Foam light-weight concrete and preparation method thereof

A light-weight foam and concrete technology, which is applied in ceramic products, other household utensils, cement production, etc., can solve the problems of poor versatility, achieve improved performance, improve physical properties, and have a wide range of applications

Inactive Publication Date: 2019-01-18
方涛
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there is no uniform standard for the ratio of foam concrete. The versatility of the subgrade for different rock and soil conditions and environmental conditions is relatively poor. Research on the ratio of foam co

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The present embodiment provides a kind of foam lightweight concrete, and raw material formula is as follows by mass:

[0023] 150 parts of geopolymer cement, 1.0 parts of water reducing agent, 4 parts of early strength agent, 3 parts of admixture, 2 parts of fiber, 15 parts of foaming agent, 10 parts of gel material, 1 part of diatom mud, 100 parts of water;

[0024] The admixture contains the following components by mass: 8 parts of calcium oxide, 20 parts of iron oxide, 25 parts of magnesium oxide, 0.5 parts of butyl phosphate, 6 parts of polyurethane, 8 parts of sodium nitrite, 3 parts of silane coupling agent, silicon carbide 3 copies;

[0025] The foaming agent contains the following components by mass: 5 parts of limestone powder, 4 parts of slag, 7 parts of modified diatomite, 10 parts of polyacrylic resin, 3 parts of polyethylene glycol, 3 parts of anhydrite, and 2 parts of mica powder , 6 parts of hydroxypropyl methylcellulose, 4 parts of borax.

Embodiment 2

[0027] The present embodiment provides a kind of foam lightweight concrete, and raw material formula is as follows by mass:

[0028] 180 parts of geopolymer cement, 1.2 parts of water reducing agent, 5 parts of early strength agent, 5 parts of admixture, 3 parts of fiber, 18 parts of foaming agent, 11 parts of gel material, 2 parts of diatom mud, and 110 parts of water;

[0029] The admixture contains the following components by mass: 9 parts of calcium oxide, 21 parts of iron oxide, 27 parts of magnesium oxide, 0.8 parts of butyl phosphate, 7 parts of polyurethane, 9 parts of sodium nitrite, 4 parts of silane coupling agent, silicon carbide 3 copies;

[0030] The foaming agent contains the following components by mass: 6 parts of limestone powder, 5 parts of slag, 8 parts of modified diatomite, 11 parts of polyacrylic resin, 5 parts of polyethylene glycol, 5 parts of anhydrite, and 5 parts of mica powder , 8 parts of hydroxypropyl methylcellulose, 5 parts of borax.

Embodiment 3

[0032] The present embodiment provides a kind of foam lightweight concrete, and raw material formula is as follows by mass:

[0033] 200 parts of geopolymer cement, 1.5 parts of water reducing agent, 5 parts of early strength agent, 5 parts of admixture, 4 parts of fiber, 20 parts of foaming agent, 12 parts of gel material, 3 parts of diatom mud, and 120 parts of water;

[0034] The admixture contains the following components by mass: 10 parts of calcium oxide, 22 parts of iron oxide, 30 parts of magnesium oxide, 1 part of butyl phosphate, 8 parts of polyurethane, 10 parts of sodium nitrite, 5 parts of silane coupling agent, silicon carbide 4 parts;

[0035] The foaming agent contains the following components by mass: 7 parts of limestone powder, 6 parts of slag, 9 parts of modified diatomite, 12 parts of polyacrylic resin, 6 parts of polyethylene glycol, 7 parts of anhydrite, and 7 parts of mica powder , 10 parts of hydroxypropyl methylcellulose, 6 parts of borax.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses foam light-weight concrete and a preparation method thereof and relates to the technical field of preparation of concrete. A raw material formula comprises the following components in parts by mass: 150 to 200 parts of geopolymer cement, 1.0 to 1.5 parts of a water reducing agent, 4 to 5 parts of an early strength agent, 3 to 5 parts of an additive, 2 to 4 parts of fibers,15 to 20 parts of a foaming agent, 10 to 12 parts of a gel material, 1 to 3 parts of diatom ooze and 100 to 120 parts of water; the preparation method of the foam light-weight concrete comprises the following steps: (1) pouring the geopolymer cement, the water reducing agent, the early strength agent, the fibers, the gel material, the diatom ooze and a proper amount of the water into a stirring tank according to the ratio and stirring and mixing; (2) continually adding the foaming agent into the stirring tank and continuously stirring for 12 to 14min; then adding the additive and continuouslystirring for 35 to 40min. The concrete prepared by the method has the advantages of light weight and good commonality.

Description

technical field [0001] The invention relates to the technical field of concrete preparation, in particular to a foam lightweight concrete and a preparation method thereof. Background technique [0002] Foam lightweight concrete is a kind of lightweight filling material, which is composed of cement slurry and a certain proportion of small enough stable bubble groups, which are fully mixed and stirred to form a fluid, and finally solidified and formed. Foam lightweight concrete is light in weight, high in strength, wide in adjustable range, good self-supporting, convenient and fast in construction, and has good technical economy. The application of foam concrete materials to the back filling of road and bridge abutments is an innovative technology that changes the conventional abutment back filling process. The foam concrete material has the advantages of greater strength than conventional backfill, forming a whole after filling, good impact resistance, no lateral pressure, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B38/02
CPCC04B28/006C04B2201/20C04B2201/50C04B2103/302C04B2103/12C04B14/08C04B22/064C04B14/308C04B14/304C04B24/003C04B24/282C04B22/085C04B24/42C04B14/324C04B14/28C04B18/141C04B24/26C04B24/32C04B22/143C04B14/20C04B24/383C04B22/0013C04B20/0048C04B2103/44C04B38/02Y02P40/10
Inventor 方涛
Owner 方涛
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap