Wear-resistant coating for basalt reinforced forklift steel rim

A technology of wear-resistant coatings and basalt, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problems of loss of service life of forklift rims, and achieve good aging resistance, good salt water corrosion resistance, and high hardness.

Inactive Publication Date: 2019-01-15
ANHUI JIANGHUAI WHEEL CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Coatings for forklift rims require not only good surface quality and workability, but also different requirements according to different application fields. Some require the coating film to have excellent mechanical properties, and some require the coating film to have excellent salt resistance. Fog and weather resistance, and because of the environment in which the forklift rim is used, its wear resistance requirements are relatively high. If the surface of the forklift rim is not protected in time, it will greatly reduce the service life of the forklift rim and improve Cost of production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A basalt-reinforced wear-resistant coating for forklift rims, made of the following components in parts by weight, acrylate emulsion 95, modified basalt fiber 6, methyl ethoxy silicone oil 8, nano silicon dioxide 3.8, tripolyphosphoric acid Aluminum 1.4, nano zinc oxide 3, ammonium polyphosphate 1.9, glycerin 15, leveling agent 0.5, deionized water 70, defoamer 0.55.

[0017] Further, the preparation method of the modified basalt fiber is:

[0018] (1) Treat the basalt fiber at 200°C and 400°C for 20 minutes respectively, and then naturally cool to room temperature;

[0019] (2) Add the above treated basalt fibers to an acidic potassium permanganate solution with a mass fraction of 10%, soak at 80°C for 2 hours, then filter, and then dry at 120°C to constant weight to obtain .

[0020] Further, the mass fraction of potassium permanganate in the acidic potassium permanganate solution is 5.8%.

[0021] Further, the pH of the acidic potassium permanganate solution is 3....

Embodiment 2

[0026] A basalt-reinforced wear-resistant coating for forklift rims, made of the following components in parts by weight: acrylate emulsion 95, modified basalt fiber 10, methyl ethoxy silicone oil 8, nano silicon dioxide 3.8, tripolyphosphoric acid Aluminum 1.4, nano zinc oxide 3, ammonium polyphosphate 1.9, glycerin 15, leveling agent 0.5, deionized water 70, defoamer 0.55.

[0027] Further, the preparation method of the modified basalt fiber is:

[0028] (1) Treat the basalt fiber at 200°C and 400°C for 20 minutes respectively, and then naturally cool to room temperature;

[0029] (2) Add the above treated basalt fibers to an acidic potassium permanganate solution with a mass fraction of 10%, soak at 80°C for 2 hours, then filter, and then dry at 120°C to constant weight to obtain .

[0030] Further, the mass fraction of potassium permanganate in the acidic potassium permanganate solution is 5.8%.

[0031] Further, the pH of the acidic potassium permanganate solution is 3...

Embodiment 3

[0036] A basalt-reinforced wear-resistant coating for forklift rims, made of the following components in parts by weight, acrylate emulsion 95, modified basalt fiber 8, methyl ethoxy silicone oil 8, nano silicon dioxide 3.8, tripolyphosphoric acid Aluminum 1.4, nano zinc oxide 3, ammonium polyphosphate 1.9, glycerin 15, leveling agent 0.5, deionized water 70, defoamer 0.55.

[0037] Further, the preparation method of the modified basalt fiber is:

[0038] (1) Treat the basalt fiber at 200°C and 400°C for 20 minutes respectively, and then naturally cool to room temperature;

[0039] (2) Add the above treated basalt fibers to an acidic potassium permanganate solution with a mass fraction of 10%, soak at 80°C for 2 hours, then filter, and then dry at 120°C to constant weight to obtain .

[0040] Further, the mass fraction of potassium permanganate in the acidic potassium permanganate solution is 5.8%.

[0041] Further, the pH of the acidic potassium permanganate solution is 3....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a wear-resistant coating for a basalt reinforced forklift steel rim, wherein the wear-resistant coating is prepared from the following ingredients: an acrylate emulsion, modified basalt fibers, methyl-ethyoxyl silicone oil, nano silica, aluminum tripolyphosphate, nano zinc oxide, ammonium polyphosphate, glycerin, a leveling agent, deionized water and a defoaming agent. Thewear-resistant coating for the basalt reinforced forklift steel rim has the advantage of fast curing and film forming speed, and a coating film is compact, high in hardness and good in wear resistance.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a wear-resistant coating for basalt-reinforced steel rings of forklifts. Background technique [0002] Forklift rims are pressed and welded steel to assemble tubeless tires. Coatings for forklift rims require not only good surface quality and workability, but also different requirements according to different application fields. Some require the coating film to have excellent mechanical properties, and some require the coating film to have excellent salt resistance. Fog and weather resistance, and because of the environment in which the forklift rim is used, its wear resistance requirements are relatively high. If the surface of the forklift rim is not protected in time, it will greatly reduce the service life of the forklift rim and improve Cost of production. Contents of the invention [0003] The object of the present invention is to provide a wear-resistant coating for b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D183/04C09D5/08C09D7/61C09D7/62
CPCC09D133/04C08K2003/2296C08K2201/011C09D5/08C09D7/61C09D7/68C09D7/70C08L83/04C08K13/06C08K9/02C08K7/10C08K3/36C08K3/22
Inventor 朱加强
Owner ANHUI JIANGHUAI WHEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap