Skin-core polypropylene composite plastic high imitation rattan and preparation method thereof

A composite plastic and polypropylene technology, applied in the direction of coating, can solve the problems of stress cracking, the influence of the bending resistance of rattan, difficult to use in high-end furniture and handicrafts, etc., to achieve high tensile strength and folding resistance, application Wide range and good mechanical properties

Inactive Publication Date: 2019-03-29
CHENDU NEW KELI CHEM SCI CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] It can be seen that the biggest disadvantage of plastic imitation rattan in the prior art is poor texture, and its woven products are far from the characteristics of natural rattan close to nature, so it is difficult to use it as high-end furniture and handicrafts indoors
At the same time, the mechanical properties of some imitation rattan materials are not ideal. At the same time, the filler has a great influence on the bending resistance of rattan. During the weaving process, there will be obvious stress cracking and whitening, which will affect its use effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] a. Mix the polypropylene matrix, toughening agent polyethylene resin, compatibilizer ethylene-octene copolymer, physical foaming agent, antioxidant, and pigment on a high-speed mixer, and then put it into the preheated extruder In the process, through melt-extruding the foaming rods, pulling and winding after cooling, the foamed polypropylene imitation rattan matrix is ​​obtained; wherein, 80 parts by weight of the polypropylene matrix, 5 parts by weight of the toughening agent polyethylene resin, and a compatibilizer 3 parts by weight of ethylene-octene copolymer, 3 parts by weight of physical blowing agent, 12 parts by weight of antioxidant, and 8 parts by weight of pigment; the physical blowing agent is hexane, and the antioxidant is N,N'-diphenyl p-phenylenediamine, the pigment is phthalocyanine blue;

[0032] b. Mix the soluble pore-forming agent, straw glue, and inorganic whiskers evenly in an organic solvent to prepare a viscous outer wall liquid; wherein, the or...

Embodiment 2

[0035] a. Mix the polypropylene matrix, toughening agent polyethylene resin, compatibilizer ethylene-octene copolymer, physical foaming agent, antioxidant, and pigment on a high-speed mixer, and then put it into the preheated extruder In the process, the foamed rod is melted and extruded, pulled and rolled after cooling, and the foamed polypropylene imitation rattan matrix is ​​obtained; wherein, 86 parts by weight of the polypropylene matrix, 4 parts by weight of the toughening agent polyethylene resin, and a compatibilizer 2 parts by weight of ethylene-octene copolymer, 2 parts by weight of physical blowing agent, 1 part by weight of antioxidant, and 5 parts by weight of pigment; the physical blowing agent is trifluoroacetic acid, the antioxidant is diphenylamine sulfide, and the pigment is Phthalocyanine green;

[0036] b. Mix the soluble pore-forming agent, straw glue, and inorganic whiskers uniformly in an organic solvent to prepare a viscous outer wall liquid; wherein, 1...

Embodiment 3

[0039]a. Mix the polypropylene matrix, toughening agent polyethylene resin, compatibilizer ethylene-octene copolymer, physical foaming agent, antioxidant, and pigment on a high-speed mixer, and then put it into the preheated extruder In the process, the foamed strips are melted and extruded, pulled and rolled after cooling, and the foamed polypropylene imitation rattan matrix is ​​obtained; wherein, 74 parts by weight of the polypropylene matrix, 6 parts by weight of the toughening agent polyethylene resin, and a compatibilizer 4 parts by weight of ethylene-octene copolymer, 4 parts by weight of physical blowing agent, 2 parts by weight of antioxidant, 10 parts by weight of pigment; physical blowing agent is tetrahydrofuran, and antioxidant is N-phenyl-α-naphthylamine , the pigment is azo yellow;

[0040] b. Mix the soluble pore-forming agent, straw glue, and inorganic whiskers uniformly in an organic solvent to prepare a viscous outer wall liquid; wherein, 15 parts by weight ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a skin-core polypropylene composite plastic high imitation rattan and a preparation method thereof. The high imitation rattan is prepared by the steps of: a. mixing a polypropylene matrix, a toughening agent, a compatilizer, a physical foaming agent, an antioxidant and a pigment, then conducting melt extrusion and foaming to obtain a foamed polypropylene rattan-imitating substrate; b. adding a soluble pore-forming agent, straw glue and inorganic whisker into an organic solvent to prepare a viscous outer wall solution; and c. impregnating the rattan-imitating substrate in the outer wall solution, then conducting washing and drying curing, thus obtaining the skin-core polypropylene composite plastic high imitation rattan. The method has the beneficial effects that: the high imitation rattan prepared by the method provided by the invention has a rough and matt surface, has appearance, texture and density similar to those of natural rattan, also has soft texture like natural rattan, completely achieves the performance of natural rattan, at the same time has high tensile strength and folding endurance, good mechanical properties and good durability, thus having wide application range.

Description

technical field [0001] The invention relates to the field of preparation of rattan-like materials, in particular to a skin-core polypropylene composite plastic high-like rattan and a preparation method thereof. Background technique [0002] Natural rattan has certain mechanical properties, and its color is simple and natural. It is the main material for fabricating daily necessities such as furniture, baskets, boxes, and frames. However, natural rattan tends to reduce its strength after being exposed to moisture, and is prone to mold and rot, so the products processed by it are not suitable for outdoor use. In addition, the extensive use of natural rattan may cause ecological damage, and the treatment process before weaving is complicated, which greatly limits its practical application. [0003] Polymer materials have a wide range of sources, easy processing, high mechanical properties, light weight, etc., and are widely used in daily necessities, especially polyolefin poly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J7/04C08L23/12C08K7/08
CPCC08J7/0427C08J2323/12C08K7/08
Inventor 陈庆昝航
Owner CHENDU NEW KELI CHEM SCI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products