Nano composite stone material protection agent and preparation method thereof

A nano-composite and protective agent technology, which is applied to biocide-containing paints, anti-fouling/underwater coatings, coatings, etc., can solve the problems of not being able to meet the user's continuous improvement in the quality of stone protective agent products, and achieve self- Improvement of cleaning performance and adhesion, improvement of aging resistance, and enhancement of hardness

Inactive Publication Date: 2019-03-29
云浮华云创新设计有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when traditional stone protective coatings are used in the application of stone floor tiles, stone furniture, countertops, etc., they cannot meet the requirements of users for the continuous improvement of the quality of stone protective agent products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Preparation of nanocomposite modifier: (1) Add 37.5 mL of isopropanol to 1000 mL of deionized water while stirring, then slowly add 37.5 mL of tetraisopropyl titanate dropwise, stir for 1 hour after the addition, and add a little over Oxidize the hydrogen solution until the solution becomes clear. Then transfer it to a constant temperature oil tank, and return to the oil bath for 48 hours to prepare the titanium dioxide sol. After the sol is prepared, add 15g nano-SiO 2 Mixed with 25g nano tourmaline powder to prepare modified TiO 2 Sol. (2) Weigh 100g of carbon nanotube powder and place it in a beaker, disperse it in mixed acid, oscillate ultrasonically for 2 hours, then wash it with deionized water until neutral, filter it through a microporous membrane, put it into a vacuum drying oven, After drying at 110°C for 24 hours, take it out for use. (3) Using carbon nanotubes as a carrier to modify TiO 2 sol for loading, carbon nanotubes and modified TiO 2 The sol was...

Embodiment 2

[0023] Preparation of nanocomposite modifier: (1) Add 75mL of isopropanol to 2000mL of deionized water while stirring, then slowly add 75mL of tetraisopropyl titanate dropwise, stir for 2 hours after the addition is complete, and add a little hydrogen peroxide again solution until the solution becomes clear. Then transfer it to a constant temperature oil tank, and return to the oil bath for 48 hours to prepare the titanium dioxide sol. After the sol is prepared, add 50g of nano-SiO 2 Mixed with 120g nano tourmaline powder to prepare modified TiO 2 Sol. (2) Weigh 500g of carbon nanotube powder and place it in a beaker, disperse it in mixed acid, vibrate ultrasonically for 2h, then wash with deionized water until neutral, filter it through a microporous membrane, put it into a vacuum drying oven, After drying at 110°C for 24 hours, take it out for use. (3) Using carbon nanotubes as a carrier to modify TiO 2 sol for loading, carbon nanotubes and modified TiO 2 The sol was m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a nano composite stone material protection agent. A carbon nanotube-supported TiO2/tourmaline nano-composite modifier is added, wherein the TiO2 particles can reduce the scattering intensity of long wave ultraviolet ray and absorb short wave ultraviolet ray; nano SiO2 particles can absorb and reflect the ultraviolet ray, wavelength being less than 400 nm, and infrared ray,wavelength being larger than 800 nm, both absorption rate and reflection rate reaching more than 70%, so that anti-aging effect of the protection agent is greatly enhanced; meanwhile, the nano-particles have photocatytic function, so that organics can be decomposed at high efficiency. The protection agent is higher than hypochlorous acid in sterilization effect and is significantly enhanced in anti-bacterial corrosion property and improved in self-cleaning performance and adhesion force. Meanwhile, the hardness, anti-scrubbing effect and anti-wearing effect of a coating layer are enhanced by means of the carbon nanotubes and nano SiO2.

Description

Technical field: [0001] The invention relates to a stone protective agent, in particular to a nanocomposite stone protective agent and a preparation method thereof Background technique: [0002] In interior decoration, the application of stone occupies a relatively large proportion. For example, fluorocarbon stone protective agent is widely used in the coating protection of indoor stone countertops and stone wash basins. It is one of the coatings with important applications for indoor high-grade stone protection. Stone waterproof coating is a kind of stone protection technology, which has a wide range of applications in the modern stone industry. The waterproof coating makes the synthetic resin evenly distributed on the surface of the stone or slowly penetrates into the stone to form a protective film, so that the stone has waterproof, anti-fouling, oil-proof, acid and alkali resistance, weathering resistance, aging resistance, freeze-thaw resistance, Anti-biological erosio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/16C09D133/12C09D5/32C09D5/33C09D5/16C09D5/14C09D7/62
CPCC08L2201/08C09D5/004C09D5/14C09D5/1618C09D5/32C09D7/62C09D127/16C08L33/12C08K9/12C08K3/041C08K3/36C08K3/38
Inventor 文中流余宇
Owner 云浮华云创新设计有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap