Composite cigarette paper applied to magnetic particle uniform heating type tobacco product

A technology for tobacco products and cigarette paper, which is applied in the field of composite cigarette paper for magnetic particle soaking tobacco products, can solve the problems of solvent spots at the punching position, the burning appearance of cigarettes, affecting the consumption experience, etc., so as to avoid the overflow of smokeless gas. , beautiful appearance, good adaptability to the machine

Inactive Publication Date: 2019-08-27
CHINA TOBACCO ANHUI IND CO LTD
View PDF10 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary cigarette paper cannot meet the requirements of magnetic particle soaking tobacco products, and the cigarette paper used in other types of new tobacco products (such as low-temperature non-burning tobacco products) cannot meet the requirements. For example, CN 104452479B relates to a composite cigarette with an aluminum foil layer Paper, which burns the outer layer of wood pulp fiber paper to provide heat energy and heats the shredded tobacco wrapped in aluminum foil. Because the outer layer of fiber paper is flammable, it will cause the cigarette to burn or the appearance of carbonization to blacken. It is not suitable for magnetic soaking tobacco In addition, due to the use of laser or mechanical drilling, it is easy to cause smoke overflow during the suction process, resulting in solvent spots at the drilling position, which affects the consumer experience; CN 104452418B, CN201510624220 and CN 201420653193 all have similar technical applications problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite cigarette paper applied to magnetic particle uniform heating type tobacco product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] Example 1: Composite Cigarette Paper for Magnetic Particle Soaking Tobacco Products

[0068] The implementation mode of this embodiment is as follows:

[0069] The composite cigarette paper is composed of cigarette fiber paper, film-forming material and an adhesive layer between the fiber cigarette paper and the film-forming material according to the thickness ratio of 1:0.2:0.06.

[0070] Among them, the cigarette fiber paper is wood pulp fiber plant fiber sold by Qingdao Zhongyi Trade Development Co., Ltd. under the trade name of Chilean Venus, and light calcium carbonate sold by Jiangxi Darui Chemical Co., Ltd. under the trade name of Darui Light Calcium Carbonate. The calcium carbonate filler and the sodium silicate additive sold by Jinan Xinsenyuan Chemical Co., Ltd. under the trade name instant sodium silicate are composed of a weight ratio of 62:20:3.

[0071] The film-forming material is an iron-aluminum alloy film-forming material with a thickness of 0.1 mm an...

Embodiment 2

[0075] Example 2: Composite Cigarette Paper for Magnetic Particle Soaking Tobacco Products

[0076] The implementation mode of this embodiment is as follows:

[0077] The composite cigarette paper is composed of cigarette fiber paper, film-forming material and an adhesive layer between the fiber cigarette paper and the film-forming material according to the thickness ratio of 1:0.06:0.02.

[0078] Among them, the cigarette fiber paper is the hemp pulp fiber plant fiber sold by Shanghai Pulaima International Trade Co., Ltd. under the trade name of Spain Selesa, and the product sold by Guangzhou Bangyou Chemical Technology Co., Ltd. under the trade name of heavy calcium carbonate. The heavy calcium carbonate filler and the diammonium hydrogen phosphate additive sold by Jiangsu Kelundo Food Ingredients Co., Ltd. under the trade name of food grade diammonium hydrogen phosphate are composed of a weight ratio of 74:34:2.

[0079] The film-forming material is an iron-aluminum alloy ...

Embodiment 3

[0083] Example 3: Composite Cigarette Paper for Magnetic Particle Soaking Tobacco Products

[0084] The implementation mode of this embodiment is as follows:

[0085] The composite cigarette paper is composed of cigarette fiber paper, film-forming material and an adhesive layer between the fiber cigarette paper and the film-forming material according to the thickness ratio of 1:0.5:0.1.

[0086] Among them, the cigarette fiber paper is the straw pulp fiber plant fiber sold by Dalian Yangrun Trading Co., Ltd. under the trade name of chemical straw pulp, and the colloidal carbonic acid sold by Jiangxi Darui Chemical Co., Ltd. under the trade name of nano-active calcium carbonate. The calcium filler and the silica additive sold by Guangzhou Zhongqi Silicon Industry Co., Ltd. under the trade name of silica are composed according to the weight ratio of 80:28:3.

[0087] The film-forming material is an iron-aluminum alloy film-forming material with a thickness of 0.008 mm and an al...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thermal resistanceaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a composite cigarette paper applied to a magnetic particle uniform heating type tobacco product. The composite cigarette paper is composed of a cigarette fiber paper, a film forming material, and an adhesive layer between the cigarette fiber paper and the film forming material. The composite cigarette paper solves the basic problems of temperature resistance, heat preservation and constant temperature of the cigarette paper applied to the magnetic particle uniform heating type tobacco product; at the same time, by means of the composite cigarette paper, the surface ofthe fiber paper, after a cigarette is sucked, has no discoloration or carbonization or the like, and the appearance of the cigarette is beautiful. The composite cigarette paper not only avoids the overflow of smoke in the uniform heating process of the cigarette, but also effectively improves the feeling of suction and the sensory quality of the smoke.

Description

[0001] 【Technical field】 [0002] The invention belongs to the technical field of cigarette production. More specifically, the present invention relates to a composite cigarette paper for magnetic particle soaking tobacco products. [0003] 【Background technique】 [0004] In recent years, with the tightening of the tobacco control situation and the gradual increase of consumers' health concerns, countries have become more stringent in the control of smoking in public places. New types of tobacco products such as heat-not-burn, magnetic particle soaking, electronic cigarettes and smokeless tobacco products are gradually favored by consumers. At present, the R&D, design and manufacturing of various types of new tobacco products are highly valued by the tobacco industry at home and abroad, and have become a hot topic in tobacco research. [0005] As a new category of new tobacco products-magnetic soaking tobacco products, there is no essential difference in appearance from ordin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/38D21H21/06D21H11/12D21H17/67D21H17/68D21H17/66C09J11/04
CPCC09J11/04D21H11/12D21H17/66D21H17/675D21H17/68D21H21/06D21H27/38
Inventor 徐迎波葛少林佘世科张亚平王健朱栋梁陈开波张超
Owner CHINA TOBACCO ANHUI IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap