Chinese fir anticorrosion modification agent and preparing method and constructing process thereof

A treatment agent and technology for fir, applied in the field of anti-corrosion modified treatment agent for fir and its preparation, can solve the problems of polluting the environment, active ingredients, unstable size, easy loss of fir, etc., and achieves improved dispersibility, good chemical stability, improved The effect of corrosion resistance and corrosion stability

Active Publication Date: 2019-08-13
福建省顺昌县升升木业有限公司
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the disadvantages of currently commonly used fir anticorrosion and modification treatment agents such as toxicity, environmental pollution, and easy loss of active components, as well

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chinese fir anticorrosion modification agent and preparing method and constructing process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A preparation method of fir anticorrosion modification treatment agent, characterized in that: the specific steps are as follows:

[0026] Add 40g of copper ion and borate ion-supported graphene oxide, 250g of water-based polyurethane, 4.5g of didecyldimethylammonium chloride and 4.5g of polyoxypropylene oxide ethylene glyceryl ether into 1500mL of water, and mechanically stir for 90min at room temperature , and then sonicated for 90 minutes, and finally mechanically stirred for 45 minutes to prepare the fir anticorrosion modification treatment agent.

[0027] In the graphene oxide supported by copper ions and borate ions, the weight percentage of copper ions is 17.7%, and the weight percentage of borate ions is 10.5%.

[0028] A kind of construction technology of Chinese fir anticorrosion modification treatment agent, it is characterized in that: comprise the following steps:

[0029] (1) Place the dried Chinese fir sample in an automatic vacuum pressurized tank, evac...

Embodiment 2

[0032] A preparation method of fir anticorrosion modification treatment agent, characterized in that: the specific steps are as follows:

[0033] Add 20g of copper ion and borate ion-supported graphene oxide, 100g of water-based polyurethane, 2g of sodium polyacrylate and 1g of polyoxyethylene polyoxypropanolamine ether into 1000mL of water, mechanically stir for 60min at room temperature, then sonicate for 60min, and finally Stir mechanically for another 30 minutes to prepare the fir anticorrosion modification treatment agent.

[0034] In the graphene oxide supported by copper ions and borate ions, the weight percentage of copper ions is 21.9%, and the weight percentage of borate ions is 13.6%.

[0035] A kind of construction technology of Chinese fir anticorrosion modification treatment agent, it is characterized in that: comprise the following steps:

[0036] (1) Place the dried fir sample in an automatic vacuum pressurized tank, evacuate to a vacuum degree of 0.03MPa, and...

Embodiment 3

[0039] A preparation method of fir anticorrosion modification treatment agent, characterized in that: the specific steps are as follows:

[0040] Add 60g of copper ion and borate ion-supported graphene oxide, 400g of water-based polyurethane, 8g of didecyldimethylammonium chloride and 10g of defoamer DF681F into 2000mL of water, mechanically stir for 120min at room temperature, and then sonicate for 120min. Finally, mechanically stir for 60 minutes to prepare the Chinese fir anticorrosion modification treatment agent.

[0041] In the graphene oxide supported by copper ions and borate ions, the weight percentage of copper ions is 12.2%, and the weight percentage of borate ions is 7.55%.

[0042]A kind of construction technology of Chinese fir anticorrosion modification treatment agent, it is characterized in that: comprise the following steps:

[0043] (1) Place the dried Chinese fir sample in an automatic vacuum pressurized tank, evacuate to a vacuum degree of 0.06 MPa, keep ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a Chinese fir anticorrosion modification agent and a preparing method and constructing process thereof, and belongs to the technical field of wood anticorrosion treatment. Theanticorrosion modification agent is prepared by adding copper-ion-loaded and borate-ion-loaded graphene oxide, waterborne polyurethane, a dispersing agent and a defoaming agent to water for mechanicalstirring and ultrasonic processing. The constructing process includes the steps of conducting impregnation treatment on Chinese fir through the prepared anticorrosion modification agent and conducting thermal treatment on the Chinese fir through a superheated steam drying box. By means of the prepared anticorrosion modification agent and the constructing process, the anticorrosion property and anticorrosion stability of the Chinese fir can be remarkably improved, the hardness, wear resistance and size stability of the Chinese fir can be greatly improved, and the Chinese fir anticorrosion modification agent has the remarkable economic value and social benefits.

Description

technical field [0001] The invention belongs to the technical field of wood anticorrosion treatment, and in particular relates to a fir anticorrosion modification treatment agent, a preparation method and a construction process thereof. Background technique [0002] Chinese fir is one of the tree species with the largest planting area in my country, and is an important fast-growing timber species unique to my country. Chinese fir wood is widely used in the fields of construction, furniture, and wood-based panels. However, due to the fast growth rate and short rotation period of Chinese fir, the wood contains a high proportion of young and middle-aged wood, the wood is loose, and the strength is poor, so Chinese fir products are easy to produce. There are problems with rot and moth. Plantation fir must be treated with antiseptic before use. [0003] Water-based preservative injection is a more commonly used method of wood preservation in recent years. Chromated copper arse...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27K3/08B27K3/02B27K5/04B27K3/52
CPCB27K3/02B27K3/08B27K3/52B27K5/04B27K2240/20
Inventor 毛克升陈怡
Owner 福建省顺昌县升升木业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap