Manufacturing method for dispersion strengthened oxygen-free copper alloy board

An alloy sheet and dispersion strengthening technology are applied in the field of preparation of dispersion strengthened oxygen-free copper alloy sheet, which can solve the problems of hot-rolling cracking and oxygen control of dispersion-strengthened oxygen-free copper, so as to solve the problems of hot rolling cracking and oxygen control, and ensure stability. The effect of low performance and material utilization

Active Publication Date: 2019-03-29
中铝洛阳铜加工有限公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to overcome the deficiencies in the prior art, to provide a preparation method of dispersion strengthened oxygen-free copper alloy plate, which breaks through the history that dispersed oxygen-free copper can only be supplied by rods before, and improves the quality of dispersed oxygen-free copper. The utilization rate and processing efficiency of the material, through hot rolling in a protective atmosphere under high temperature conditions, solve the problem of hot rolling cracking and oxygen control of dispersed oxygen-free copper, ensure the stability of the material size, and prepare 1.0-5mm thick Dispersion-strengthened oxygen-free copper sheets meet the needs of key materials such as high-power microwave tube cavities in the electronic information industry and vacuum high-voltage switch contacts in the electrical industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Dispersion strengthened oxygen-free copper plate for electric vacuum microwave tube, thickness 2.0mm, Al 2 o 3 Content is 0.25wt%, and its preparation method comprises the following steps:

[0027] The first step, nitrogen atomization powder making: Use a 100kg intermediate frequency melting furnace for melting, first add high-purity oxygen-free electric copper to the intermediate frequency melting furnace for 40-70 minutes, cover the melting process with charcoal; then add copper-13% phosphorus The master alloy is deoxidized for 0.5-3 minutes, then copper-30% aluminum master alloy is added for smelting for 3-8 minutes, the content of Al in the Cu-Al alloy is controlled at 0.09-0.14wt%, and then the pressure is 0.7-1.0Mpa Nitrogen gas is used to atomize and make powder, dry and sieve out -100 mesh Cu—Al alloy original powder;

[0028] The second step, preparation of oxygen source: sieve the -100 mesh Cu-Al alloy raw powder again, sieve out -200 mesh Cu-Al powder, oxid...

Embodiment 2

[0038] Dispersion-strengthened oxygen-free copper sheet for vacuum high-voltage switch contacts, thickness 1.2mm, Al 2 o 3 Content is 0.11wt%, and its preparation method comprises the following steps:

[0039] The first step, nitrogen atomization powder making: Use a 100kg intermediate frequency melting furnace for melting, first add high-purity oxygen-free electric copper to the intermediate frequency melting furnace for 40-70 minutes, cover the melting process with charcoal; then add copper-13% phosphorus The master alloy is deoxidized for 0.5-3 minutes, then copper-30% aluminum master alloy is added for smelting for 3-8 minutes, the content of Al in the Cu-Al alloy is controlled at 0.09-0.14wt%, and then nitrogen gas with a pressure of 0.7-1.0Mpa is used to carry out Atomized powder, dried, sieved -100 mesh Cu-Al alloy original powder;

[0040] The second step, preparation of oxygen source: sieve the -100 mesh Cu-Al alloy raw powder again, sieve out -200 mesh Cu-Al powder...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing method for a dispersion strengthened oxygen-free copper alloy board. A technological process of the manufacturing method comprises the following steps: atomizing nitrogen gas to prepare powder, preparing an oxygen source, mixing powder, performing cold isostatic pressing and processing, performing short-process integrated thermal treatment, extrusion-processing, performing hot-rolling on an extruded board or a sheared billet into a board, straightening and face-milling, cold-rolling, and straightening and finishing. The manufacturing method breaks through the history that only bars can be supplied for dispersion oxygen-free copper, increases a utilization rate of a dispersion oxygen-free copper material, improves the processing efficiency of the dispersion oxygen-free copper material, solves the hot-rolled cracking problem and the oxygen control problem of dispersion oxygen-free copper very well, ensures stability of the material dimension, manufactures the dispersion strengthened oxygen-free copper alloy board which is 1.0-5 mm thick, and meets needs of key materials such as an electronic information industry large-power microwave tube cavity and an electric industry overhead high-voltage switch contact sheet.

Description

technical field [0001] The invention relates to the dual technical fields of powder metallurgy and non-ferrous processing, in particular to a method for preparing a dispersion-strengthened oxygen-free copper alloy plate. Background technique [0002] At present, dispersion strengthened copper alloy is considered as a new functional material with great development potential and application prospect because of its excellent electrical conductivity, high strength and superior high temperature resistance. Many high-tech fields such as conductors, high-power microwave tubes, overhead wires for high-speed rail transit, electrodes for resistance welding, and molds for continuous casting machines have been widely used. [0003] Dispersion-strengthened copper has high strength and high softening temperature because of the small and uniform oxide points dispersed in the copper matrix; at the same time, the fine and dispersed oxide points will not have adverse effects on the electrical...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C9/00C22C1/05C22C1/10C22C1/03C22C1/06B22F9/08B22F1/00B22F3/04B22F3/10B22F3/24
CPCB22F1/0003B22F3/04B22F3/1017B22F3/24B22F9/082B22F2998/10C22C1/03C22C1/0425C22C1/05C22C1/06C22C9/00
Inventor 曹先杰牛立业郭慧稳蒋小亮李新华
Owner 中铝洛阳铜加工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap