Submerged arc welding flux, welding wire and preparation method for welding ultra-low temperature high manganese steel

A welding method and high manganese steel technology, applied in the field of welding wire and preparation, submerged arc welding flux, can solve the problems of irregular weld seam, low tensile strength of joints, and inapplicability, and achieve beautiful appearance, good mechanical properties, The effect of excellent mechanical properties

Active Publication Date: 2021-07-09
ATLANTIC CHINA WELDING CONSUMABLES
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] As we all know, the higher the manganese content is, the more difficult it is for the process and mechanical properties of the welding material. The higher the Mn content of the base metal and welding material, the more obvious the degree of metallurgical reaction in the welding process. Higher, after recent years of development, in order to improve the creep strength, durable strength and structural stability of the steel, a small amount of chromium, nickel, molybdenum, copper and other elements have been added to the steel, but how to ensure that after welding, the welded joint It has the same performance as the base metal under various corrosive media conditions such as ultra-low temperature and high pressure, which is a test for welding materials. In the existing welding materials, although some submerged arc fluxes are disclosed, such as CN107206549A (flux for submerged arc welding ), but the flux disclosed by it is used for welding the high-manganese steel of the present invention (such as manganese-carbon ratio 20), after welding, there are pores, slag inclusions and cracks inside the weld, and the low-temperature impact toughness of the weld metal (-196°C) is lower than 90J, not suitable for welding in narrow gaps, the tensile strength of joints is low, and the welds are irregular

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] SiO 2 5kg, MgO 35kg, Al 2 o 3 35kg, CaF 2 15kg, TiO 2 5kg, Fe 2 o 3 3kg, S 0.015kg, P0.010kg powders are automatically added to the mixer (the order of addition is SiO 2 --Al 2 o 3 --CaF 2 --MgO--TiO 2 , after mixing evenly, add Fe which has been mixed evenly 2 o 3 , S, P mixture and continue to stir), stir for more than 15 minutes, then add 20kg of sodium water glass to mix and adjust the powder. Machine mixing and granulation, followed by pre-drying at 100°C, low-temperature baking at 200°C, high-temperature sintering at 800°C, and screening to obtain flux with an alkalinity of 2.0.

[0039] This flux is matched with welding wire (the welding wire composition is: carbon 0.15wt%, silicon 0.3wt%, manganese 17wt%, chromium 4wt%, nickel 6wt%, molybdenum 3wt%, copper 0.3wt%, nitrogen 0.12wt%, aluminum 0.05 wt%, sulfur 0.005wt%, phosphorus 0.007wt%, the balance is iron and essential impurities), using 20mm thick A1106-Mn25 steel for submerged arc welding, ...

Embodiment 2

[0041] SiO 2 3kg, MgO 40kg, Al 2 o 3 30kg, CaF 2 18kg, TiO 2 6kg, Fe 2 o 3 2kg, S 0.014kg, P0.010kg powders are automatically added to the mixer (the order of addition is SiO 2 --Al 2 o 3 --CaF 2 --MgO--TiO 2 , after mixing evenly, add Fe which has been mixed evenly 2 o 3 , S, P mixture and continue to stir), stir for more than 15 minutes, then add 20kg of sodium water glass to mix and granulate, then pre-dry at 100°C, bake at 200°C at low temperature, sinter at 800°C, and sieve to obtain alkalinity for 2.7 flux.

[0042] This welding flux is matched with welding wire (the welding wire component composition is: carbon 0.30wt%, silicon 0.4wt%, manganese 25wt%, chromium 3wt%, nickel 9wt%, molybdenum 4wt%, copper 0.5wt%, nitrogen 0.15wt%, aluminum 0.10wt% wt%, sulfur 0.005wt%, phosphorus 0.007wt%, the balance is iron and essential impurities), using 20mm thick A1106-Mn25 steel for submerged arc welding, the process performance is excellent, and the performance o...

Embodiment 3

[0044] SiO 2 6kg, MgO 30kg, Al 2 o 3 40kg, CaF 2 15kg, TiO 2 3kg, Fe 2 o 3 3kg, S 0.015kg, P0.010kg powders are automatically added to the mixer according to the specific gravity requirements (the order of addition is SiO 2 --Al 2 o 3 --CaF 2 --MgO--TiO 2 , after mixing evenly, add Fe which has been mixed evenly 2 o 3 , S, P mixture and continue to stir), stir for more than 15 minutes, then add 20kg of sodium water glass to mix and granulate, then pre-dry at 100°C, bake at 200°C at low temperature, sinter at 800°C, and sieve to obtain alkalinity for 1.7 flux.

[0045] This welding flux is matched with welding wire (the welding wire component composition is: carbon 0.50wt%, silicon 0.33wt%, manganese 21wt%, chromium 6wt%, nickel 10wt%, molybdenum 5wt%, copper 0.8wt%, nitrogen 0.20wt%, aluminum 0.01 wt%, sulfur 0.005wt%, phosphorus 0.007wt%, the balance is iron and essential impurities), using 20mm thick A1106-Mn25 steel for submerged arc welding, the process p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The present invention disclosed a buried arc welded welding for welding ultra -low -temperature high -manganese steel, which is made from the following components: SIO 2 3‑6 weight, MGO 30 50 weight, Al 2 O 3 30 40 weight, CAF 2 10‑20 weight, TIO 2 3‑10 weight portion, 0 <fE 2 O 3 ≤3.0 weight portion, 0

Description

technical field [0001] The invention relates to the field of welding, in particular to a submerged arc welding flux, welding wire and a preparation method for welding ultra-low temperature high manganese steel. Background technique [0002] Due to problems such as the cost and resources of nickel-based materials, it is hoped that there will be a material that can replace nickel-based materials and have properties equivalent to those of nickel-based materials. For this reason, after research, high manganese steel is used to replace nickel-based materials. Due to the special composition of high manganese steel, in addition to good wear resistance, it also has good mechanical properties, and is often used in mining, excavation, and coal industries. , foundry and steel industries, etc. The manganese content of the commonly used high-manganese steel is low. This kind of steel is difficult to machine and is basically used in the form of cast iron. After being cold and deformed in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K9/18B23K35/30B23K35/36B23K35/40
CPCB23K9/186B23K35/3073B23K35/3605B23K35/361B23K35/40
Inventor 毛兴贵杨飞蒋勇张晓柏明廷泽范银东彭祺珉贾兴旺廖芬
Owner ATLANTIC CHINA WELDING CONSUMABLES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More