Room partition board material and preparation method thereof

A technology for partition boards and rooms, applied to flat products, other household appliances, applications, etc., can solve the problems of poor treatment of toxic and harmful gases, poor air quality, and harm to human health, etc., to achieve increased strength, strong Adsorption capacity, odor elimination effect

Inactive Publication Date: 2019-03-29
贵州恒力源林业科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the process of interior decoration, toxic and harmful gases such as formaldehyde will be emitted, which cannot be removed in a short time and will seriously endanger human health
However, the existing room partition board materials are not effective in treating toxic and harmful gases such as formaldehyde emitted, and the room partition board materials are not good for its basic fire prevention, heat preservation, and There are also many deficiencies in compressive and tensile properties, which also need to be further strengthened so that they can adapt to buildings with high comprehensive performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1 of the present invention. A room divider material made from raw materials of the following weights:

[0023] Fly ash 150Kg, alkali-free glass fiber 40Kg, monostearate 40Kg, pine charcoal 30Kg, acid modified montmorillonite 18Kg, rosin 20Kg, zirconia 40Kg, boron carbide 20Kg, glass fiber 15Kg, attapulgite 13Kg, 12Kg of glass wool, 17Kg of aluminum silicate, 10Kg of barium stearate, 8Kg of carbon black, 5Kg of silane coupling agent, 5Kg of distearyl thiodipropionate and 5Kg of sodium bicarbonate.

[0024] Concrete preparation steps are as follows:

[0025] (1) Weigh the raw materials according to the parts by weight of the room partition board material;

[0026] (2) Mix the weighed fly ash, glass fiber, monostearate, charcoal, montmorillonite, rosin, zirconia, boron carbide, glass fiber, attapulgite, glass wool, aluminum silicate, , to obtain the mixture;

[0027] (3) Stir the weighed heat stabilizer, light stabilizer, coupling agent, antioxidant and foam...

Embodiment 2

[0030] Embodiment 2 of the present invention. A room divider material made from raw materials of the following weights:

[0031] Fly ash 130Kg, AR glass fiber 30Kg, monostearate 20Kg, pine charcoal 20Kg, acid modified montmorillonite 13Kg, rosin 10Kg, zirconia 30Kg, boron carbide 15Kg, glass fiber 10Kg, attapulgite 9Kg, glass 14Kg of cotton, 13Kg of aluminum silicate, 6Kg of barium stearate, 6Kg of carbon black, 2Kg of silane coupling agent, 3Kg of distearyl thiodipropionate and 2Kg of sodium bicarbonate.

[0032] Concrete preparation steps are as follows:

[0033] (1) Weigh the raw materials according to the parts by weight of the room partition board material;

[0034] (2) Mix the weighed fly ash, glass fiber, monostearate, charcoal, montmorillonite, rosin, zirconia, boron carbide, glass fiber, attapulgite, glass wool, aluminum silicate, , to obtain the mixture;

[0035] (3) Stir the weighed heat stabilizer, light stabilizer, coupling agent, antioxidant and foaming agent...

Embodiment 3

[0038] Embodiment 3 of the present invention. A room divider material made from raw materials of the following weights:

[0039] Fly ash 14Kg, alkali-free glass fiber 3.5Kg, monostearate 3Kg, pine charcoal 2.5Kg, acid modified montmorillonite 1.5Kg, rosin 1.6Kg, zirconia 3.2Kg, boron carbide 1.5Kg, glass fiber 1.3 Kg, attapulgite 1.3Kg, glass wool 1.5Kg, aluminum silicate 1.5Kg, barium stearate 0.8Kg, carbon black 0.7Kg, silane coupling agent 0.4Kg, distearyl thiodipropionate 0.4Kg and sodium bicarbonate 0.3Kg.

[0040] Concrete preparation steps are as follows:

[0041] (1) Weigh the raw materials according to the parts by weight of the room partition board material;

[0042] (2) Mix the weighed fly ash, glass fiber, monostearate, charcoal, montmorillonite, rosin, zirconia, boron carbide, glass fiber, attapulgite, glass wool, aluminum silicate, , to obtain the mixture;

[0043] (3) Stir the weighed heat stabilizer, light stabilizer, coupling agent, antioxidant and foamin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a room partition board material and a preparation method thereof. The partition board material is prepared from the following raw materials, by weight ratio: 130-150 parts of fly ash, 30-40 parts of glass fibers, 20-40 parts of monostearate, 20-30 parts of charcoal, 13-18 parts of montmorillonite, 10-20 parts of rosin, 30-40 parts of zirconia, 15-20 parts of boron carbide,10-15 parts of glass fibers, 9-13 parts of attapulgite, 12-16 parts of glass wool, 13-17 parts of alumina silicate, 6-10 parts of a heat stabilizer, 6-8 parts of light stabilizer, 2-5 parts of a coupling agent, 3-5 parts of an anti-oxidant and 2-5 parts of a foaming agent. The preparation method includes weighing the raw materials according to the weight part of the partition board material; mixing part of the raw materials to obtain a mixture; mixing the other part of the raw materials to obtain mixed slurry; mixing and stirring the mixture and the mixed slurry so that a mixed raw material can be obtained; and pouring the mixed raw material to a mold, and performing solidification so that a room partition board can be obtained. The prepared partition board material cannot affect the quality of air, and has advantages of being high in compressive strength and tensile strength and good in thermal insulation effect and fire protection effect.

Description

technical field [0001] The invention relates to a preparation method of a board material for decorating a room, in particular to a room partition board material and a preparation method thereof. Background technique [0002] Room partition boards are commonly used materials for home and company decoration. In the past, straw mats, reed mats, and wooden boards were used as the main materials in traditional houses. With the advancement of technology, more building materials have been applied. In the process of interior decoration, toxic and harmful gases such as formaldehyde will be emitted, which cannot be removed in a short time and seriously endanger human health. However, the existing room partition board materials are not effective in treating toxic and harmful gases such as formaldehyde emitted, and the room partition board materials are not good for its basic fire prevention, heat preservation, and There are also many deficiencies in compressive and tensile properties,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B26/22C04B38/02C04B38/08B29C67/24B29L7/00C04B111/40C04B111/28
CPCC04B26/22B29C67/243B29L2007/002C04B38/02C04B38/08C04B2111/00025C04B2111/28C04B2111/40C04B18/08C04B14/42C04B24/08C04B14/022C04B14/104C04B14/306C04B14/323C04B14/102C04B22/00C04B24/42C04B2103/608
Inventor 林建
Owner 贵州恒力源林业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products