A kind of anti-adhesion polyvinyl alcohol embolic microspheres and its preparation method and application

A technology for embolizing polyvinyl alcohol microspheres and polyvinyl alcohol microspheres, which is applied in the directions of application, medical preparations without active ingredients, and medical preparations containing active ingredients, etc. Good control, particle size reduction and other problems, to achieve the effect of good sphericity, low cost, and increased swelling

Active Publication Date: 2021-01-19
EZHOU INST OF IND TECH HUAZHONG UNIV OF SCI & TECH +1
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally, in the process of emulsification and crosslinking, the particle size of polyvinyl alcohol microspheres can be increased by increasing the concentration of polyvinyl alcohol, reducing the ratio of oil / water phase, reducing the stirring speed, and reducing the concentration of surfactants, but polyvinyl alcohol It has a certain viscosity, and it also increases the probability of microsphere collision and adhesion during the stirring process. The addition of cross-linking agent is likely to cause large adhesion of the microspheres that stick together; if the process of preparing microspheres is passed Reducing the concentration of polyvinyl alcohol, increasing the ratio of oil / water phase, increasing the stirring speed or increasing the concentration of emulsifier can make the microspheres isolated from each other in the oil phase, reduce the probability of collision and adhesion of the microspheres, and make the prepared microspheres more dispersed At the same time, the particle size of the microspheres will also decrease, which may not meet the particle size requirements for specific tumor embolization
Therefore, the preparation of polyvinyl alcohol microspheres with a larger particle size and non-cohesion is not easy to control during actual operation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-adhesion polyvinyl alcohol embolic microspheres and its preparation method and application
  • A kind of anti-adhesion polyvinyl alcohol embolic microspheres and its preparation method and application
  • A kind of anti-adhesion polyvinyl alcohol embolic microspheres and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The present embodiment provides a preparation method of anti-adhesion polyvinyl alcohol embolization microspheres, comprising the following steps:

[0031] (1) Preparation of polyvinyl alcohol and chitosan blend solution: polyvinyl alcohol 124 is heated and dissolved in a high temperature water bath or oil bath to obtain a polyvinyl alcohol aqueous solution with a mass fraction of 10%; Sugar is dissolved in acetic acid solution with a mass fraction of 1% to obtain a chitosan solution with a mass fraction of 0.84%; the polyvinyl alcohol solution and the chitosan solution are mixed according to the volume of 1:0.64 to prepare a chitosan solution with a mass fraction of 6.55%. mixed solution.

[0032] (2) Preparation of anti-blocking polyvinyl alcohol microspheres: slowly dropwise add the blended solution of the above step a) into 72 mL of an organic dispersed phase containing 2.43% Span80 by mass, emulsification with magnetic stirring at 350 rpm, and blend The volume rat...

Embodiment 2

[0044] The present embodiment provides a preparation method of anti-adhesion polyvinyl alcohol embolization microspheres, comprising the following steps:

[0045] (1) Preparation of polyvinyl alcohol and chitosan blend solution: polyvinyl alcohol 124 is heated and dissolved in a high temperature water bath or oil bath to obtain a polyvinyl alcohol aqueous solution with a mass fraction of 10%; Sugar is dissolved in acetic acid solution with a mass fraction of 1% to obtain a chitosan solution with a mass fraction of 0.84%; the polyvinyl alcohol solution and the chitosan solution are mixed in a volume ratio of 1:0.64 to prepare a co-coated 6.55% mass fraction. mixed solution.

[0046] (2) Preparation of anti-blocking polyvinyl alcohol microspheres: slowly dropwise add the blended solution of the above step a) into 72 mL of an organic dispersed phase containing 1.8% Span80 by mass, perform magnetic stirring emulsification at 300 rpm, and blend. The volume ratio of the solution to...

Embodiment 3

[0050] The present embodiment provides a method for preparing anti-adhesion polyvinyl alcohol embolization microspheres, the steps of which are basically the same as those in Example 2, the differences are:

[0051] (1) Preparation of polyvinyl alcohol and xanthan gum blend solution: polyvinyl alcohol 124 is heated and dissolved in a high temperature water bath or oil bath to obtain a polyvinyl alcohol aqueous solution with a mass fraction of 5%; The gum was dissolved in an acetic acid solution with a mass fraction of 1% to obtain a xanthan gum solution with a mass fraction of 1.5%; the polyvinyl alcohol solution and the xanthan gum solution were mixed in a volume ratio of 1:0.3.

[0052] (2) Preparation of anti-blocking polyvinyl alcohol microspheres: slowly dropwise add the blended solution of the above step a) into 72 mL of an organic dispersed phase containing 0.8% Span80, carry out magnetic stirring emulsification at 500 rpm, and blend. The volume ratio of the solution to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides an anti-adhesion polyvinyl alcohol embolization microsphere, and a preparation method and an application thereof, and belongs to the field of intervention polymer embolization materials. Positively charged or negatively charged polysaccharides are added in a process for preparing polyvinyl alcohol microspheres by reverse suspension crosslinking to make Coulomb repulsive force among the microspheres and the microspheres repulse each other in order to obtain the embolization microsphere with a high sphericity, non-adhesion and a controllable particle size. The anti-adhesion polyvinyl alcohol embolization microsphere has the advantages of simple preparation method, mild preparation conditions, low cost, suitableness for large-scale mass production, and broad applicationprospect in the field of clinical interventional medicine.

Description

technical field [0001] The invention relates to a preparation method of macromolecular embolization microspheres for interventional treatment of tumors, in particular to an anti-adhesion polyvinyl alcohol embolization microsphere and its preparation method and application. Background technique [0002] In recent years, with the intensification of environmental pollution, people's irregular living habits and the aging of the population, the related malignant tumors such as lung cancer, liver cancer, gastric cancer, and rectal cancer have shown an increasing trend year by year. The common treatment methods for malignant tumors are surgical resection, radiotherapy and chemotherapy, which have many disadvantages such as large side effects and high cost. For patients with advanced disease, Transcatheter arterial embolization (TAE) provides a new treatment method for the majority of patients. It has many advantages such as good targeting, minimally invasive, and low complications...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61L24/08A61L24/04A61K9/16A61K47/32A61K47/36A61P35/00
CPCA61K9/1635A61K9/1652A61K45/00A61L24/043A61P35/00C08L29/04
Inventor 杨光李晓宏纪雄发曹佳梦
Owner EZHOU INST OF IND TECH HUAZHONG UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products