Softly-polished metallic brick and preparation method thereof
A metal and brick blank technology, applied in the field of soft-polished metal bricks and their preparation, can solve the problems of insufficient single color, high cost, and inability to polish, etc., and achieves the effect of improving gloss, realistic metal imitation, and rich diversity.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0024] A soft polished metal tile, including brick adobe, surface glaze and pattern glaze.
[0025] Specifically, the surface glaze includes 45 parts by weight of potassium feldspar, 10 parts of quartz, 1 part of wollastonite, 2 parts of calcined talc, 15 parts of calcined kaolin, 12 parts of zirconium silicate, 45 parts of water, 13 parts of nephrite Stone, 7 parts of calcined alumina, 9 parts of kaolin, 0.23 parts of methylcellulose and 0.35 parts of sodium tripolyphosphate. The preparation method of the surface glaze is as follows: add each raw material into the ball mill according to the number of parts, and ball mill for 8 hours until the fineness is 325 mesh sieve, the remaining 0.9% of the sieve, the specific gravity: 1.95g / ml, and the flow rate is 80 seconds. When slurrying, perform iron removal operation and pass through a 140 mesh sieve.
[0026] Specifically, the floral glaze is composed of basic floral glaze and colored oxides. Among them, the basic floral glaze ...
Embodiment 2
[0037] A soft polished metal tile, including brick adobe, surface glaze and pattern glaze.
[0038] Specifically, the surface glaze includes 45 parts by weight of potassium feldspar, 13 parts of quartz, 1 part of wollastonite, 2 parts of burnt talc, 18 parts of calcined kaolin, 12 parts of zirconium silicate, 45 parts of water, 13 parts of nephrite Stone, 8 parts of calcined alumina, 9 parts of kaolin, 0.23 parts of methylcellulose and 0.35 parts of sodium tripolyphosphate. The preparation method of the surface glaze is as follows: add each raw material into the ball mill according to the number of parts, and ball mill for 8 hours until the fineness is 325 mesh sieve, the remaining 0.9% of the sieve, the specific gravity: 1.95g / ml, and the flow rate is 80 seconds. When slurrying, perform iron removal operation and pass through a 140 mesh sieve.
[0039] Specifically, the floral glaze is composed of basic floral glaze and colored oxides. Among them, the basic floral glaze inc...
Embodiment 3
[0050] A soft polished metal tile, including brick adobe, surface glaze and pattern glaze.
[0051]Specifically, the surface glaze includes 45 parts by weight of potassium feldspar, 15 parts of quartz, 1 part of wollastonite, 2 parts of calcined talc, 20 parts of calcined kaolin, 12 parts of zirconium silicate, 45 parts of water, 13 parts of nephrite Stone, 10 parts of calcined alumina, 9 parts of kaolin, 0.23 parts of methylcellulose and 0.35 parts of sodium tripolyphosphate. The preparation method of the surface glaze is as follows: add each raw material into the ball mill according to the number of parts, and ball mill for 8 hours until the fineness is 325 mesh sieve, the remaining 0.9% of the sieve, the specific gravity: 1.95g / ml, and the flow rate is 80 seconds. When slurrying, perform iron removal operation and pass through a 140 mesh sieve.
[0052] Specifically, the floral glaze is composed of basic floral glaze and colored oxides. Among them, the basic floral glaze ...