Temperature sensing polyurethane-acrylic resin, preparation method thereof, and hot melt adhesive membrane

A technology of acrylic resin and polyurethane, which is applied to the application of hot melt adhesive film in outdoor sportswear, temperature-sensitive polyurethane-acrylic resin and its preparation, and the field of hot melt adhesive film, which can solve the problem of being unable to be used as an adhesive, waterproof and permeable Solve problems such as high melting point of wet film and poor thermal insulation of clothing, and achieve excellent moisture permeability, excellent temperature change, and good adhesion

Active Publication Date: 2019-05-21
GUANGDONG YETOM NEW MATERIALS CO LTD
View PDF14 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the waterproof and moisture-permeable function, as an important function of outdoor sportswear, has been concerned and researched by more and more manufacturers and manufacturers. The method of wet film, the melting point of the waterproof and moisture-permeable membrane made by these technologies is generally all high, can't be used as adhesive; Waterproof and moisture-permeable function, can prevent rain and wind, and can wick away sweat, breathable, comfortable to wear
However, under the harsh external environment, such as poor warmth retention at low temperature and insufficient moisture permeability at high temperature, living in a high temperature state in summer will still feel stuffy because of insufficient moisture permeability; and living in the mountains for a long time in winter, because of moisture permeability Clothing that doesn't insulate well

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Temperature sensing polyurethane-acrylic resin, preparation method thereof, and hot melt adhesive membrane
  • Temperature sensing polyurethane-acrylic resin, preparation method thereof, and hot melt adhesive membrane
  • Temperature sensing polyurethane-acrylic resin, preparation method thereof, and hot melt adhesive membrane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] With the dimethylformamide of 25Kg, the methyl ethyl ketone of 20Kg, the hydrophilic polyethylene glycol of 35Kg and phthalic anhydride polyester diol copolymerization type (PEG+PA) polyester TPU particle (melt mass flow rate is 45g / 10 Minutes, the melt viscosity is 14000mPa.s) into the reactor together, heated to 60 ° C, heated and stirred for 1 hour to dissolve, then 20Kg of methacrylic acid and 0.02Kg of catalyst diacyl peroxide were added into the kettle together, Carry out the first polymerization reaction at 60°C, react for 0.5 hours and then add the remaining 0.05Kg of catalyst diacyl peroxide (diluted with 0.3Kg of methyl ethyl ketone and add it to the reactor, and add it within 2 hours) ), continue to react for 3 hours, and the temperature in the kettle is controlled at about 80°C. After the reaction is completed, add 0.03Kg of antioxidant 1010, 0.03Kg of ultraviolet absorber UV-328, 3Kg of nano-titanium dioxide and antimony trioxide mixture to obtain a thermos...

Embodiment 2

[0053] With the dimethylformamide of 35Kg, the methyl ethyl ketone of 15Kg, the hydrophilic polyethylene glycol of 40Kg and adipic acid (AA) series polyester diol copolymerization polyester type TPU particle (melt mass flow rate is 40g / 10 minutes, the melt viscosity is 10000mPa.s) into the reaction kettle together, heated up to 60 ℃, heated and stirred to dissolve for 1 hour, then 10Kg of ethyl acrylate and 0.01Kg of catalyst azobisisobutyronitrile were added together In the kettle, carry out the first polymerization reaction at a temperature of 60°C, add the remaining 0.03Kg catalyst azobisisobutyronitrile (diluted with methyl ethyl ketone and add to the reaction kettle after 0.5 hours) by adding dropwise. After the internal addition) continue to react for 3 hours, and the temperature in the kettle is controlled at about 80°C. After the reaction is completed, add 0.03Kg of antioxidant 1010, 0.03Kg of ultraviolet absorber UV-5411, 2Kg of nano-titanium dioxide and antimony trio...

Embodiment 3

[0056] With the dimethyl formamide of 33Kg, the methyl ethyl ketone of 15Kg, the hydrophilic polyethylene glycol of 40Kg and the polyester type TPU particle (melt mass flow rate is 35g) of adipic acid (AA) series polyester diol copolymerization / 10 minutes, the melt viscosity is 15000mPa.s) together into the reactor, heated to 55 ℃, heated and stirred to dissolve for 1 hour, the mixture of 12Kg of methyl acrylate and acrylamide, 0.02Kg of the catalyst azobisiso Add butyronitrile together in the kettle, carry out the first polymerization reaction under 60 ℃ of temperature, add remaining 0.03Kg catalyst agent azobisisobutyronitrile (diluted with methyl ethyl ketone and add reaction In the still, add within 2 hours) continue to react for 5 hours, and the temperature in the kettle is controlled at about 75°C. After the reaction is completed, add 0.03Kg of antioxidant 168, 0.05Kg of ultraviolet absorber UV-9, 8Kg of nano-titanium dioxide And the mixture of antimony trioxide to obta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melt viscosityaaaaaaaaaa
Melt viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses temperature sensing polyurethane-acrylic resin, a preparation method of the temperature sensing polyurethane-acrylic resin, and a hot melt adhesive membrane. The temperature sensing polyurethane-acrylic resin comprises the following raw materials in percentage by weight: 80-99% of polyurethane-acrylic acid copolymer, and 1-20% of metal oxide, wherein the polyurethane-acrylic acid copolymer comprises the following raw materials in percentage by weight: 25-50% of hydrophilic TPU particles, 20-35% of dimethylformamide, 15-20% of butanone, 10-20% of acrylic acid and derivative of acrylic acid, 0.01-0.1% of catalyzer and 0.01-0.5% of assistant. The hot melt adhesive membrane obtained by solidifying the temperature sensing polyurethane-acrylic resin is soft in hand feeling, has excellent moisture permeability and good adhesion and a temperature sensing function, and can be widely applied to outdoor sports apparel such as mountaineering jackets, skiing wear, cold protective clothing and climbing clothes.

Description

technical field [0001] The invention belongs to the field of polymer adhesives, and in particular relates to a temperature-sensitive polyurethane-acrylic resin and a preparation method thereof, a hot-melt adhesive film obtained by curing the temperature-sensitive polyurethane-acrylic resin, and the hot-melt adhesive film outdoors Applications in sportswear. Background technique [0002] Polyurethane adhesives have been developed rapidly due to their excellent adhesion, outstanding elasticity, wear resistance and low temperature resistance, and have been widely used in shoemaking, packaging, wood processing, automobiles, textiles and other industries. Acrylic polyurethane is a material that combines the excellent weather resistance and optical properties of acrylic acid, and the comprehensive advantages of polyurethane such as low temperature resistance, good flexibility, good wear resistance, high tear strength, and high bonding strength. Broad application space. [0003] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F283/00C08F220/06C08F220/18C08F220/14C08F220/56C09J7/35C09J7/21A41D31/00
Inventor 梁坤焕欧阳效明梁锋
Owner GUANGDONG YETOM NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com