Flame retardant for plywood glue and application of flame retardant
A technology for plywood and flame retardant, which is applied in the direction of adhesive application device, bonding of wooden veneers, wood treatment, etc., can solve the problems of reducing the quality of plywood, high production cost, poor flame retardant effect, etc., saving drying space, Low production cost and improved flame retardant properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0035] Take 30kg of flame retardant and 100kg of urea-formaldehyde resin adhesive, mix and stir evenly, then add 28kg of flour to the mixture of flame retardant and adhesive, continue stirring, and get the required flame retardant adhesive after mixing evenly.
[0036] Among them, the flame retardant is compounded by the following components by weight: 50kg of modified aluminum hydroxide, 12kg of ammonium phosphate, 6kg of diammonium phosphate, and 35kg of zinc borate. The decomposition temperature of the flame retardant is 310°C.
[0037] The 1.5mm poplar veneer is pre-dried to make the moisture content of the veneer 8% to 10%. Using the flame retardant configured above, glue the poplar veneer on both sides at room temperature through a double-sided gluing machine, and the amount of glue is 420g / m 2 .
[0038] Make imposition of 7 poplar veneers after gluing, and let them stand at room temperature and pressure of 1.0MPa for 14h. Then put the impositioned poplar veneer into ...
Embodiment 2
[0041] Take 32kg of flame retardant and 100kg of urea-formaldehyde resin adhesive, mix and stir evenly, then add 30kg of flour to the mixture of flame retardant and adhesive, continue to stir, and mix evenly to obtain the required flame retardant adhesive.
[0042] Among them, the flame retardant is compounded by the following components by weight: 55kg of modified magnesium hydroxide, 10kg of ammonium polyphosphate, 8kg of ammonium chloride, and 25kg of borax. The decomposition temperature of the flame retardant is 300°C.
[0043] The 1.5mm poplar veneer is pre-dried to make the moisture content of the veneer 8% to 10%. Using the flame retardant configured above, glue the poplar veneer on both sides at room temperature through a double-sided gluing machine, and the amount of glue is 480g / m 2 .
[0044] Make imposition of 7 poplar veneers after gluing, and let them stand at room temperature and pressure of 0.8MPa for 10h. Then put the imposition poplar veneer into the cold p...
Embodiment 3
[0047] Take 31kg of flame retardant and 100ka of urea-formaldehyde resin adhesive, mix and stir evenly, then add 25kg of flour to the mixture of flame retardant and adhesive, continue stirring, and get the required flame retardant adhesive after mixing evenly.
[0048] Among them, the flame retardant is compounded by the following components by weight: 7kg of modified magnesium hydroxide, 53kg of modified aluminum hydroxide, 15kg of melamine polyphosphate, 4kg of ammonium phosphate, and 30kg of ammonium pentaborate. The decomposition temperature of the fuel is 308°C.
[0049] The 1.5mm poplar veneer is pre-dried to make the moisture content of the veneer 8% to 10%. Using the flame retardant configured above, double-sided gluing of 1.5mm poplar veneer at room temperature is carried out through a double-sided gluing machine, and the amount of glue is 520g / m 2 .
[0050] Make imposition of 7 poplar veneers after gluing, and let them stand for 12 hours at room temperature and pres...
PUM
![No PUM](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/noPUMSmall.5c5f49c7.png)
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap