High-toughness wear-resisting cable material

A cable material and high-toughness technology, applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve the problems of low tensile strength, poor wear resistance, inconvenient processing, etc., to improve impact resistance and mechanical properties , Improve the effect of dispersion

Pending Publication Date: 2019-07-23
北京中科惠景储能材料科技有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to provide a high-toughness wear-resistant cable material for the problems of poor wear resistance, low tensile strength, weak toughness and inconvenient processing of commonly used cable materials at present.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033]The preparation method of composite cable auxiliary material comprises the steps:

[0034] (1) According to the mass ratio of 5:1:3:0.1:50~85, take the shrimp shell powder, grape skin, yeast extract, casein, and water through a 100-mesh sieve and mix them in the fermenter, stirring and mixing at 400~550r / min 15~30min, stand still for 2~4h, add pretreated biogas slurry with 3~7% mass of shrimp shell powder, stir magnetically at 350~550r / min for 20~45min, seal and let stand for fermentation for 3~5 days, discharge , filter, collect the fermentation liquid and transfer it to an autoclave, heat and sterilize it at 121°C for 12-18 minutes to obtain a sterilized liquid, take the sterilized liquid in a rotary evaporator, and concentrate it by rotary steaming at 75-85°C for 40~ 60min to obtain a concentrated solution, mix the concentrated solution and reagent A according to the mass ratio of 1:12~20, and stir magnetically at 500~800r / min for 40~60min to obtain a compound mixture...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-toughness wear-resisting cable material and belongs to the technical field of wires and cables. According to the invention, biogas slurry is firstly treated and then shrimp shells are treated in the manner of mixed fermentation, so that chitin is differentiated and degraded, active ingredients can be generated, cross-linking action can be enhanced and overall wear-resisting property can be promoted; aramid fiber pulp has a fluff structure, has an ultra-large contact area with a resin component and is capable of promoting interaction of inner components of the system, improving shock resistance, promoting toughness, increasing degree of orientation, increasing surface roughness, promoting compatibility thereof with a modified resin component and jointly promoting toughness and wearing resistance; due to the addition of castor oil, vibration strength of covalent bonds in the resin component can be reduced, tensile strength can be effectively promoted, and the castor oil and the compound modified resin component can be combined into an interwound firm three-dimensional network so as to promote the inner mechanical properties. The high-toughness wear-resisting cable material is capable of solving the problems of inferior wear-resisting property, low tensile strength, low toughness and inconvenience in processing of the present common cable material.

Description

technical field [0001] The invention belongs to the technical field of electric wires and cables, and in particular relates to a high-toughness wear-resistant cable material. Background technique [0002] Power supply has become an indispensable part of the rapid development of the world economy, and wires and cables, as the carrier of power supply, pervade all walks of life. Since the polymer insulation materials used in wires and cables are flammable materials, the internal factors (cable self-heating, short circuit, etc.) and external factors (fire, etc.) often cause the cable to burn during the transmission of electric energy, causing damage to life and property. Traditional flame-retardant cables mainly use halogen-containing polymers (such as PVC) and halogen-containing flame retardants (chlorine- or bromine-containing compounds) to obtain good flame-retardant properties through mixing, but fires still cause cables to burn, and cables A large amount of toxic fumes and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L63/00C08L61/06C08L97/02C08L77/10C08L27/06C08L9/02C08L91/00C08K13/02C08K5/098C08K3/22C08K3/34H01B3/40
CPCC08K2003/2241C08K2201/011C08L63/00C08L2203/202C08L2205/035C08L2205/16H01B3/40C08L61/06C08L97/02C08L77/10C08L27/06C08L9/02C08L91/00C08L91/005C08K13/02C08K5/098C08K3/22C08K3/34
Inventor 赵玲玲
Owner 北京中科惠景储能材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products