Water-based resin for waterproof oil paint and its preparation method and application

A water-based and water-based resin technology for pigments, applied in the field of painting materials, can solve the problems of labor and time-consuming, difficult to repair, poor waterproof performance, etc., and achieve the effects of safe preparation process, improved water resistance and scrub resistance.

Active Publication Date: 2021-07-13
北京勇搏科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to production technology, the water-based resins used in oil paints often have poor waterproof performance, which restricts the waterproof performance of outdoor oil paintings.
[0003] For oil paintings, especially large-scale outdoor oil paintings, due to wind, sun, rain, outdoor oil paintings often need to be waterproofed after the completion of the production. repair

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based resin for waterproof oil paint and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Add 4.0 grams of alkylphenol polyoxyethylene ether TX-10, 1.0 grams of sodium lauryl sulfate K-12, 0.75 grams of polyacrylamide, and 0.9 grams of ammonium persulfate into the three-necked bottle in sequence; The three-necked bottle is installed on the temperature control device; weigh 127 grams of deionized water, add it to the three-necked bottle, and start stirring at room temperature for 15-20 minutes until the materials are completely dissolved; then deliver 56.3 grams of styrene to the three-necked bottle in turn , 49.0 grams of butyl acrylate, 1.35 grams of methyl methacrylate, 2.5 grams of acrylic acid, continued to stir and emulsify at room temperature for 30 minutes;

[0030] Stop stirring, and after exporting 2 / 3 or 1 / 2 or 2 / 5 of the emulsion, start stirring and heating up, the heating rate is controlled at 2-3°C / min, and the heating temperature is controlled within the range of 90-93°C to prevent temperature rise Jump beyond the limit; after the initiation of...

Embodiment 2

[0034] Add 3.0 grams of alkylphenol polyoxyethylene ether TX-10, 0.9 grams of sodium lauryl sulfate K-12, 0.65 grams of polyacrylamide, and 0.8 grams of ammonium persulfate in sequence in the three-necked bottle; The three-necked bottle is installed on the temperature control device; weigh 117 grams of deionized water, add it to the three-necked bottle, and start stirring at room temperature for 15-20 minutes until the materials are completely dissolved; then deliver 55.3 grams of styrene to the three-necked bottle in turn , 48.0 grams of butyl acrylate, 1.0 grams of methyl methacrylate, 2.0 grams of acrylic acid, continued to stir and emulsify at room temperature for 30 minutes;

[0035] Stop stirring, and after exporting 2 / 3 or 1 / 2 or 2 / 5 of the emulsion, start stirring and heating up, the heating rate is controlled at 2-3°C / min, and the heating temperature is controlled within the range of 90-93°C to prevent temperature rise Jump beyond the limit; after the initiation of th...

Embodiment 3

[0039] Add 5.0 grams of alkylphenol polyoxyethylene ether TX-10, 1.1 grams of sodium lauryl sulfate K-12, 0.85 grams of polyacrylamide, and 1.0 grams of ammonium persulfate in turn into the three-necked bottle; The three-necked bottle is installed on the temperature control device; weigh 137 grams of deionized water, add it to the three-necked bottle, and start stirring at room temperature for 15-20 minutes until the materials are completely dissolved; then deliver 57.3 grams of styrene to the three-necked bottle in turn , 50.0 grams of butyl acrylate, 1.7 grams of methyl methacrylate, 3.0 grams of acrylic acid, continued to stir and emulsify at room temperature for 30 minutes;

[0040] Stop stirring, and after exporting 2 / 3 or 1 / 2 or 2 / 5 of the emulsion, start stirring and heating up, the heating rate is controlled at 2-3°C / min, and the heating temperature is controlled within the range of 90-93°C to prevent temperature rise Jump beyond the limit; after the initiation of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a water-based resin for waterproof oil paint and a preparation method thereof. The water-based resin of the present invention is made of water, alkylphenol polyoxyethylene ether, sodium lauryl sulfate, polyacrylamide, styrene, butyl acrylate, methyl methacrylate, acrylic acid, ammonium persulfate, and ammonia solution . The preparation method of the resin is as follows: adding alkylphenol polyoxyethylene ether, sodium lauryl sulfate, polyacrylamide, ammonium persulfate and water in sequence to the reaction vessel, stirring and dissolving, and then adding styrene and butyl acrylate in sequence Ester, methyl methacrylate and acrylic acid are synthesized after being stirred and emulsified for 20-40 minutes. The emulsion back-drop method is adopted in the synthesis process. After the reaction is completed, ammonia water is added to adjust the pH value to obtain the water-based resin. When the resin is used in oil paints, oil paints with good water resistance and scrub resistance can be obtained. Because the chemical heat energy generated by the reaction is fully utilized, it belongs to the energy-saving and environment-friendly oil paint waterproof resin.

Description

technical field [0001] The invention relates to the field of painting materials, in particular to a water-based resin for waterproof oil paint and its preparation method and application. Background technique [0002] The waterproof ability of the oil paint itself mainly depends on the natural resin or synthetic resin used to process the oil paint. However, due to production technology, the water-based resins used in oil paints often have poor waterproof performance, which restricts the waterproof performance of outdoor oil paintings. [0003] For oil paintings, especially large-scale outdoor oil paintings, due to wind, sun, rain, outdoor oil paintings often need to be waterproofed after the completion of the production. repair. Contents of the invention [0004] One of the purposes of the present invention is to synthesize a water-based resin for waterproof oil paints. The specific technical scheme is as follows: [0005] A water-based resin for waterproof oil paint, s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F212/08C08F220/18C08F220/14C08F220/06C09D125/14C09D5/06
CPCC08F212/08C09D5/06C09D125/14C08F220/1804C08F220/14C08F220/06
Inventor 谷燕王奇陈曦
Owner 北京勇搏科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka