A kind of epoxy anticorrosion coating and preparation method thereof

An epoxy anti-corrosion coating and epoxy resin technology, applied in the coating field, can solve the problems of poor corrosion resistance and high temperature resistance of epoxy resin, poor durability of epoxy resin, reduced adhesion performance of epoxy resin, etc. Application range, increased thermal stability, improved self-cleaning effect

Active Publication Date: 2021-02-02
上海博歌建材有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Epoxy resin is an important thermosetting resin. The cured epoxy resin has the advantages of good electrical properties, adhesive properties and mechanical properties. It is widely used in mechanical processing, aerospace and other fields. A large amount of epoxy resin molecular chains The rigid benzene ring endows the resin with rigidity and heat resistance; polar groups such as hydroxyl and ether bonds make the epoxy resin have strong adhesion to the base metal after curing, but the corrosion resistance of the epoxy resin itself Poor performance and high temperature resistance. In the prior art, some modifiers are often added to modify it, but the durability of physically modified epoxy resin is poor. Chemical modification is often used with epoxy resin end rings. Oxygen grafting method, this method will reduce the adhesion performance of epoxy resin, resulting in weakened adhesion of the modified epoxy resin, and the epoxy coating after coating is easy to fall off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of epoxy anticorrosion coating and preparation method thereof
  • A kind of epoxy anticorrosion coating and preparation method thereof
  • A kind of epoxy anticorrosion coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] Preparation of S6 modified epoxy resin

[0048] Add 1kg of epoxy resin to the reaction kettle, then add 200g of modifier E, stir evenly, heat up to 100°C, then add 25ml of triethylamine drop by drop, complete the dropwise addition within 30min, keep warm and continue to stir for 2h. Promptly obtain modified epoxy resin;

[0049] The structures of possible modified epoxies are shown below:

[0050]

[0051] The alcoholic hydroxyl group on the epoxy resin can react with the two epoxy groups on the modifier E, or one molecule of the modifier E can be cross-linked with two molecules of the epoxy resin, thereby embedding the modifier E branched into epoxy resin;

[0052] The infrared characterization of modified epoxy resin is as follows: IR(KBr): 3032, 3005 (benzene ring), 2964, 2920 (-CH 2 -, -CH 3 ), 1375 (-CH 3 ), 1294, 1205 (-C-N), 1180 (-O-Si-C-), 915 (epoxy) cm -1 .

Embodiment 1

[0054] An epoxy anticorrosion coating, comprising the following raw materials by weight: 100g of modified epoxy resin, 80g of pigment and filler, 5g of dispersant, 15g of film-forming aid, 1g of leveling agent, and 1g of defoamer;

[0055] A preparation method of epoxy anti-corrosion coating is as follows: put the raw materials of epoxy anti-corrosion coating into the mixing tank for pre-mixing for 5 minutes, and then melt and extrude the pre-mixture. The extrusion parameters are: 1 zone 120°C , the second zone is 180°C, the screw speed is 50Hz, and the extruded flakes are put into a ball mill for grinding. The speed of the ball mill is 2200rpm. The ground coarse powder is passed through a 200-mesh sieve by a rotary sieve to obtain a fine powder of 10-80 microns as the final product. Epoxy anti-corrosion coating.

Embodiment 2

[0057] An epoxy anticorrosion coating, comprising the following raw materials by weight: 100g of modified epoxy resin, 120g of pigment and filler, 2g of dispersant, 20g of film-forming aid, 3g of leveling agent, and 3g of defoamer;

[0058] A preparation method of epoxy anti-corrosion coating is as follows: put the raw materials of epoxy anti-corrosion coating into the mixing tank for pre-mixing for 10 minutes, and then melt and extrude the pre-mixture. The extrusion parameters are: 1 zone 120°C , second zone 180°C, screw speed 50Hz, extrude flakes and put them into a ball mill for grinding. The speed of the ball mill is 1600rpm. The ground coarse powder is passed through a 200-mesh sieve by a rotary sieve to obtain a fine powder of 10-80 microns as the final product. Epoxy anti-corrosion coating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an epoxy anticorrosive paint, and a preparation method thereof. The epoxy anticorrosive paint comprises, by weight, 100 parts of modified epoxy resin, 80 to 120 parts of a pigment filler, 2 to 5 parts of a dispersant, 15 to 20 parts of a film forming auxiliary agent, 1 to 3 parts of a leveling agent, and 1 to 3 parts of an antifoaming agent. According to the preparation method, epoxy resin is modified without influencing the viscosity of epoxy resin, active anticorrosive functional groups are introduced into the epoxy resin through grafting, so that the epoxy resin paint is provided with excellent scrubbing resistance, shedding of the anticorrosive function groups is not easily caused, and the corrosion resistance of the epoxy resin paint can be maintained for a long term.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to an epoxy anticorrosion coating and a preparation method thereof. Background technique [0002] Epoxy resin is an important thermosetting resin. The cured epoxy resin has the advantages of good electrical properties, adhesive properties and mechanical properties. It is widely used in mechanical processing, aerospace and other fields. A large amount of epoxy resin molecular chains The rigid benzene ring endows the resin with rigidity and heat resistance; polar groups such as hydroxyl and ether bonds make the epoxy resin have strong adhesion to the base metal after curing, but the corrosion resistance of the epoxy resin itself Poor performance and high temperature resistance. In the prior art, some modifiers are often added to modify it, but the durability of physically modified epoxy resin is poor. Chemical modification is often used with epoxy resin end rings. The me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/10C09D163/00C09D5/08C08G77/42
CPCC08G77/42C09D5/08C09D163/00C09D183/10
Inventor 何文霞
Owner 上海博歌建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com