A dental filling resin material and a preparation method thereof

A technology of resin material and dental filling, applied in dental preparations, dentistry, dental prosthesis, etc., can solve the problems of glass ionomer cement surface hardness and wear resistance, air bubbles, difficult to polish, etc., to achieve excellent surface hardness, inhibit oral cavity Bacteria, easily scalable effects

Inactive Publication Date: 2019-01-15
佛山市佛冠义齿有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the surface hardness and wear resistance of glass ionomer cement are poor, and it is not easy to be polished, and its operation technology is strict, and water in the early stage of setting reaction may cause air bubbles, cracks and subsequent staining and material dissolution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A dental filling resin material, which is made of the following components in proportion by weight: 15 parts of polyvinyl chloride resin, 5 parts of propylene glycol alginate, 6 parts of lauryl amine oxide, and 15 parts of polyhydroxyethyl methacrylate , 10 parts of chitin, 2 parts of fibroin, 10 parts of chitosan fiber, 10 parts of diethyl cystine, 5 parts of anti-caries agent, 4 parts of nano-silver powder, 5 parts of paeonol, 10 parts of antioxidant, 5 parts of nano filler, 2 parts of stabilizer, 15 parts of double distilled water.

[0021] Further, the nano-filler is a mixture of zirconia and silica nano-powders, the ratio of which is 2:1.

[0022] Further, the stabilizer is p-methoxyphenol.

[0023] Further, the antioxidant is 2,6-di-tert-butyl-p-cresol.

[0024] Further, the anti-caries agent is a mixture of sodium fluoride and strontium fluoride, the ratio of which is 3:2; the mixture of sodium fluoride and strontium fluoride can directly inhibit the ability of...

Embodiment 2

[0029] The preparation method of the dental filling resin material described in Example 2 is the same as that of the dental filling resin material in Example 1, and the raw materials and their proportions in Example 2 are as follows.

[0030] A dental filling resin material, made of the following components by weight: 30 parts of polyvinyl chloride resin, 11 parts of propylene glycol alginate, 10 parts of lauryl amine oxide, and 18 parts of polyhydroxyethyl methacrylate , 15 parts of chitin, 5 parts of fibroin, 11 parts of chitosan fiber, 12 parts of diethyl cystine, 6 parts of anti-caries agent, 6 parts of nano-silver powder, 7 parts of paeonol, 12 parts of antioxidant, 6 parts of nano filler, 3 parts of stabilizer, 20 parts of double distilled water.

[0031] Further, the nano-filler is a mixture of zirconia and silica nano-powders, the ratio of which is 2:1.

[0032] Further, the stabilizer is p-methoxyphenol.

[0033] Further, the antioxidant is 2,6-di-tert-butyl-p-creso...

Embodiment 3

[0036] The preparation method of the dental filling resin material described in Example 3 is the same as that of the dental filling resin material in Example 1, and the raw materials and their proportions in Example 3 are as follows.

[0037] A dental filling resin material, which is made of the following components in proportion by weight: 20 parts of polyvinyl chloride resin, 7 parts of propylene glycol alginate, 8 parts of lauryl amine oxide, and 16 parts of polyhydroxyethyl methacrylate , 13 parts of chitin, 3 parts of fibroin, 11 parts of chitosan fiber, 11 parts of diethyl cystine, 6 parts of anti-caries agent, 5 parts of nano-silver powder, 6 parts of paeonol, 11 parts of antioxidant, 5 parts of nano filler, 3 parts of stabilizer, 16 parts of double distilled water.

[0038] Further, the nano-filler is a mixture of zirconia and silica nano-powders, the ratio of which is 2:1.

[0039] Further, the stabilizer is p-methoxyphenol.

[0040] Further, the antioxidant is 2,6-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A dental filling resin material and a preparation method thereof are provided. The material is made of the following components in parts by weight, 15 to 30 parts of polyvinyl chloride resin, 5 to 11parts of propylene glycol alginate, 6 to 10 parts of dodecylamine oxide, 15-18 parts of polyhydroxyethyl methacrylate, 10-15 parts of chitin, 2-5 part of fimbrin, 10-11 parts of chitosan fiber, 10-12parts of cystine diethyl ester, 5-6 part of anti-caries agent, 4-6 parts of nano silver powder, 5-7 parts of paeonol, 10-12 parts of antioxidant, 5-6 parts of nano filler, 2-3 parts of stabilizer and15-20 parts of double distilled water. The filling resin material has excellent surface hardness and good abrasion resistance, and is easy to be polished. An anti-caries agent is added into the filling resin material in the invention, which can effectively prevent dental caries; The dental filling resin of the invention is added with nano silver salt, which can effectively inhibit oral bacteria; The filling resin material does not contain heavy metals and is environmentally friendly; And the preparation method is simple and feasible.

Description

technical field [0001] The invention belongs to the technical field of biomedical materials, and in particular relates to a dental filling resin material and a manufacturing method thereof. Background technique [0002] Teeth are the organs that humans use to chew food. Teeth are the hardest organ in the human body. Generally speaking, teeth are white and hard in texture. The various shapes of teeth are suitable for many purposes, including tearing, grinding food. Teeth are the hardest organs in the human body, and their main component is basic calcium phosphate. [0003] Dental caries, also known as tooth decay or tooth decay, is a bacterial disease, which can be secondary to pulpitis and periapical periodontitis, and even cause alveolar bone and jaw inflammation in severe cases. If it is not treated in time, the lesion will continue to develop, forming cavities, and eventually the crown will be completely destroyed and disappeared. The final result of its development i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K6/097A61K6/087A61K6/083A61K6/04A61K6/027A61K6/02A61K6/00A61K6/891A61K6/898
CPCA61K6/15A61K6/69A61K6/71A61K6/76A61K6/80A61K6/831A61K6/844A61K6/887A61K6/891A61K6/898C08L89/00C08L5/08C08L5/04C08L33/14C08L27/06
Inventor 刘秀兰吴活权郭园
Owner 佛山市佛冠义齿有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com