A kind of viscosity reducing agent and its preparation method and paper coating

A technology of viscosity reducer and coating, which is applied in paper coating, paper, textiles and papermaking, etc. It can solve the problems of affecting the use effect of paper, unsatisfactory viscosity reduction effect, and affecting paper quality, so as to achieve suitable scale production and prevent precipitation , dispersion and precipitation effects

Active Publication Date: 2021-11-23
深圳市瑞成科讯实业有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to meet this development trend, the paper machine is usually required to run faster during the coating process, and the coating speed is increased, which will cause high shear. However, the viscosity of the coating will increase significantly under high shear, which will affect the paper quality.
The traditional viscosity reducer is not ideal for reducing the viscosity of the coating under high shear conditions, which may easily cause problems such as drying on the roller and coating streaks, which will affect the actual use effect of the paper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of viscosity reducing agent and its preparation method and paper coating
  • A kind of viscosity reducing agent and its preparation method and paper coating
  • A kind of viscosity reducing agent and its preparation method and paper coating

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0037] The present invention provides the preparation method of the viscosity reducer described in the above technical scheme, comprising the following steps:

[0038] (1) Mix functional monomers, maleic anhydride, part of itaconic acid, part of reducing agent and water, and mix at 78-85°C to obtain the first slurry;

[0039] (2) Mix the first slurry with part of acrylic acid and part of oxidant, keep it warm at 75-85°C for 2.5-3.5 hours, and carry out polymerization reaction to obtain the second slurry;

[0040] (3) mixing the second slurry with the remaining itaconic acid, the remaining reducing agent, the remaining acrylic acid and the remaining oxidizing agent, keeping the temperature at 75-85° C. for 2.5-3.5 hours, and performing a polymerization reaction to obtain the third slurry;

[0041] (4) Mixing the third slurry with an inorganic base to obtain a viscosity reducer.

[0042] The present invention mixes functional monomers, maleic anhydride, part of itaconic acid, p...

Embodiment 1

[0055] In terms of parts by weight, put 62.5 parts of allyl polyoxyethylene ether in a four-necked flask, raise the temperature to 80°C, make it melt, then add 200 parts of water, heat to 80°C, and then add 25 parts of maleic anhydride , 22.5 parts of itaconic acid, 6.4 parts of sodium hypophosphite and 42 parts of water are heated up to 80°C to obtain the first slurry;

[0056] 28.13 parts of acrylic acid and 7 parts of ammonium persulfate were successively added dropwise to the first slurry, the total dropping time was 1 hour, and the temperature was kept at 80° C. for 2.5 hours to obtain the second slurry;

[0057] Add 27.5 parts of itaconic acid and 9.6 parts of sodium hypophosphite to the second slurry, then add 34.37 parts of acrylic acid and 7 parts of ammonium persulfate dropwise, the total dropping time is 1 hour, and keep warm at 80°C for 3 hours , to obtain the third slurry;

[0058] The temperature of the obtained third slurry was lowered to 45° C., 50 parts of so...

Embodiment 2

[0061] In parts by weight, put 50 parts of methallyl alcohol polyoxyethylene ether into a four-necked flask, heat up to 80°C, make it melt, then add 180 parts of water, heat to 80°C, and add 12.5 parts of horse Toric anhydride, 22.5 parts of itaconic acid, 7 parts of sodium hypophosphite and 44 parts of water are heated up to 80°C to obtain the first slurry;

[0062] Add 60 parts of acrylic acid and 7.7 parts of ammonium persulfate successively dropwise to the first slurry, the total dropping time is 1 hour, keep warm at 80°C for 3 hours, to obtain the second slurry;

[0063] Add 15 parts of itaconic acid and 7 parts of sodium hypophosphite to the second slurry, then dropwise add 40 parts of acrylic acid and 6.3 parts of ammonium persulfate in sequence, the total time of dropping is 1.5h, and keep warm at 80°C 3h, obtain the third slurry;

[0064] The temperature of the obtained third slurry was lowered to 45° C., 70 parts of sodium hydroxide was added, and stirred for 0.5 h ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of coatings. The invention provides a viscosity reducer, which is prepared from raw materials comprising the following components in parts by weight: 10-62.5 parts of functional monomers; 1-25 parts of maleic anhydride; 10-50 parts of itaconic acid; 1-20 parts of reducing agent; 10-150 parts of acrylic acid; 1-15 parts of oxidizing agent; 10-80 parts of inorganic base; 50-250 parts of water; Polyoxyethylene ether or methallyl alcohol polyoxyethylene ether. The present invention uses allyl polyoxyethylene ether or methallyl alcohol polyoxyethylene ether as a functional monomer, under the action of reducing agent, oxidizing agent and water, undergoes copolymerization reaction with maleic anhydride, itaconic acid and acrylic acid , the pH value is adjusted by an inorganic base to obtain a copolymer composed of functional groups and long-chain structures. The viscosity reducer provided by the invention has a good viscosity reduction effect, especially has a good high-shear viscosity reduction effect, and is environmentally friendly and degradable .

Description

technical field [0001] The invention relates to the field of coatings, in particular to a viscosity reducer, a preparation method thereof and paper coatings. Background technique [0002] Paper coating is an important factor that determines the quality of the final paper product and the coating process. The ideal paper coating is a pseudoplastic fluid with a certain thixotropy, that is, the fluid characteristics of shear thinning or viscosity reduction. The runnability of the paint not only refers to the runnability of the coating machine, but also includes the runnability of the entire coating process. Good rheological properties of the paint must meet the requirements of various aspects, including pumping, sieving, feeding, and metering. , sizing, reflow and flow and other processes. If the rheological properties of the paint cannot meet the corresponding requirements, then there will be runnability problems. Most of the viscosity reducers on the market can effectively co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F283/06C08F220/06C08F222/02C08F4/40D21H19/38D21H19/40D21H19/44D21H19/58D21H19/64D21H21/08D21H21/12D21H21/14
CPCC08F4/40C08F283/065D21H19/385D21H19/40D21H19/44D21H19/58D21H19/64D21H21/08D21H21/12D21H21/14C08F220/06C08F222/02
Inventor 胡志滨潘好学鲁代玉沈杰赵玥祯
Owner 深圳市瑞成科讯实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com