Iron runner casting material for blast furnaces and preparation method thereof

A technology of tapping trough and castables, which is applied in the field of tapping trough castables, can solve the problems of low superheat in blast furnace smelting, affect the service life of iron trough, and high melting temperature, achieve low water addition, reduce porosity, improve The effect of high temperature strength

Inactive Publication Date: 2019-02-15
CHANGXING MINGTIAN FURNACE CHARGE
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The melting temperature of titanium-containing blast furnace slag is high, and the superheat degree of blast furnace smelting is low. However, the slag contains more minerals with high melting point and easy crystallization. Titanium slag is easy to adhere to the refractory material of the main trench, and if it is not cleaned in time, the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] A tap trough castable for a blast furnace and a preparation method thereof, the specific steps of which are:

[0051] One, the raw material and content thereof of described blast furnace tap trough castable (hereinafter referred to as "castable") are:

[0052] Fused brown corundum with a particle size of 8~5mm is 15~18wt%;

[0053] Fused brown corundum with a particle size of 5~3mm is 18~20 wt%;

[0054] Fused brown corundum with a particle size of 3-1mm is 24-25 wt%;

[0055] Silicon carbide with a particle size of 0.088~1mm is 10~11 wt%;

[0056] Silicon carbide with particle size ≤0.088mm is 13~15 wt%;

[0057]Ball pitch is 2~3 wt%;

[0058] Silica powder is 1 ~ 2wt%;

[0059] Activated alumina micropowder is 5~6wt%;

[0060] Silica powder is 2~3 wt%;

[0061] CA-70 cement is 5 ~ 6wt%.

[0062] The following are the admixtures used in the preparation of castables:

[0063] Metal aluminum powder is 0.04 ~ 0.06 wt% of the raw material,

[0064] The polycarbox...

Embodiment 2

[0071] A tap trough castable for a blast furnace and a preparation method thereof, the specific steps of which are:

[0072] One, the raw material and content thereof of described blast furnace tap trough castable (hereinafter referred to as "castable") are:

[0073] Fused brown corundum with a particle size of 8~5mm is 18~22wt%;

[0074] Fused brown corundum with a particle size of 5~3mm is 16~18 wt%;

[0075] Fused brown corundum with a particle size of 3-1mm is 22-24 wt%;

[0076] Silicon carbide with a particle size of 0.088~1mm is 11~13 wt%;

[0077] Silicon carbide with particle size ≤0.088mm is 11~13 wt%;

[0078] Ball pitch is 3~4 wt%;

[0079] Silica powder is 2 ~ 3wt%;

[0080] Activated alumina micropowder is 4~5wt%;

[0081] Silica powder is 3~4 wt%;

[0082] CA-70 cement is 4~5wt%.

[0083] The following are the admixtures used in the preparation of castables:

[0084] Metal aluminum powder is 0.04 ~ 0.06 wt% of the raw material,

[0085] The polycarboxy...

Embodiment 3

[0092] A tap trough castable for a blast furnace and a preparation method thereof, the specific steps of which are:

[0093] One, the raw material and content thereof of described blast furnace tap trough castable (hereinafter referred to as "castable") are:

[0094] Fused brown corundum with a particle size of 8~5mm is 22~25wt%;

[0095] Fused brown corundum with a particle size of 5~3mm is 15~16wt%;

[0096] Fused brown corundum with a particle size of 3~1mm is 20~22wt%;

[0097] Silicon carbide with a particle size of 0.088~1mm is 13~15wt%;

[0098] Silicon carbide with particle size ≤0.088mm is 10~11wt%;

[0099] Ball pitch is 4~5 wt%;

[0100] Silica fine powder is 3 ~ 4wt%;

[0101] Activated alumina micropowder is 3~4wt%;

[0102] Silica powder is 4~5 wt%;

[0103] CA-70 cement is 3 ~ 4wt%.

[0104] The following are the admixtures used in the preparation of castables:

[0105] Metal aluminum powder is 0.04 ~ 0.06 wt% of the raw material,

[0106] The polycarb...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention relates to an iron runner casting material for blast furnaces and a preparation method thereof. According to the technical scheme, the method comprises the steps of placing 1-4wt% of a silicon dioxide micro-powder, 3-6wt% of an activated alumina micro-powder and 2-5wt% of a silica micro-powder in a conical mixer, adding 0.04-0.06wt% of a metal aluminum powder and 0.3-0.5wt% of a polycarboxylic water reducer, and stirring for 20 to 30 minutes to obtain a premix; and mixing the premix, 10-150wt% of silicon carbide having the particle size of 0.088-1 mm, 10-150wt% of silicon carbidehaving the particle size of less than or equal to 0.088 mm, 3-6wt% of CA-70 cement, 2-5wt% of ball pitch and 50-70wt% of fused brown corundum particles with a planetary mixer for 8 to 12 minutes to obtain the iron runner casting material for blast furnaces. The gradations of the fused brown corundum particle are: 15-25wt% for 8-5 mm, 15-20wt% for 5-3 mm, and 20-25wt% for 3-1 mm. The iron runner casting material has good erosion resistance, oxidation resistance, thermal shock resistance, non-stickiness, long service life and high one-time iron flux.

Description

technical field [0001] The invention belongs to the technical field of tap trough castables. In particular, it relates to a castable castable for a blast furnace and a preparation method thereof. Background technique [0002] In the process of smelting vanadium-titanium magnetite, due to the low ore grade, the iron content is less than 50%, and the amount of slag and iron in front of the furnace is large, about 700 kg of slag is produced per ton of iron, which is much higher than the amount of slag smelted by ordinary ore blast furnaces. Moreover, the erosion of castables by titanium-containing blast furnace slag is also more serious than that of ordinary blast furnace slag. The melting temperature of titanium-containing blast furnace slag is high, and the superheat degree of blast furnace smelting is low. However, the slag contains more minerals with high melting point and easy crystallization. Titanium slag is easy to adhere to the refractory material of the main trench,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/66
CPCC04B35/66C04B2235/3217C04B2235/3418C04B2235/3826C04B2235/402
Inventor 张志成佘凤娅王娇佘亚锋司志刚
Owner CHANGXING MINGTIAN FURNACE CHARGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap