andthe modified polyurethane, and the lubricity of the silk protein improves the affinity of the fabric and the skin. In addition, the plant extract is obtained by mixing of multiple plants, extractionand concentration, thereby reducing the addition of chemicals while ensuring the anti-crease effect of the finishing agent.

Description

technical field [0001] The invention belongs to the field of fabric finishing, and in particular relates to an anti-wrinkle finishing agent for shirt fabric and its application. Background technique [0002] Application No. 201610547449.9, titled as a preparation method of an anti-wrinkle, antibacterial and non-irritating shirt fabric finishing agent, belongs to the field of fabric finishing agents. The present invention first reacts chitosan solution with linoleic acid and linolenic acid to obtain fatty acid chitosan, then extracts coconut oil from coconut meat, mixes the two and adds aloe vera juice, citronella essential oil, dextrin, benzyl Thonium chloride etc. are mixed to obtain a mixed solution, and the mixed solution is heated and mixed with malic acid, sodium hypophosphite, triethanolamine, butane tetracarboxylic acid and ethylene glycol to obtain a finishing agent. Although the finishing agent prepared by the present invention Good anti-wrinkle effect on fabrics, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/564D06M15/03D06M11/44D06M15/643D06M15/09D06M11/46D06M11/56D06M13/144D06M15/15D06M13/00
CPCD06M11/44D06M11/46D06M11/56D06M13/00D06M13/144D06M15/03D06M15/09D06M15/15D06M15/564D06M15/643D06M15/6436D06M16/00D06M2200/20
Inventor 唐儒军杨娟娟
Owner 常州依丝特纺织服饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap