Method for preparing biomass cushion packaging material

A technology of cushioning packaging and biomass, which is applied in the field of preparation of biomass cushioning packaging materials, can solve the problems of high cost and white pollution, and achieve good antibacterial properties, good mechanical properties and cushioning properties, and good inhibition effect

Inactive Publication Date: 2019-02-22
浙江卫斯敦环境科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Since the 20th century, expanded polystyrene cushioning packaging materials have been widely used as cushioning packaging for electronic products, but expanded polystyrene has stable chemical properties and will not degrade naturally within 200 years under natural conditions after being discarded, resulting in serious " White Pollution”, if the expanded polystyrene is recycled for degradation, it will cost a lot of money

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing biomass cushion packaging material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A preparation method of a biomass cushioning packaging material, the components are calculated by weight, comprising the following steps:

[0030] (1) Get 20 parts of corn stalks and pulverize them, and pass through a 60-mesh sieve;

[0031] (2) Add 30 parts of 2mol / L sodium hydroxide solution and stir for 20 minutes;

[0032] (3) filtering and cleaning to obtain product A;

[0033] (4) Take 10 parts of cassava residue and sieve to remove impurities, immerse in dilute sodium hydroxide solution and stir mechanically for 1 hour, filter and wash with distilled water until neutral, move to an oven to dry at 60°C, and crush to 40 mesh screen;

[0034] (5) Add 10 parts of giant dragon bamboo powder and 200 parts of benzene-ethanol solution and mix, extract at 90°C for 5 hours, and discard the extract, wherein the volume ratio of benzene and ethanol is 2:1;

[0035] (6) Add 200 parts of ethanol aqueous solution, adjust the pH to 4 with glacial acetic acid, and stir for 5 ho...

Embodiment 2

[0044] A preparation method of a biomass cushioning packaging material, the components are calculated by weight, comprising the following steps:

[0045] (1) Get 25 parts of corn stalks and pulverize them, and pass through an 80-mesh sieve;

[0046] (2) Add 40 parts of 2mol / L sodium hydroxide solution and stir for 25 minutes;

[0047] (3) filtering and cleaning to obtain product A;

[0048] (4) Take 15 parts of cassava residue and sieve to remove impurities, immerse in dilute sodium hydroxide solution and stir mechanically for 1 hour, filter and wash with distilled water until neutral, move to an oven to dry at 60°C, and crush to 40 mesh screen;

[0049] (5) Add 15 parts of giant dragon bamboo powder and 200 parts of benzene-ethanol solution and mix, extract at 90°C for 5.5 hours, discard the extract, wherein the volume ratio of benzene and ethanol is 2:1;

[0050] (6) Add 200 parts of aqueous ethanol, adjust the pH to 4.5 with glacial acetic acid, and stir for 5.5 hours; ...

Embodiment 3

[0059] A preparation method of a biomass cushioning packaging material, the components are calculated by weight, comprising the following steps:

[0060] (1) Get 30 parts of corn stalks and pulverize them, and pass through an 80-mesh sieve;

[0061](2) Add 50 parts of 2mol / L sodium hydroxide solution and stir for 30 minutes;

[0062] (3) filtering and cleaning to obtain product A;

[0063] (4) Take 20 parts of cassava residue and sieve to remove impurities, immerse in dilute sodium hydroxide solution and stir mechanically for 1 hour, filter and wash with distilled water until neutral, move to an oven to dry at 60°C, and crush to 40 mesh screen;

[0064] (5) Add 20 parts of giant dragon bamboo powder and 200 parts of benzene-ethanol solution and mix, extract at 90°C for 6 hours, and discard the extract, wherein the volume ratio of benzene and ethanol is 2:1;

[0065] (6) Add 200 parts of ethanol aqueous solution, adjust the pH to 5 with glacial acetic acid, and stir for 6 ho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
elastic recovery rateaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for preparing a biomass cushion packaging material. The method comprises the following steps: grinding corn straws, and screening; adding a sodium hydroxide solution, and stirring; filtering and washing to obtain a product A; screening manioc waste, soaking in the sodium hydroxide solution, stirring, filtering, drying and grinding; adding dendrocalamus sinicus powder and benzene-alcohol solution, mixing and extracting; stirring with an alcohol aqueous solution; preparing an aqueous suspension liquid, grinding and homogenizing to obtain a suspension liquid B; mixing konjac glucomannan, gingko starch and deionized water, heating and stirring; adding epoxidized soybean oil and acetyl tributyl citrate, and keeping on stirring; adding the product A and the suspension liquid B, stirring, azodicarbonamide, silver-loaded chitosan microspheres, vinyl acetate-ethylene copolymer emulsion and surfactant, and keeping on stirring; and injecting into a die, performinghot-press molding, and insulating and drying for 30 seconds in the die. The packaging material has good mechanical performance, good buffer performance and good antibacterial effect.

Description

technical field [0001] The invention relates to a preparation method of a biomass cushioning packaging material. Background technique [0002] Since the 20th century, expanded polystyrene cushioning packaging materials have been widely used as cushioning packaging for electronic products, but expanded polystyrene has stable chemical properties and will not degrade naturally within 200 years under natural conditions after being discarded, causing serious " "White pollution", if the expanded polystyrene is recycled for degradation, it will cost a lot of money. Therefore, it will have very important practical significance for sustainable development to develop a natural degradable environmentally friendly green packaging material to replace the widely used expanded polystyrene foam material. Contents of the invention [0003] Technical problem to be solved: The purpose of this invention is to provide a preparation method of biomass cushioning packaging material. The prepared...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L5/02C08L97/02C08L3/02C08L91/00C08L31/04
CPCC08L3/02C08L5/02C08L97/02C08L2205/025C08L2205/035C08L91/00C08L31/04
Inventor 李志松
Owner 浙江卫斯敦环境科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com